High-strength water-permeable concrete floor brick and its production method

A technology of permeable concrete and floor tiles, applied in floors, buildings, building structures, etc., can solve the problems of wasting clay resources and wasting energy, and achieve good freeze-thaw resistance, resource saving, good cooling and heat insulation effects Effect

Inactive Publication Date: 2006-04-26
潘英豪
View PDF0 Cites 65 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-strength permeable concrete floor tile and its production method, which solves the problem that the floor tile must have high strength and has water permeability; at the same time, it solves the waste of clay resources and a large amount of energy in the production of permeable floor tiles. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength water-permeable concrete floor brick and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0052] See the accompanying drawings for the embodiment: This high-strength permeable concrete pavement brick is composed of a base layer 2 and a surface layer 1. The base layer 2 includes small crushed stones 3 and large crushed stones 4, and the cement slurry is wrapped on the aggregate surface composed of large and small crushed stones. , The pores 5 between the aggregates form water-permeable channels. The weight ratio of the base layer is as follows:

[0053] Examples of cement selection: 18%, 19%, 20%, 21%.

[0054] Among them, not more than 30% of cement can be replaced by slag or fly ash.

[0055] Examples of the selection of 3-5mm small gravel: 50%, 51%, 52%, 53%, 54%, 55%;

[0056] Examples of the selection of 7-10mm large gravel: 18%, 19%, 20%, 21%.

[0057] The weight ratio of the above-mentioned 7-10mm large crushed stones to 3-5mm small crushed stones is 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10. The size ratio of large particles and small particles can b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The production process of permeable high-strength concrete paver includes the steps of: the first making base layer via mixing cement 18-21 wt%, small rubble of 3-5 mm size 50-55 wt%, large rubble of 7-10 mm size 18-21 wt%, admixture 0.1-6 wt% and water in 0.2-0.23 weight of cement, molding and vibrating to form; and the subsequent making facing layer via mixing cement 15-22 wt%, quartzite 76-85 wt%, admixture 0.1-6 wt%, dispersible latex powder 0.2-0.6 wt% and water in 0.24-0.26 weight of cement, pouring the mixture onto freshly formed base layer, and vibrating to form; demolding; and curing to obtain the finished product. The permeable high-strength concrete paver has high strength, high water permeability and no need of baking, and may be used widely.

Description

(1) Technical field [0001] The invention relates to a floor paving building material, in particular to a floor tile and a production method thereof. (2) Background technology [0002] Floor tiles are subject to greater pressure and therefore require higher strength. The existing floor tiles have high density, such as concrete floor tiles, concrete, polymer synthetic floor tiles, ceramic floor tiles, etc. These floor tiles are all formed from the same material at one time, and the internal material has fewer pores, and the pores are not connected. , impermeable, cut off the communication between the subgrade and the outside world, and destroyed the natural ecological environment. Existing water-permeable floor tiles are made of sintered ceramic materials. Although they have a certain water-permeable function and meet ecological needs, they consume a lot of energy and consume a lot of energy and precious clay resources during firing. If the porosity of the existing concrete ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B14/04C04B14/06C04B14/48E04F15/08
Inventor 潘英豪
Owner 潘英豪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com