Heat pressing burnt carbon brick for lining and hearth of iron smelting blast furnace
An iron-making blast furnace and carbon brick technology, which is applied in the field of refractory materials, can solve the problems of limited life of iron-making blast furnace, low brick quality, low production efficiency, etc. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0035] The hot-pressed fired charcoal brick of the present invention can be prepared according to the following weight percentage proportions and steps:
[0036] a. Weight percentage ratio:
[0037] Electric calcined anthracite 20, natural graphite 30, artificial graphite 30,
[0038] Silicon metal 1, silicon oxide 1, aluminum oxide 3, high temperature asphalt 15;
[0039] b. Preparation steps:
[0040] In the first step, the above-mentioned raw materials are crushed and pulverized, and then mixed and proportioned;
[0041] The second step is to take the mixed powder obtained in the first step and knead it, put it into a molding mold, and keep it under a pressure of 3Mpa for 1 minute to obtain a pre-pressed carbon brick;
[0042] The third step is to heat the pre-pressed carbon brick in the second step to 800°C in the forming mold and pressurize it to 30Mpa. After keeping it for 8 minutes, take it out and process it according to the conventional method.
Embodiment 2
[0044] The hot-pressed fired charcoal bricks of the present invention can also be prepared according to the following weight percentage proportions and steps:
[0045] a. Weight percentage ratio:
[0046] Electric calcined anthracite 50, natural graphite 20, artificial graphite 10, metal silicon 2, silicon oxide 3, aluminum oxide 5, high-temperature pitch 10;
[0047] b. Preparation steps:
[0048] In the first step, the above-mentioned raw materials are crushed and pulverized, and then mixed and proportioned;
[0049] In the second step, after kneading the mixed powder obtained in the first step, put it into a forming mold, and keep it for 1.5 minutes under a pressure of 5Mpa to obtain a pre-pressed carbon brick;
[0050] The third step is to heat the pre-pressed carbon brick in the second step to 1000°C in the forming mold and pressurize it to 40Mpa. After keeping it for 9 minutes, take it out and process it according to the conventional method.
Embodiment 3
[0052] The hot-pressed fired charcoal brick of the present invention can also be prepared according to the following weight percentage proportions and steps:
[0053] a. Weight percentage ratio:
[0054] Electric calcined anthracite 30, natural graphite 10, artificial graphite 20, metal silicon 5, silicon oxide 5, aluminum oxide 10, high-temperature pitch 20;
[0055] b. Preparation steps:
[0056] In the first step, the above-mentioned raw materials are crushed and pulverized, and then mixed and proportioned;
[0057] In the second step, after kneading the mixed powder obtained in the first step, put it into a forming mold, and keep it for 2 minutes under a pressure of 7Mpa to obtain a pre-pressed carbon brick;
[0058] The third step is to heat the pre-pressed carbon brick in the second step to 1100°C in the forming mold and pressurize it to 50Mpa. After keeping it for 10 minutes, take it out and process it according to the conventional method.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com