Epoxy group anti-skid glue and preparation method thereof

An epoxy-based, anti-skid technology, applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve the problems of poor aging resistance and poor wear resistance, and achieve a rough anti-skid surface, long service life and high bonding strength. Effect

Active Publication Date: 2008-03-26
JIANGSU DALISHI YUNSHI NURSING MATERIAL CO LTD
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the disadvantages of poor wear resistance and aging resistance of the existing anti-skid tapes, which can only be used indoors, the present invention provides an epoxy-based anti-skid adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Epoxy-based anti-skid adhesive, which includes A component and B component, A component includes 20 parts of epoxy resin, 0.5 parts of thinner, 1 part of white carbon black, 20 parts of quartz sand, 1 part of quartz powder, and 1 part of active calcium 1 part of heavy calcium; Component B includes 20 parts of organic modified amine, 1 part of accelerator, 5 parts of white carbon black, 20 parts of quartz sand, 1 part of quartz powder, and 1 part of silicon powder.

[0040] The coupling agent is vinyl silane, the diluent is propylene oxide nonyl ether and propylene oxide C 12-14 1. The epoxy resin is bisphenol A glycidyl ether, the organic modified amine is alicyclic amine, the accelerator is 4-ethyl-1,6-lutidine, and the quartz sand is 40 mesh.

[0041] The preparation method of epoxy-based anti-slip glue: A component is to add white carbon black to the mixed solution of epoxy resin and diluent to disperse evenly, and add quartz sand, quartz powder, active Calcium, hea...

Embodiment 2

[0044] Epoxy-based anti-skid adhesive, which includes A component and B component, A component includes 35 parts of epoxy resin, 3 parts of thinner, 5 parts of white carbon black, 60 parts of quartz sand, 6 parts of quartz powder, 10 parts of active calcium 5 parts of heavy calcium; B component includes 40 parts of organic modified amine, 5 parts of accelerator, 3 parts of coupling agent, 10 parts of white carbon black, 50 parts of quartz sand, 10 parts of quartz powder, and 10 parts of silicon powder.

[0045] The coupling agent is γ-propyltrimethoxysilane, the diluent is ether 5-octadecone and polyglycidyl ether, the epoxy resin is bisphenol F glycidyl ether epoxy resin, and the organic modified amine is isophordione Diamine, accelerator are a, a'-diethyldibenzylamine and 1,1,4-trimethyl-6-ethoxytetrahydroquinoline, and quartz sand is 100 mesh.

[0046] The preparation method of epoxy-based anti-slip glue: A component is to add white carbon black to the mixed solution of epo...

Embodiment 3

[0049] Epoxy-based anti-slip glue, the A component includes 25 parts of epoxy resin, 1 part of diluent, 1 part of white carbon black, 40 parts of quartz sand, 2 parts of quartz powder, 6 parts of active calcium, and 2 parts of heavy calcium; B The components include 30 parts of organic modified amine, 2 parts of accelerator, 4 parts of white carbon black, 40 parts of quartz sand, 5 parts of quartz powder and 5 parts of silicon powder.

[0050] The coupling agent is γ-aminopropyltriethoxysilane and anilinomethyltriethoxysilane, and the diluent is propylene oxide C 12-14 And ether 5-octadecanone, the epoxy resin is bisphenol A glycidyl ether and bisphenol F glycidyl ether epoxy resin, the organic modified amine is low molecular polyamide and isophordione diamine, and the accelerator is 4 -Ethyl-1,6-lutidine, a,a'-diethyldibenzylamine, 1,1,4-trimethyl-6-ethoxytetrahydroquinoline, 4-nonylphenol , Quartz sand is 80 mesh.

[0051] The preparation method of epoxy-based anti-skid gl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The epoxy-base antislip glue includes one component A and one component B. It features the component A comprising epoxy resin 20-35weight portions, diluent 0.5-3weight portions, carbon white 1-5weight portions, quartz sand 20-60 weight portions, quartz powder 1-6weight portions, active calcium 1-10weight portions and coarse whiting 1-5weight portions; and the component B comprising modifying organic amine 20-40weight portions, promoter 1-5weight portions, coupling agent 0-3weight portions, carbon white 5-10weight portions, quartz sand 20-50weight portions, quartz powder 1-10weight portions, and silica powder 1-10weight portions. The epoxy-base antislip glue has obvious antislip effect, simple construction, long service and environment friendship. It may be applied for indoor and outdoor antislip. The present invention also discloses the preparation process of the epoxy-base antislip glue.

Description

technical field [0001] The invention belongs to an epoxy adhesive with anti-skid function, more specifically, it is an epoxy-based anti-skid adhesive. The invention also relates to a preparation method of the epoxy-based anti-skid glue. Background technique [0002] Existing anti-slip products mainly include anti-slip coatings, anti-slip agents and anti-slip tapes, etc., which are only suitable for indoor use and cannot be widely used in outdoor places with a large flow of people, thereby limiting the promotion of its application range. The most widely used is slotting in the anti-slip area or inlaying copper strips after slotting. These two forms are a kind of damage to the surface of the substrate, especially when the anti-slip area is used on the stone base surface, slotting or external force inlaying The form is easy to damage the protective surface of the stone, causing stone lesions, easy to fall off, poor anti-skid effect, and limited life. And because of the high c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/02C09J11/00C09J9/00
CPCE01C11/24C09J163/00C08L2666/54
Inventor 孙丹九伍双凤项英凡杜昆文
Owner JIANGSU DALISHI YUNSHI NURSING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com