Aqueous rust-conversion rust-inhibiting primer

A technology of rust conversion and anti-rust primer, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of resin coordination, biological genetic gene changes, and conversion products without adhesion, etc., to achieve good compatibility and good resistance , the effect of cost advantage

Active Publication Date: 2008-04-16
安泰能(上海)高分子材料有限公司
View PDF0 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. Tannic acid and maleic acid only have the transformation effect on iron rust, and cannot form a film after transformation. There are no other film-forming substances in the formula, so that the transformation product has no adhesion, sealing performance, and extremely poor anti-corrosion effect;
[0007] 2. Nonylphenol polyoxyethylene ether has the effect of improving penetration, but it is already a banned surfactant in Europe, and has the risk of genetically changing organisms;
[0008] 3. Sodium nitrite is also carcinogenic and should be limited in use
[0009] The research on water-based rust conversion anti-rust primer abroad began in the 1970s, and it has a history of nearly 20 years in China. Although many technicians have done some work in the conversion of rust and made some progress, they have not been able to solve the problem with resins. There is a problem with cooperation, so it cannot be promoted in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] formula:

[0040] raw material

[0041] Its product production process:

[0042] Raw materials→measurement→wetting→moisturizing→converting agent→film former→defoaming→corrosion→measurement→packaging

[0043] The steps are:

[0044] Step 1. Accurately weigh various raw materials according to the formula weight ratio with a weighing device;

[0045] Step 2. Add deionized water into the material tank, add fatty alcohol polyoxyethylene ether, and raise the temperature to 65°C at the same time;

[0046] Step 3. Then add propylene glycol, start the high-speed disperser and adjust the speed to above 500 rpm for 10 minutes;

[0047] Step 4. Add tributyl phosphate, potassium sorbate, tannic acid, and phosphoric acid, and adjust the rotation speed to 1200 rpm, stir for 50 minutes, and then cool to 22°C.

[0048] Step 5. Add the vinylidene chloride modified acrylic resin emulsion, adjust the rotation speed to 800 rpm, stir for 15 minutes and discharge.

[0049] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based rust conversion antirust primer which is characterized in that: the primer comprises the following components with the corresponding percentage by weight : main conversion agent 5-35, auxiliary conversion agents 2-15, film forming material 40-55, penetrant 0.2-1.0, humectant 1-10, anti-forming agent 0.1-0.5, corrosion inhibitor 0.2-0.5 and solvent 0.5-8; the process is as follows: adding deionized water to a charging basket and heating the water to 60-80 DEG C with aliphatic alcohol polyethenoxy ether added, adding propylene glycol and starting a high-speed dispersion machine for agitation, later on adding tributyl phosphate, potassium sorbate, tannic acid and one of the auxiliary conversion agents and cooling down to 20-33 DEG C after agitating for 30-55 minutes, and adding vinyl chloride-modified acrylic resin latex and discharging material after agitating for 10-20 minutes. The invention has the advantages of direct application to steel surfaces with rust, thorough conversion of rust, excellent adhesive force of a conversion film, good flexibility, adaptation to various forms, and good compatibility with various top coatings.

Description

technical field [0001] The invention relates to a water-based rust conversion anti-rust primer, which can be applied to any kind of rusted steel surface, without derusting the substrate, and can be directly applied to convert it into a primer with good antirust performance, which belongs to the primer Lacquer technology field. Background technique [0002] According to statistics, the world releases 20 million tons of hydrocarbons into the atmosphere every year, of which 10 million tons are organic solvents, most of which are produced by the coating industry. The organic solvent discharged into the atmosphere during paint manufacturing is 20% of the paint output, and the organic solvent volatilized into the atmosphere during the paint coating process is 50%-80% of the paint amount. These organic volatiles emitted into the atmosphere can poison people and even cause cancer. Organic compounds emitted into the atmosphere react chemically under sunlight, producing many active ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/02C09D5/12
Inventor 王峰
Owner 安泰能(上海)高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products