Spherical and microporous composite zine oxide-SiO2 particles and preparing process and usage thereof

A technology of silica and composite particles, applied in catalyst activation/preparation, metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, etc., can solve the problem of high cost of ZnO, low product quality, and power consumption It is easy to prepare, easy to popularize and apply, and has a wide range of uses.

Inactive Publication Date: 2002-11-27
TECHNICAL INST OF PHYSICS & CHEMISTRY - CHINESE ACAD OF SCI
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are some disadvantages, and it is not easy to obtain monodisperse and uniform ZnO particles with controllable particle size.
The direct method uses zinc oxide as a raw material, reduces the zinc oxide to gaseous zinc, and then introduces air to oxidize and shape the product, but the product quality is not high, especially the content of low melting point impurities is high; the indirect method uses zinc ingots As a raw material, zinc vapor is passed into the air to oxidize to obtain zinc oxide, but the cost is high and the total power consumption is large; the liquid phase chemical method uses a soluble metal salt solution to prepare ultrafine powder, but the particle size prepared by the previous liquid phase method is difficult control, difficult to redistribute
[0009] When ZnO particles are used as excellent pigments and some special purposes, it is usually the outer surface of the particles that can actually be utilized and function, while the inner core of the particles does not play a role, so the cost of ZnO in the form of ZnO as the core is high, in fact is a huge waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spherical and microporous composite zine oxide-SiO2 particles and preparing process and usage thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0037] In the dispersed silicon dioxide (particle size is 500 nanometers) ethanol-water mixed solution, at the same time, double-injection drips triethanolamine and zinc acetate solution with a molar concentration ratio of 66:1 to make silicon dioxide-triethanolamine-acetic acid The initial molar ratio of zinc is 11:300:8, and the dropping time is 80 minutes. After the temperature is raised to 85° C., the reaction is stirred for 90 minutes, aged for 8.0 hours, and a white turbid solution is obtained, which is centrifuged, and the obtained centrifuged product is vacuum-dried. Composite particles of zinc oxide and silicon dioxide with a spherical shape and micropores were obtained, with a particle diameter of 560 nanometers, that is, zinc oxide particles coated with a thickness of about 60 nanometers. Example 3

Embodiment 3

[0038] (1). 0.2 g of the particles prepared according to Example 1 were ultrasonically dispersed into a 1:1 mixed solvent of ethanol-water.

[0039] (2). Simultaneously double-injection dripping molar concentration ratio is 66: 1 triethanolamine and zinc acetate solution again, makes the initial molar ratio of silicon dioxide-triethanolamine-zinc acetate be 11: 100: 2, and its dropping time is For 40 minutes, heat up to 80°C and react under stirring for 90 minutes, age for 6.0 hours to obtain a white turbid solution, centrifuge, and vacuum-dry the obtained centrifuged product to obtain spherical and microporous zinc oxide and silicon dioxide composite particles , with a particle size of 220 nanometers, that is, zinc oxide particles coated with a thickness of about 50 nanometers. Example 4

Embodiment 4

[0040] In the ethanol-water mixed solution containing silicon dioxide with a particle size of 300 nanometers and a volume ratio of 2:1, a solution of triethanolamine and zinc acetate with a molar concentration ratio of 80:1 was added dropwise at the same time to make the silicon dioxide -The initial molar ratio of triethanolamine-zinc acetate is 11:400:1, and its dropwise addition time is 60 minutes. After heating up to 90°C, it reacts for 120 minutes under stirring, and ages for 10.0 hours to obtain a white turbid solution, which is centrifuged to obtain The centrifuged product was vacuum-dried to obtain composite particles of zinc oxide and silicon dioxide with a particle size of 380 nanometers having a spherical shape and micropores, that is, zinc oxide particles coated with a thickness of about 80 nanometers. Example 5

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A composite particle material containing spherical and miniporous zine oxide and SiO2 is prepared through such steps as dispersing SiO2 particles in the alcohol-water mixed solvent, preparing the aqueous solution of zine salt, preparing the aqueous solution of hydramine compound, adding the last two solutions to the first one, ageing, and centrifugal separation. The said material can be used for photon crystal assembly, electrorheopectic material and high-grade paint.

Description

technical field [0001] The invention belongs to the field of semiconductor inorganic nanomaterials, in particular to spherical and microporous zinc oxide (ZnO) and silicon dioxide (SiO 2 ) composite particle and its preparation method and application. Background technique [0002] ZnO, commonly known as zinc white, is a highly functional fine inorganic material that has been studied more. It is an important ceramic, semiconductor and catalytic material, and nano-ZnO is widely used due to its excellent optical, electrical, chemical and biological effects. Used in chemical industry, electronics, biology, coatings, sensors, dielectric materials, plastics, ink, paper, chemical fiber, rubber and other fields, such as: [0003] (1) Application in cosmetics - new sunscreens and antibacterial agents. In recent years, countries have actively carried out research and development of sunscreens. Such as ZnO, TiO 2 Sunscreen agents such as a batch of inorganic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/06B01J37/02C04B35/628C09C1/04C09C3/00
Inventor 唐芳琼夏海龙
Owner TECHNICAL INST OF PHYSICS & CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com