Aluminum conductor composite core reinforced cable and method of manufacture

Abstract

This invention relates to an aluminum conductor composite core reinforced cable (ACCC) and method of manufacture. An ACCC 303 cable (300) has a composite core surrounded by an outer film (305) and at least one layer of aluminum conductor (306). The composite core (303) comprises a plurality of fibers from at least one fiber type in one or more matrix materials. According to the invention, unique processing techniques such a B-Staging and / or film-coating techniques can be used to increase production rates from a few feet per minute to sixty or more feet per minute.

Description

TECHNICAL FIELD [0001] The present invention relates to an aluminum conductor composite core (ACCC) reinforced cable and method of manufacture. More particularly, the present invention relates to a cable for providing electrical power having a composite core, formed by fiber reinforcements and a matrix, surrounded by aluminum conductor wires capable of carrying increased ampacity and operating at elevated temperatures. BACKGROUND ART [0002] Attempts have been made to develop a composite core comprised of a single type of fiber and thermoplastic resin. The object was to provide an electrical transmission cable which utilizes a reinforced plastic composite core as a load bearing element in the cable and to provide a method of carrying electrical current through an electrical transmission cable which utilizes an inner reinforced plastic core. The single fiber / thermoplastic composite core failed in these objectives. A one fiber / thermoplastic system does not have the required physical ch...

AI Technical Summary

Benefits of technology

[0007] An aluminum conductor composite core (ACCC) reinforced cable can ameliorate the problems in the prior art. The ACCC cable is an electrical cable with a composite core comprised of one or more fiber type reinforcements embedded in a matrix. The composite core is wrapped with electrical conductor wires. An ACCC reinforced cable is a high-temperature, low-sag conductor, which can be operated at temperatures above 100° C. while exhibiting stable tensile strength and creep elongation properties. In exemplary embodiments, the ACCC cable can operate at temperatures above 100° C. and in some embodiments above 240° C. An ACCC cable with a similar outside diameter may increase the line rating over a prior art cable by at least 50% without any significant changes in the overall weight of the conductor.

[0008] In accordance with the invention, in one embodiment, an ACCC cable comprises a core comprised of composite material surrounded by a protective coating. The composite material is comprised of a plurality of fibers selected from one or more fiber types and embedded in a matrix. The important characteristics of the ACCC cable are a relatively high modulus of elasticity and a relatively low coefficient of thermal expansion of the structural core. The ACCC core, which is also smaller in diameter, lighter in weight, and stronger than previous core designs allows an increase the ampacity of the conductor cable, by allowing the addition of additional conductor material in the same overall area, with an approximately equal weight. It is further desirable to design composite cores having long term durability. The composite strength member should operate at a minimum of 40 years and more preferably twice that, at elevated operating temperatures and in the other environmental conditions to which it will be exposed.

Problems solved by technology

The single fiber / thermoplastic composite core failed in these objectives.

A one fiber / thermoplastic system does not have the required physical characteristics to effectively transfer load while keeping the cable from sagging.

Secondly, a composite core comprising glass fiber and thermoplastic resin does not meet the operating temperatures required for increased ampacity, namely, between 90° C. and 240° C. or higher.

Physical properties of thermoplastic composite cores are further limited by processing methods.

Previous processing methods cannot achieve a high fiber to resin ratio by volume or weight.

These processes do not allow for creation of a fiber rich core that will achieve the strength required for electrical cables.

Moreover, the processing speed of previous processing methods is limited by inherent characteristics of the process itself.

The longer dies create increased friction between the composite and the die slowing processing time.

With thousands of miles of cables needed, these slow processing speeds fail to meet the need in a financially acceptable manner.