Process for preparing chitosan nano fiber film with stable state

A technology of chitosan nanometer and nanofiber, which is applied in the direction of fiber treatment, fiber chemical characteristics, and conjugated synthetic polymer artificial filament, can solve the problems of inability to maintain the structure and shape of nanofiber composite membrane, and achieve stable shape structure, The effect of high porosity and high specific surface area

Inactive Publication Date: 2007-02-07
ZHEJIANG UNIV
View PDF7 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem that the currently prepared chitosan / polyvinyl alcohol nanofiber composite membrane cannot maintain the original structure of the nanofiber composite membrane in an aqueous solution, the present invention provides a chitosan nanofiber membrane with a stable morphological structure. Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Be that 5% chitosan (viscosity-average molecular weight is 100,000) is dissolved in 90% acetic acid aqueous solution by weight percent, mechanically stirs at normal temperature, after dissolving completely, form homogeneous, transparent, viscous solution; 9% polyvinyl alcohol (the degree of polymerization is 1700, and the degree of alcoholysis is 88%) is dissolved in water to form a homogeneous, transparent, viscous solution; Mix evenly to get the spinning solution, add it to the injector, connect it to the spinneret, connect the spinneret to the high-voltage power supply, the distance between the spinneret and the acceptor is about 10 cm, and the spinneret spinning solution The flow rate is 0.3 ml / hour, the voltage is 20 kV, electrospinning is performed, and a chitosan / polyvinyl alcohol nanofiber composite membrane with a diameter of 50-200 nanometers is obtained. Then immerse the obtained nanofiber composite membrane in 0.5 mol / liter sodium carbonate solution, soak it...

Embodiment 2

[0017] The chitosan (viscosity-average molecular weight is 200,000) that is 4% by weight percentage is dissolved in 90% acetic acid aqueous solution, mechanically stirred at normal temperature, after dissolving completely, form homogeneous, transparent, viscous solution; 9% polyvinyl alcohol (polymerization degree is 2400~2500, alcoholysis degree is 99%) is dissolved in water, forms homogeneous, transparent, viscous solution; : 1 mix evenly to obtain the spinning solution, add it to the sample injector, connect to the spinneret, connect the spinneret to the high voltage power supply, the distance between the spinneret and the acceptor is about 10 cm, and the spinneret spins The flow rate of the silk liquid is 0.5 ml / hour, the voltage is 20 kV, electrospinning is carried out, and a chitosan / polyvinyl alcohol nanofiber composite membrane with a diameter of 100-300 nanometers is obtained. Then immerse the obtained nanofiber composite membrane in 0.5 mol / liter sodium hydroxide sol...

Embodiment 3

[0019] The chitosan (viscosity-average molecular weight is 500,000) that is 3% by weight percent is dissolved in 90% acetic acid aqueous solution, mechanically stirred at normal temperature, after dissolving completely, form homogeneous, transparent, viscous solution; 10% polyvinyl alcohol (polymerization degree is 1700, alcoholysis degree is 88%) is dissolved in water, forms homogeneous, transparent, viscous solution; Mix evenly to get the spinning solution, add it to the injector, connect to the spinneret, connect the spinneret to the high-voltage power supply, the distance between the spinneret and the acceptor is about 15 cm, and the spinneret spinning solution The flow rate is 1.0 ml / hour, the voltage is 20 kV, electrospinning is carried out, and a chitosan / polyvinyl alcohol nanofiber composite membrane with a diameter of 400-800 nanometers is obtained. Then immerse the obtained nanofiber composite membrane in 1 mol / liter of potassium carbonate solution, soak it at room t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

the invention discloses a chitose nanometer fiber film and preparing method with stable shape structure in the carrier domain, which comprises the following steps: forming transparent solution in the water mixed solvent through dissolving chitose and polyvinyl alcohol in the glacial acetic acid; putting the spin liquid in the feeder; connecting spin-spraying head with high-pressure power at 5-30 kV; spinning; immersing the film material in the strong alkaline solution; possessing stable shape structure.

Description

technical field [0001] The invention relates to a preparation technology of a chitosan nanofiber membrane with a stable morphological structure. Background technique [0002] The use of electrospinning to prepare nano-sized fiber composite membrane materials has attracted more and more attention. Electrospinning technology is to spin a polymer solution or melt under an electric field, stretch it due to electrostatic action, and obtain ultra-fine nanofibers after cooling or solvent volatilization. This type of material has the advantages of high specific surface area and high porosity. . The electrospinning method can be used to prepare various polymer nanofiber composite membrane materials. US 20030215624; 20040013873 common polymers such as: polyvinyl alcohol, polyethylene, polypropylene, polystyrene, polysulfone, polycarbonate, polyurethane, polymethacrylate, polyvinyl chloride, polyamide by electrospinning , polyacrylate, polyvinylpyrrolidone, etc. to prepare superfine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J5/18C08L5/08D01F8/18D01F8/04D01D5/00
Inventor 徐志康黄小军弋丹
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com