Flexible dye sensitized solar energy cell photoanode preparation method and apparatus

A solar cell and dye sensitization technology, which is applied in the field of preparing dye-sensitized solar cell photoanodes, can solve the problems of easy cracking, long time consumption, poor reproducibility, etc., achieve energy saving in production, good uniformity, and improve universal application sexual effect

Inactive Publication Date: 2009-08-26
SOUTHEAST UNIV
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Technical problem: In view of the above technical problems, the present invention provides a fast and convenient method and equipment for preparing the photoanode of flexible dye-sensitized solar cells with low cost and simple manufacturing process, which can realize the obtained semiconductor film without cracks and uniformity. Good, controllable thickness, solves the shortcomings of the current electrode preparation technology, such as long time-consuming, poor reproducibility, random distribution of local surface density of semiconductor films, and easy cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible dye sensitized solar energy cell photoanode preparation method and apparatus
  • Flexible dye sensitized solar energy cell photoanode preparation method and apparatus

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Example 1: a. Use flexible conductive polymer film ITO / PET as the photoanode electrode material, the substrate thickness is 100um, the visible light transmittance is 75%, and the surface sheet resistance is 14Ω / □.

[0037] b. Clean the substrate. Drop a few drops of detergent in deionized water, rinse the substrate in it for a few minutes, rinse with deionized water, then soak in KOH isopropanol saturated solution for 2 hours, rinse with deionized water, and then rinse in deionized water Clean with ultrasonic vibration in water and absolute ethanol for 10 minutes, rinse with absolute ethanol and blow dry with nitrogen.

[0038] c. According to actual needs, the place on the substrate that does not need to be sprayed is encapsulated with insulating tape, and the shape of the photoanode is controlled by adjusting the geometry and size of the encapsulation area to manufacture photoanodes that meet the needs of different places, even on non-planar surfaces Photoanodes with...

Embodiment 2

[0043] Example 2: a. Use flexible conductive polymer film ITO / PET as the photoanode electrode material, the substrate thickness is 125um, the visible light transmittance is 80%, and the surface sheet resistance is 100Ω / □.

[0044] b. Clean the substrate. Drop a few drops of detergent in deionized water, rinse the substrate in it for a few minutes, rinse with deionized water, then soak in KOH isopropanol saturated solution for 2 hours, rinse with deionized water, and then rinse in deionized water Clean with ultrasonic vibration in water and absolute ethanol for 10 minutes, rinse with absolute ethanol and blow dry with nitrogen.

[0045] c. According to actual needs, the place on the substrate that does not need to be sprayed is encapsulated with insulating tape, and the shape of the photoanode is controlled by adjusting the geometry and size of the encapsulation area to manufacture photoanodes that meet the needs of different places, even on non-planar surfaces Photoanodes wit...

Embodiment 3

[0050] Example 3: a. Use flexible conductive polymer film ITO / PET as the photoanode electrode material, the substrate thickness is 200um, the visible light transmittance is 85%, and the surface sheet resistance is 14Ω / □.

[0051] b. Clean the substrate. Drop a few drops of detergent in deionized water, rinse the substrate in it for a few minutes, rinse with deionized water, then soak in KOH isopropanol saturated solution for 2 hours, rinse with deionized water, and then rinse in deionized water Clean with ultrasonic vibration in water and absolute ethanol for 10 minutes, rinse with absolute ethanol and blow dry with nitrogen.

[0052] c. According to actual needs, the place on the substrate that does not need to be sprayed is encapsulated with insulating tape, and the shape of the photoanode is controlled by adjusting the geometry and size of the encapsulation area to manufacture photoanodes that meet the needs of different places, even on non-planar surfaces Photoanodes with...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a method and equipment of preparing flexible photo-anodes for dye-sensitized solar cells, and ensures an obtained semiconductor film free of cracks and superior in good uniformity and controllable thickness. The invention solves the problems of the prior art, such as long preparation time, poor repeatability, random distribution of local surface density of the semiconductor film, and high cracking risk. The flexible photo-anode is obtained by spray-coating of a conductive substrate by using a high-voltage electrostatic method and has good surface uniformity, and the surface semiconductor film doesn't produce cracks after random bending, thereby substantially realizing the flexibility. The preparation method is performed at normal temperature and pressure, without needing sinter process, thereby saving production energy and making it possible for nano-sized semiconductor materials with poor heat resistance to be applied in the field. The invention provides a new approach to improve the quality of the dye-sensitized solar cells.

Description

1. Technical field [0001] The invention belongs to a technology for preparing a photoanode of a dye-sensitized solar cell, in particular to a preparation method and equipment for a photoanode of a flexible dye-sensitized solar cell. 2. Background technology [0002] Existing technology: As the focus of solving the energy crisis and environmental pollution, solar energy is a pollution-free and inexhaustible energy source, which has been paid more and more attention by governments in recent years. The United States, Japan, Germany and other countries have promulgated corresponding laws and regulations to encourage the use of renewable energy such as solar energy. With the improvement of the conversion efficiency of solar cells and the reduction of cost, solar energy will be able to compete with other power sources within 20 years. [0003] my country is the country with the fastest growing energy consumption in the world. 2 , NO x , CO 2 As a large emission country, the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L31/18H01L51/48H01L21/28H01G9/04H01G9/20H01M14/00H01M4/04
CPCY02E60/12Y02E10/542Y02E10/549Y02E60/10Y02P70/50
Inventor 代云茜孙岳明王育乔宋铂
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com