Soluble salt core for extrusion casting and its making process

A technology of squeeze casting and manufacturing method, which is applied to casting molding equipment, casting molds, cores, etc., can solve the problems of increased manufacturing cost, long manufacturing cycle, processing waste and other problems, and achieves reduced manufacturing equipment requirements, simple manufacturing process, The effect of shortened production cycle

Inactive Publication Date: 2006-03-01
SOUTH CHINA UNIV OF TECH
View PDF1 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the soluble salt core in this method needs to be processed through multiple processes, the production cycle is long, the production cost is increased, and the mechanical processing is easy to bring processing waste.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The outer dimensions of the aluminum alloy bracket are 617×516×210mm, and there are two inner cavities inside, which cannot be formed by core pulling and machining. Both inner cavities have dimensional accuracy requirements and are not allowed to be processed, one of which is 220mm long , 80mm wide, 10-11mm thick, the castings are required to be free of porosity and shrinkage cavity defects, and the tightness test is carried out under 5 atmospheres, and no leakage is required. Squeeze casting of the support was carried out on the LY-1600 vertical press, and the specific implementation is as follows

[0014] 1. Preparation of soluble salt core

[0015] Proportion of soluble salt core: by weight percentage, commercially available edible salt is 70%, adding water glass 10%, high alumina bauxite 16% and water 4%;

[0016] Production process: 1) After roasting commercially available edible salt, dry mix it evenly with high alumina bauxite; 2) Add water glass and mix thoroug...

Embodiment 2

[0031] The outer dimensions of the aluminum alloy bracket are 584×490×190mm, and there are two inner cavities inside, which cannot be formed by core pulling and machining, and both have dimensional accuracy requirements, and are not allowed to be processed. Squeeze casting of the support was carried out on the LY-1600 vertical press, and the specific implementation is as follows

[0032] 1. Preparation of soluble salt core

[0033] Proportion of soluble salt core: by weight percentage, commercially available edible salt is 85%, adding water glass 6%, high alumina bauxite 7% and water 2%;

[0034] Production process: 1) After roasting commercially available edible salt, dry mix it with high-alumina vanadium; 2) Add water glass and mix thoroughly, then add water and mix thoroughly, and let it stand for 5 minutes; 3) Add the above mixture to complete the pre-made 1. In two metal molds with the inner cavity of the salt core shape required by the support, squeeze them tightly on t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The making process of soluble salt core for extrusion casting includes the following steps: mixing roasted marketable table salt in 70-85 wt%, high aluminum bauxite in 7-16 wt%, water glass in 6-10 wt% and water in 2-5 wt% successively and fully and letting stand for over 5 min; applying the mixture into metal mold with required complicated inner cavity shape and pressing in press for densifying, blowing CO2 gas and demolding; and stoving the soluble salt core at 150 deg.c or over for over 2 hr. The soluble salt core can bear the high pressure and high temperature of extrusion casting and can obtain casting with high size precision and high surface smoothness. After the casting is set in water, the soluble salt core will dissolve and disintegrate well. The soluble salt core has less making steps, low production cost, and less corrosion to equipment.

Description

technical field [0001] The invention relates to squeeze casting technology, in particular to a soluble salt core for squeeze casting and a manufacturing method thereof, which is especially suitable for complex inner cavity forming of nonferrous alloy squeeze casting. Background technique [0002] Squeeze casting is an advanced material forming processing technology combining casting and forging. During the processing, the liquid metal is filled, solidified, crystallized and formed under external pressure. The obtained casting has a dense internal structure, high surface finish, and fine grains. , good mechanical properties, high dimensional accuracy and so on. [0003] In the process of squeeze casting, because ordinary sand cores will be broken, deformed, aluminized, etc. during the erosion and extrusion of high-temperature and high-pressure liquid metal, for the inner cavity that cannot be obtained through core pulling and processing, the squeeze ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/02
Inventor 赵海东罗宗强陈维平潘国如张卫文李元元
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com