Prick-resistant leakage-proof material for inner tube-free tyre and its preparation method and spray-coating method
A tire and inner tube technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of lack of high temperature resistance, low temperature resistance, oil resistance and water resistance, simple coating method, inability to achieve results, etc. Tightness and adhesion, improve safety effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] Step 1, mix 80kg SEBS and 120kg white oil for industrial use according to the ratio, stir and foam in a container for 24 hours to form a mixed material for later use;
[0028] Step 2. Put the foamed mixed material into the reaction pot, add 2.4kg carbon 5 and 0.8kg TPE, heat at 250-280°C for 20 minutes, stop heating after the mixed material melts, and cool to 190°C It's ready to spray.
[0029] When spraying, the tire should be rotated in a balanced manner at about 90 revolutions per minute, and the thickness of the sprayed leak-proof layer should be 5-8mm. The spraying thickness is controlled by the spraying time and spraying amount. After spraying, the speed of rotation should be increased to 120 rpm, so that under the action of centrifugal force, the anti-leakage layer material will be evenly cooled on the inner wall of the tire, and the cooling time is about 5 minutes, so that the anti-leakage layer of the tire is formed.
[0030] In addition, ultrasonic or impact...
Embodiment 2
[0032] Step 1, mix 80kg SEBS and 160kg white oil for industrial use according to the ratio, stir and foam in a container for 24 hours to form a mixed material for later use;
[0033] Step 2. Put the foamed mixed material into the reaction pot, add 0.8kg of carbon 9 and 4kg of TPE, heat at a temperature of 250-280°C for 20 minutes, stop heating after the mixed material melts, and cool to 170°C. Sprayed.
[0034] The rest are the same as Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
brittleness temperature | aaaaa | aaaaa |
service temperature | aaaaa | aaaaa |
decomposition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com