Mass production of nano-scaled platelets and products

a technology of nano-scale platelets and products, applied in the direction of single-layer graphene, silicate, silicon compounds, etc., can solve the problems of high material cost, tedious washing step, and high cost of cnts, and achieve the effect of reducing the intercalation tim

Active Publication Date: 2010-09-02
GLOBAL GRAPHENE GRP INC
View PDF15 Cites 50 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0020]In summary, the present invention provides a process for exfoliating a layered (laminar) material to produce nano-scaled platelets having a thickness smaller than 100 nm. The process comprises: (a) charging a layered material to an intercalation chamber comprising a gaseous environment at a first temperature (typically 50° C. to 200° C., but could be higher) and a first pressure (typically 2 atm to 10 atm) sufficient to cause gas species to penetrate into the interstitial space between layers of the layered material, forming a gas-intercalated layered material; and (b) operating a discharge valve to rapidly eject the gas-intercalated layered material through a nozzle into an exfoliation zone at a second pressure and a second temperature, allowing gas species residing in the interstitial space to exfoliate the layered material to produce the platelets. The gaseous environment preferably contains only environmentally benign gases that are reactive (e.g., oxygen) or non-reactive (e.g., noble gases) with the layered material. Step (a) may be preceded by a step of pre-pressurizing or pre-intercalating the layered material in a separate chamber to reduce the necessary intercalation time in step (a).

Problems solved by technology

However, CNTs are extremely expensive due to the low yield and low production and purification rates commonly associated with all of the current CNT preparation processes.
The high material costs have significantly hindered the widespread application of CNTs.
In addition to the utilization of undesirable chemicals, in most of these methods of graphite intercalation and exfoliation, a tedious washing step is required, which produces contaminated waste water that requires costly disposal steps.
This earlier application did not address the issue of mass production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mass production of nano-scaled platelets and products
  • Mass production of nano-scaled platelets and products
  • Mass production of nano-scaled platelets and products

Examples

Experimental program
Comparison scheme
Effect test

example 1

Nano-Scaled Graphene Platelets (NGPs) from Graphite Flakes

[0051]One hundred grams of natural graphite flakes ground to an average size of approximately 2.3 μm were sealed in a helium gas-filled steel container (the intercalation chamber schematically shown in FIG. 2) at 150° C. and 16 atm for 20 minutes to yield the desired gas-intercalated graphite (GIG). Subsequently, the exit valve was opened to expel the GIG out of the chamber. The GIG was exfoliated to a good extent with an expansion ratio (exfoliated flake thickness / GIG flake thickness) of approximately 12 / 1 to 26 / 1. The thickness of individual platelets was found to range from single graphene sheet to approximately 20 graphene sheets. A small portion of the exfoliated graphite particles were then ball-milled in a high-energy plenary ball mill machine for 24 hours to produce nano-scaled particles with reduced length and width (now 0.5-2 μm).

example 2

NGPs from Short Carbon Fibers

[0052]The procedure was similar to that used in Example 1, but the starting material was carbon fibers chopped into segments with 0.2 mm or smaller in length prior to the gas intercalation treatment. The diameter of carbon fibers was approximately 12 μm. An exfoliation ratio of 6 / 1-8 / 1 was observed after being discharged from the exit nozzle.

example 3

NGPs from Graphitic Nano-Fibers (GNFs)

[0053]A powder sample of graphitic nano-fibers was prepared by introducing an ethylene gas through a quartz tube pre-set at a temperature of approximately 800° C. A small amount of Cu—Ni powder was positioned on a crucible to serve as a catalyst, which promoted the decomposition of the hydrocarbon gas and growth of GNFs. Approximately 2.5 grams of GNFs (diameter of 10 to 80 nm) were intercalated with a mixture of hydrogen and helium gases at approximately 12 atm and 150° C. for 30 minutes and then to 200° C. at 10 atm for additional 10 minutes. After discharge from the chamber, the intercalated particles were found to be exfoliated to a great extent (without an expansion ratio measurement). A large number of single- or double-layer graphene discs of 10-80 nm in diameter and 0.34 or 0.68 nm in thickness were obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

Disclosed is a process for exfoliating a layered material to produce nano-scaled platelets having a thickness smaller than 100 nm, typically smaller than 10 nm, and often between 0.34 nm and 1.02 nm. The process comprises: (a) charging a layered material to an intercalation chamber comprising a gaseous environment at a first temperature and a first pressure sufficient to cause gas species to penetrate into the interstitial space between layers of the layered material, forming a gas-intercalated layered material; and (b) operating a discharge valve to rapidly eject the gas-intercalated layered material through a nozzle into an exfoliation zone at a second pressure and a second temperature, allowing gas species residing in the interstitial space to exfoliate the layered material to produce the platelets. The gaseous environment preferably contains only environmentally benign gases that are reactive (e.g., oxygen) or non-reactive (e.g., noble gases) with the layered material. The process can additionally include dispersing the platelets in a matrix material to form a nanocomposite. The process also can include an additional process of re-compressing the nana-scaled platelets into a product such as a flexible graphite sheet.

Description

[0001]This invention is based on the research result of a DoE SBIR project. The US government has certain rights on this invention.FIELD OF THE INVENTION[0002]The present invention relates generally to a process for mass-producing nano-scaled plate-like or sheet-like structures, such as nano-scaled graphene platelets (NGPs) and clay nano-platelets, and products derived from these platelets.BACKGROUND[0003]Carbon is known to have four unique crystalline structures, including diamond, graphite, fullerene and carbon nano-tubes. The carbon nano-tube (CNT) refers to a tubular structure grown with a single wall or multi-wall, which can be conceptually obtained by rolling up a graphene sheet or several graphene sheets to form a concentric hollow structure. A graphene sheet is composed of carbon atoms occupying a two-dimensional hexagonal lattice. Carbon nano-tubes have a diameter on the order of a few nanometers to a few hundred nanometers. Carbon nano-tubes can function as either a conduc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): C08K3/20C08K3/34C01B31/04C01B19/04C01B33/26
CPCB82Y30/00B82Y40/00C01B31/0415C01B2204/04C01B31/0469C01B33/40C01B2204/02C01B31/043C01B32/22C01B32/23C01B32/19
Inventor JANG, BOR Z.ZHAMU, ARUNAGUO, JIUSHENG
Owner GLOBAL GRAPHENE GRP INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com