Novel environment protective adhesives free of formaldehyde and its manufacturing process

A technology of adhesive and formaldehyde, which is applied in the field of new formaldehyde-free environmentally friendly adhesive and its preparation process, can solve the problems affecting the application and promotion of artificial marble, the adhesive cannot reach the strength, and the natural marble is fragile, so as to achieve development and application The effect of broad prospects, strong adhesion, and low cost

Inactive Publication Date: 2006-02-08
忻健存 +1
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the rapid development of modern economy and science and technology, the application range of marble is becoming more and more extensive. However, natural marble is fragile and has many cracks. It is difficult to use it in a large area or deal with special shapes. Some adhesives cannot reach the required strength, which greatly affects the application and promotion of artificial marble

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The invention includes two parts: main agent and auxiliary agent. The main agent is composed of sodium silicate, polyvinyl alcohol, ammonium polypropylene oxide, urea and aluminum sulfate, and the auxiliary agent is composed of sodium fluorosilicate and bentonite.

[0023] The weight of various ingredients in the main agent is:

[0024] Sodium silicate 95.5kg

[0025] Polyvinyl alcohol 0.5kg

[0026] Polypropylene milled ammonium 0.5kg

[0027] Urea 3kg

[0028] Aluminum sulfate 0.5kg

[0029] The weight of various ingredients in the auxiliary agent is:

[0030] Sodium Fluosilicate 17kg

[0031] Bentonite 6kg

[0032] During production, mix sodium silicate, polyvinyl alcohol, polypropylene ammonium ammonium, urea and aluminum sulfate according to the above weight ratio, heat (90-110°C), stir and dissolve completely, and then pack the finished product to make it 100kg of main agent; after mixing and stirring sodium fluorosilicate and bentonite according to the abo...

Embodiment 2

[0035] The weight of various components in the main agent of the present invention is:

[0036] Sodium silicate 98.7kg

[0037] Polyvinyl alcohol 0.1kg

[0038] Polypropylene ammonium 0.1kg

[0039] Urea 1kg

[0040] Aluminum sulfate 0.1kg

[0041] The weight of various ingredients in the auxiliary agent is:

[0042] Sodium Fluosilicate 23kg

[0043] Bentonite 6kg

[0044] During production, mix sodium silicate, polyvinyl alcohol, polypropylene ammonium ammonium, urea and aluminum sulfate according to the above weight ratio, heat (90-110°C), stir and dissolve completely, and then pack the finished product to make it 100kg of main agent; after mixing and stirring sodium fluorosilicate and bentonite according to the above weight ratio, the finished product can be packaged to make 29kg of auxiliary agent.

[0045] When in use, disassemble the prepared main agent and auxiliary agent, and mix and stir.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel environment protective adhesive free of formaldehyde and its manufacturing process, wherein the adhesive comprises main agent and auxiliary agent, the main agent comprises sodium silicate, polyvinyl alcohol, polyacrylamide, urea and aluminium sulphate, the auxiliary agent comprises sodium silicofluoride and alta-mud. The preparing process comprises the steps of mixing, heating, agitating, dissolving, mixing and stirring.

Description

technical field [0001] The invention relates to the fields of artificial wood board processing, building block (including other artificial stone) production and circuit insulation board manufacturing, in particular to a novel formaldehyde-free environmental-friendly adhesive and a preparation process thereof. Background technique [0002] At present, people use a lot of adhesives in the production of wood processing and circuit insulation boards, but the adhesives contain various toxic and harmful substances such as formaldehyde and polychlorinated biphenyls, which cannot be completely solved, pollute the environment, and have long-term effects. human health. [0003] The same problem also exists in the construction industry. When the old buildings are demolished, the building blocks become garbage waste. In order to move and transport these wastes, people have to pay a high price. Someone once tried to use cement to bond buildings. In order to achieve the purpose of second...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J129/04C09J133/26
Inventor 忻健存高莉亚
Owner 忻健存
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products