Impact-modified poly vinyl chloride polymer blend

A polyvinyl chloride, impact modification technology, applied in the field of polyvinyl chloride blends, can solve the problems of poor binding force between core and shell, poor compatibility, poor impact performance of polyvinyl chloride blends, etc. , to achieve the effect of stable heat release, easy polymerization process and easy scale-up

Inactive Publication Date: 2005-05-04
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that in the prior art, when using the core-shell material to modify polyvinyl chloride, due to the poor compatibility between the core and the shell, the binding force between the core-shell is poor, resulting in its modified To solve the problem of poor impact performance of polyvinyl chloride blends, a new impact-modified polyvinyl chloride blend is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1) Preparation of alkyl acrylate polymer

[0033] Add 800 grams of deionized water, 0.5 grams of sodium dodecylbenzenesulfonate, 80 grams of butyl acrylate, and 2 grams of hexamethylene diacrylate into a polymerization kettle equipped with a thermometer, a stirrer, a nitrogen gas introduction device, and a monomer feeding device. alcohol esters. The temperature of the reactant was raised to 70° C. with stirring, and nitrogen gas was continuously blown in. After the reaction was initiated, continuously add the pre-emulsion containing 800 gram deionized water, 10 gram sodium dodecylbenzenesulfonate, 680 gram butyl acrylate, 18 gram hexanediol diacrylate and 7.5 gram ammonium persulfate, about Added within 2 hours. After the dropwise addition, the reaction was continued for 2 hours to obtain an alkyl acrylate polymer latex (A) with a particle diameter of 200 nanometers.

[0034] 2) Preparation of copolymer of alkyl acrylate-methyl methacrylate

[0035] Add 0.3 gram of ...

Embodiment 2

[0052] The preparation process is similar to that of Example 1, except that the amount of methyl methacrylate added in the process 3) in the preparation of the methyl methacrylate polymer is 247 grams. The maximum temperature rise during this process was about 3°C.

[0053] The acrylate core-shell polymer prepared in this example was prepared into a polyvinyl chloride blend according to the preparation process in Example 1, and the performance test results are shown in Table 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a kind of polyvinyl-chlorid blend with impact modification. The invention mainly solves the problem that bad compatibility and bad binding force of nucleus and shell cause the bad impact property of polyvinyl-chlorid blend with impact modification in modifying polyvinyl-chlorid with putamen material by previous technology. In the invention, use acrylic acid carbalkoxy polymer and acrylic acid carbalkoxy-methyl methacrylate copolymer compatiblizing agent as nucleus, use methyl methacrylate as shell, and nucleus-shell are connected with compatiblizing agent. The invention can solve the problems mentioned above through the technical proposal of impact modification polyvinyl-chlorid with acrylate putamen polymer described above, and it can be used in industrial production.

Description

technical field [0001] The invention relates to an impact-modified polyvinyl chloride blend, in particular to a polyvinyl chloride blend using an acrylate core-shell polymer as an impact modifier. Background technique [0002] Polyvinyl chloride is widely used due to its excellent mechanical properties and chemical properties. However, due to its poor impact resistance, polyvinyl chloride resin itself needs to add impact modifiers to improve its impact properties. At present, methacrylic acid is more widely used. Methyl ester-butadiene-styrene graft copolymer (MBS), but because the double bonds in MBS make it easy to degrade under ultraviolet light, the impact performance of polyvinyl chloride modified with MBS will decrease when it is used outdoors for a long time More, poor weather resistance. Weatherable PVC impact modifiers are typically based on acrylate core-shell polymers and have been widely used in outdoor applications such as pipes, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06
Inventor 周文乐赵申谭宏亮王玮郁俭乙王荣伟
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap