Glue preparation method by dissolving chitin and vinylon fiber with ionic liquid

A vinylon fiber and ionic liquid technology, applied in the field of spinning engineering, can solve the problems of high price, difficulty in blending and making glue, and high cost, and achieve the effect of reducing production cost and solving the problem of blending and making glue.

Pending Publication Date: 2022-07-12
LUOYANG CHANGLONG CHEM TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pure chitin fiber lacks the physical and mechanical properties required for post-textile processing, and the cost is high, expensive, and its popularization and application are limited.
Composite fibers with excellent performance can be produced by blending with other materials, but it is difficult to blend and make rubber. How to solve the problem of blending chitin with other materials has become a technical problem that has been difficult to solve for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Weigh and grind 5g of chitin raw material to 300 mesh, add 10g of vinylon to a container containing 100g of 1,3-diethylimidazolium diethyl phosphate, stir and dissolve in an oil bath at 120 °C until a transparent glue is formed The concentration of the transparent glue solution is 5-25%, there is no layering and no impurities, and then the spinning glue solution is prepared by vacuum degassing in the environment of -0.95MPa.

Embodiment 2

[0016] Weigh and pulverize 4 g of chitin raw materials to 400 meshes, add 12 g of vinylon to a container containing 100 g of 1-ethyl-3-methylimidazolium dimethyl phosphate, stir and dissolve in an oil bath at 120 ° C until the formation of Transparent glue solution, the concentration of transparent glue solution is 5-25%, no layering and no impurities, and then the spinning glue solution is prepared by vacuum degassing in the environment of -0.95MPa.

Embodiment 3

[0018] Weigh and pulverize 6 g of chitin raw materials to 500 meshes, add 13 g of vinylon to a container containing 100 g of dimethyl 1-butyl-3-methylimidazole phosphate, stir and dissolve in an oil bath at 120 ° C until the formation of Transparent glue solution, the concentration of transparent glue solution is 5-25%, no layering and no impurities, and then the spinning glue solution is prepared by vacuum degassing in the environment of -0.95MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a glue preparation method by dissolving chitin and vinylon fibers with an ionic liquid, which comprises the following steps: adding crushed chitin and polyvinyl butyral into a container filled with the ionic liquid, stirring and dissolving under the condition of 120 DEG C oil bath until a transparent glue solution is formed, the concentration of the transparent glue solution is 5-25%, and the transparent glue solution is free from layering and impurities; then carrying out vacuum defoaming in an environment of-0.95 MPa to obtain a spinning glue solution; vinylon and chitin can be dissolved in the same ionic liquid at the same time, the problem of blending of chitin and vinylon for glue preparation is well solved, and the production cost is greatly reduced.

Description

technical field [0001] The invention relates to the technical field of spinning engineering, in particular to a glue-making method for dissolving chitin and vinylon fibers in an ionic liquid. Background technique [0002] Chitin is a linear polysaccharide biopolymer that widely exists in the shells of insects, aquatic crustaceans and the cell walls of seaweeds, such as crabs, shrimps, gong fish bones, egg shells, bee bees, fungi, etc. The amount is second only to plant fibers. Chitosan, also known as chitosan, has unsaturated cationic groups in its molecular structure, so it has a strong adsorption effect on all kinds of negatively charged harmful substances and harmful bacteria, so that it can absorb harmful bacteria. The activity is inhibited, making it inactive, so as to achieve the purpose of antibacterial. It not only has a structure similar to plant fiber, but also has a structure similar to that of human bone collagen. It has good compatibility with the human body a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/18D01F8/10D01D1/02
CPCD01F8/18D01F8/10D01D1/02Y02P20/54
Inventor 周永生李军锋
Owner LUOYANG CHANGLONG CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com