Corn straw particle board and manufacturing method thereof

A technology of particle board and corn stalks, which is applied in the field of wood-based panels and its manufacturing, can solve the problems of shortening the hot-pressing time, achieve the effects of shortening the hot-pressing time, ensuring the appearance quality, and improving productivity

Active Publication Date: 2008-06-04
SHANGHAI COMPAK ENVIRONMENTAL PROTECTION EQUIP CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a corn stalk particle board and its manufacturing method to solve the technical problems of improving the strength of the corn stalk particle board itself, simplifying the glue sizing and mixing process, and increasing the hot pressing temperature to shorten the hot pressing time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corn straw particle board and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Please refer to Fig. 2, the present invention uses a peeling machine to separate the pith from the corn stalks after ear removal and leaf removal, the pith core after separation is used for other purposes, and the epidermis after separation is then cut off as a board-making raw material , usually cut according to the length of 20cm. The cut corn stalk epidermis is then crushed into crushed material with a pulverizer. The mesh size of the pulverizer is 6mm, and the composition of the crushed material is in the following range:

[0015] Particle size (mm)

＜6～4.75

＜4.75～2.26

＜2.26～1.63

＜1.63～1.41

＜1.41～1.096

＜1.096～0.56

＜0.56～0.216

＜0.216

weight percentage (%)

1.00～1.50

6.90～7.30

11.00～11.50

8.20～8.70

6.75～7.15

29.80～30.50

25.00～25.40

9.40～10.40

[0016] Then apply 3.2-3.7% isocyanate adhesive of the weight of the corn stalks to the crumbs and stir evenly,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the category of cropper straw wood based panel. A maize straw grain plate comprises maize straw broken material and isocyanate adhesive. The invention is characterized in that the maize straw broken material is the grain of the skin of the marrow-removed maize straw; the weight percentage of the grain composition can be seen in the table; the content of the isocyanate is 3.2% to 3.7% times of the weight of the maize straw broken material. The manufacturing method of the maize straw grain plate is that the skin and marrow of the maize straw are removed; the peeled skin of the maize straw is cut off, crushed, screened, glued, paved, pre-pressed, hot pressed under the temperature ranging from 170 DEG C to 175 DEG C and edge cut. The invention solves the technical problems of improving the strength of maize straw crushed grain plate, simplifying gluing and glue mixing process, raising hot pressing temperature and shortening hot pressing time.

Description

Technical field: [0001] The invention belongs to the field of crop stalk-based panels, in particular to an artificial panel using corn stalks as a raw material and a manufacturing method thereof. Background technique: [0002] Since the 1980s, my country has begun to use straws of crops, such as wheat, rice, rapeseed, corn, flax, sugar cane, sunflower, etc., to replace wood to make wood-based panels. In the "Forest Industry" There have been many related reports in the publications, but so far only a few crop straws such as wheat and rice have entered the industry of manufacturing artificial particle boards, and most of the rest of the crop straws have not shown their glory in the wood-based panel industry. Among them, corn straw particle board is an example. Some corn straw board factories successively established in Jilin, Shaanxi, Inner Mongolia, and Heilongjiang failed to persist. The reason is that these enterprises still use the old idea of ​​using the whole straw of crop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/02B27N1/00B27N3/08
Inventor 王步宁
Owner SHANGHAI COMPAK ENVIRONMENTAL PROTECTION EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com