Double-face glass fibre board and production thereof

A glass fiber board and manufacturing method technology, applied in chemical instruments and methods, glass/slag layered products, sheets/boards, etc., can solve the problems of single function, high cost, low strength, etc. Long service life effect

Inactive Publication Date: 2006-08-16
卢伟汉
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a multi-functional, low-cost, high-strength double-sided glass fiber board, and a method for making this fiber board, so as to overcome the defects of existing glass fiber boards such as single function, high cost, and low strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-face glass fibre board and production thereof
  • Double-face glass fibre board and production thereof
  • Double-face glass fibre board and production thereof

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0046] The first embodiment of the present invention is such as figure 1 As shown, the double-sided fiberglass board includes a crystal glue layer 1 and a glass fiber layer 2 made of glass fiber cloth and a surface glue layer 3, wherein the glass fiber layer is placed between the crystal glue layer and the surface glue layer; A filler is placed between layer 1 and fiberglass layer 2 (as in one photo 4). Therefore, the double-layer fiberglass board has a permanent commemorative value, and the fiberglass board can also be placed anywhere for decoration, and can also be used as a gift to relatives and friends, because the main raw materials of its crystal glue layer and surface glue layer are all different. Saturated resin for durability and long shelf life.

[0047] The method of manufacturing the first embodiment of the present invention is as follows:

[0048] Take the first mold, such as Figure 5Described, described first mold comprises a bottomed outer frame 10, the bott...

no. 2 example

[0057] The second embodiment of the present invention is such as figure 2 As shown, the double-sided fiberglass board includes crystal glue layers 1', 1'a and glass fiber layers 2', 2a' made of glass fiber mats and a surface glue layer 3', and the glass fiber layer 2a' is attached to the surface The glue layer 3', the crystal glue layer 1a' is arranged between the glass fiber layer 2a' and the glass fiber layer 2', the glass fiber layer 2' is close to the crystal glue layer 1' on one side, and the other side is close to the crystal glue layer 1a '; There is a watch 4' between the crystal glue layer 1' and the glass fiber layer 2'. Therefore, the double-layer fiberglass board can be used as a clock and can be used to decorate indoors or outdoors. Meanwhile, the crystal glue layer and the surface glue layer are unsaturated resins, which are durable and can protect the clock inside.

[0058] The method for manufacturing the double-sided glass plate in the second embodiment of t...

no. 3 example

[0070] The third embodiment of the present invention is such as image 3 As shown, the double-sided fiberglass board includes crystal glue layers 1", 3" and a glass fiber layer 2" made of glass fiber cloth, and the glass fiber layer 2" is arranged on the crystal glue layer 1" and the crystal glue layer 3". Between; the crystal glue layer 1" and the crystal layer 3" are provided with a laser strip 4". The laser strip itself can emit light, while the crystal glue is transparent, so that the double-sided fiberglass board can emit beautiful light at night and can It is installed on the exterior of the building to play a decorative role, especially at night, and it can also form a special pattern through multiple pieces of the same double-sided glass.

[0071] The method for manufacturing the double-sided glass plate in the third embodiment of the present invention is as follows:

[0072] Take the first mold, such as Figure 5 Described, described first mold comprises a bottomed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A double-sided fiberglass board and its manufacturing method, including product invention and method invention, wherein the product mainly refers to a panel composed of resin, drier, accelerator, glass fiber and filler as raw materials, wherein the filler can be Signs in Chinese and English and patterns, or flowers and plants, or daily necessities, or building materials, or clothing, or jewelry, jewelry, or newspapers, magazines, books, readable materials, or photos, or clocks, or luminous powder, or luminous stones, or laser strips, or The combination of the above-mentioned fillers; the method includes using a mold, mixing various raw materials according to the ratio, pouring them into the mold, and then putting the fillers into the mold and completing the process by heating, cooling and other processes.

Description

technical field [0001] The invention relates to a glass fiber board made of resin as the main raw material and its manufacturing method, in particular to a double-sided glass fiber board with some specific functions and its manufacturing method. Background technique [0002] Since the appearance of glass fiber board, due to its high and low temperature resistance, high strength and hardness, good insulation performance, wear resistance, moisture-proof, waterproof and noise-proof, no aging, long storage time and other characteristics, it can be widely used in different parts of the building Such as doors, floors, interior decoration and outdoor furniture, as well as kitchens, etc., which have unlimited business opportunities. So in order to strengthen its function, specific ingredients can be added therein, such as adding ABC powder to make it more resistant to high temperature and fire prevention, or any toner can be added therein for the sake of appearance, as disclosed in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44C5/04B32B27/04B32B27/06B32B17/04B32B27/20B29C39/12B29C39/26F16S1/10B32B17/02E04C
CPCB32B17/02B44C5/0423B44C5/0453
Inventor 卢伟汉
Owner 卢伟汉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com