High-brightness black composite nylon material as well as preparation method and application thereof
A nylon and polyamide technology, applied in the field of high-gloss black composite nylon material and its preparation, can solve the problems of increased density of high-gloss black nylon, high price of transparent nylon material, influence of blackness, etc., to reduce the crystallinity, improve the Transparency, low cost effect
Pending Publication Date: 2022-07-29
SHANGHAI KINGFA SCI & TECH +1
View PDF9 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, due to the addition of silicon dioxide and silicone powder, the density and blackness of high-gloss black nylon are respectively affected.
In addition, compared with conventional nylon materials, transparent nylon materials are expensive, which makes them encounter greater resistance in the promotion and application of high-gloss black materials in automobiles and in the process of domestic marketization
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 11
[0072] The high-brightness black composite nylon material of Example 3 is used to make a sample plate, and the performance test is carried out. The results are: the blackness value is 24, the appearance has no pitting, and the linear wear resistance is 88%. It can be shown that the high-gloss black composite nylon material provided by the present invention can be suitable for preparing vehicle exterior parts with high requirements on appearance and wear resistance.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
length | aaaaa | aaaaa |
degree of grafting | aaaaa | aaaaa |
Login to view more
Abstract
The invention discloses a high-brightness black composite nylon material and a preparation method thereof. The high-brightness black composite nylon material is prepared from the following raw materials in parts by weight: 65-90 parts of nylon 6, 10-35 parts of nylon 56, 0.1-1 part of a functional nucleating agent, 0.15-0.6 part of carbon black and 0.4-1 part of an auxiliary agent, the functional nucleating agent is a polyamide-amine dendrimer grafted carboxylated carbon nano tube. The high-brightness black composite nylon material prepared by the invention has the advantages of low cost, good appearance and scratch resistance, meets the performance requirements of good appearance and scratch resistance when the high-brightness black composite nylon material is applied to automobile exterior trimming, and meanwhile, compared with a high-brightness black material which takes special nylon as a matrix in the market at present, the high-brightness black composite nylon material has the advantages of low cost, good appearance and scratch resistance. The obvious price advantage is realized.
Description
technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high-brightness black composite nylon material and a preparation method and application thereof. Background technique [0002] As we all know, the quality of the car is reduced by half, and the fuel consumption is also reduced by nearly half. Therefore, with the increasing demand for environmental protection and energy saving, the lightweight of automobiles, that is, reducing the curb weight of automobiles as much as possible on the premise of ensuring the strength and safety performance of automobiles has become the main theme of global automobile development. Therefore, in recent years, the proportion of plastic parts in auto parts has continued to expand, and a large number of plastic parts have been used for exterior parts. At present, parts with a high-gloss black appearance similar to piano black are more and more recognized by consumers, and the exterior parts...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08K3/04C08K9/04
CPCC08L77/02C08L2205/24C08L77/06C08K3/04C08K9/08C08K9/04C08K3/041
Inventor 诸金陈平绪叶南飚张永李明昆李欣达季得运李鹏浩林荣涛薛飞
Owner SHANGHAI KINGFA SCI & TECH
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap