Method of manufacturing oriented silicon steel strip in razor-thin

A manufacturing method and technology of oriented silicon steel, which is applied in the direction of manufacturing tools, metal rolling, metal rolling, etc., can solve the problems that affect the operation rate and hourly output, the silicon steel sheet is brittle, and the magnetic performance is not high, so as to reduce broken edges and The effect of broken belt phenomenon, large reduction rate and stable magnetic performance

Inactive Publication Date: 2007-01-17
NORTHEASTERN UNIV LIAONING
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although very thin strips of silicon steel can be made by this method, due to the high brittleness of silicon steel sheets, it brings great difficulties to cold rolling. Accidents such as edge cracking, strip breaking, and roll wrapping often occur, which affect the operating rate and hourly output, and also affect the cost. , the magnetic performance is not high, and it is very unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The 0.3mm thick secondary recrystallized finished oriented silicon steel is used as raw material, and its chemical composition is (mass fraction,%): C0.02, Si3.12, Mn0.12, S0.02, Cu0.01, N0.01, P2 +H 2 (1:3) Annealing at 950°C for 10 minutes in a mixed atmosphere annealing furnace. The magnetic properties of the strips after annealing were measured using ring samples. B 10 At 1.93T, P 15 / 400 =13W / Kg.

Embodiment 2

[0021] The 0.3mm thick secondary recrystallized finished oriented silicon steel is used as raw material, and its chemical composition is (mass fraction,%): C0.01, Si3.10, Mn0.085, S0.03, Cu0.01, N0.001, P0.009, I Fe. After pickling to remove the surface insulation layer, on a four-roll asynchronous cold rolling mill 90mm / 200mm×200mm, cold rolling to 0.08mm by asynchronous speed ratio 1.17 rolling method, and 850 ° C in a pure hydrogen annealing furnace for 20 minutes annealing. The magnetic properties of the strips after annealing were measured using ring samples. B 10 At 1.98T, P 15 / 400 =14W / Kg.

Embodiment 3

[0023] The 0.3mm thick secondary recrystallized finished oriented silicon steel is used as raw material, and its chemical composition is (mass fraction,%): C0.02, Si3.13, Mn0.06, S0.002, Cu0.01, N0.004, P10 At 1.94T, P 15 / 400 = 11W / Kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A process for preparing the very-thin oriented silicon steel band with high and stable magnetic property includes such steps as acid washing of recrystallized and oriented silicon steel plate, cold rolling to make its thickness reach 0.06-0.1 mm, heat treating at 700-980 deg.C in protective atmosphere, coating and annealing.

Description

technical field [0001] The invention belongs to the technical field of metal strip rolling, in particular to a method for manufacturing an ultra-thin strip of grain-oriented silicon steel. Background technique [0002] Silicon steel is an indispensable and important functional material in the electric power, motor, and electronics industries. Grain-oriented silicon steel is mainly used as a soft magnetic material for iron cores such as electrical machinery and transformers. With the development of the electronics industry, the requirements for silicon steel sheets are becoming more and more stringent. From the viewpoint of energy saving, it is always desired to increase the magnetic induction and reduce the iron loss. Especially since 1970, the iron loss of grain-oriented silicon steel sheet has been continuously reduced, and the output and quality have been greatly improved, but there is still room for further reduction of iron loss of silicon steel sheet. The measures ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/22B21B45/02B05D7/14C21D9/52
Inventor 高秀华齐克敏邱春林刘恩
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com