Self-adhesive waterproof roll cementing material and waterproof roll prepared from same

A technology of self-adhesive waterproof membrane and waterproof membrane, which is applied in the direction of adhesives, adhesive types, asphalt material adhesives, etc., can solve the problems of poor flame retardancy of self-adhesive membranes, reduce temperature sensitivity, improve High temperature stability and aging resistance, effect of reducing thermal volatilization

Pending Publication Date: 2022-06-21
安徽省奥佳建材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention: the flame retardancy of the self-adhesive coil is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-adhesive waterproof roll cementing material and waterproof roll prepared from same
  • Self-adhesive waterproof roll cementing material and waterproof roll prepared from same
  • Self-adhesive waterproof roll cementing material and waterproof roll prepared from same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Organically modified nano palygorskite comprises the following steps:

[0030] A1. Mix 10 mL of HCl solution with a concentration of 0.1 mol / L and 3 g of palygorskite, stir vigorously in a 60°C water bath, and then stand, suction filtration to obtain a solid, wash the solid to neutrality, and vacuum dry at 110°C. to obtain pretreated palygorskite;

[0031] A2. Add 3 g of pretreated palygorskite into 280 mL of xylene, ultrasonically disperse for 0.5 h, add 3 mL of γ-aminopropyltriethoxysilane, heat up to 80 °C, stir at constant temperature for 10 h, and then filter, wash and After vacuum drying at 60°C, the organically modified nano-palygorskite was obtained.

Embodiment 2

[0033] Organically modified nano palygorskite comprises the following steps:

[0034] A1. Mix 15 mL of HCl solution with a concentration of 0.1 mol / L and 3.5 g of palygorskite, stir vigorously in a water bath at 60 °C, and then let stand, suction filtration to obtain a solid, wash the solid to neutrality, and vacuum dry at 110 °C , to obtain pretreated palygorskite;

[0035] A2. Add 4g of pretreated palygorskite into 300mL of xylene, ultrasonically disperse for 0.5h, add 4mL of γ-aminopropyltriethoxysilane, heat up to 80°C, stir at constant temperature for 10h, and then filter, wash and After vacuum drying at 60°C, the organically modified nano-palygorskite was obtained.

Embodiment 3

[0037] Organically modified nano palygorskite comprises the following steps:

[0038] A1. Mix 20 mL of HCl solution with a concentration of 0.1 mol / L and 4 g of palygorskite, stir vigorously in a water bath at 60 °C, then let stand, and filter the solid to obtain a solid. Wash the solid to neutrality, and vacuum dry at 110 °C. to obtain pretreated palygorskite;

[0039] A2. Add 5g of pretreated palygorskite into 320mL of xylene, ultrasonically disperse for 0.5h, add 5mL of γ-aminopropyltriethoxysilane, heat up to 80°C, stir at constant temperature for 10h, and then filter, wash and After vacuum drying at 60°C, the organically modified nano-palygorskite was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a self-adhesion waterproof coiled material cementing material and a waterproof coiled material prepared from the same, and belongs to the technical field of building waterproof engineering, the self-adhesion waterproof coiled material cementing material comprises the following raw materials: type I waterproof coiled material asphalt, ethylene tar, SBS, organic modified nano palygorskite, ammonium polyphosphate, naphthenic oil and modified chitosan; the modified chitosan is prepared by the following steps: dissolving chitosan in a methanol / acetic acid mixed solution with a volume ratio of 10: 1, heating to 50 DEG C, preserving heat, adding a flame retardant, heating to reflux, and reacting to obtain the modified chitosan. In the technical scheme, the palygorskite is a natural mineral microfiber, and after the palygorskite is added into the asphalt, the movement of asphalt molecules is limited, so that the viscosity of the asphalt is further increased, and the stiffness modulus of the asphalt is improved; in addition, a reinforced network composed of a large number of microfibers can improve the integrity of the asphalt, reduce the generation of microcracks on the surface of the asphalt, and contribute to improving the cohesive work of the asphalt and resisting the erosion of water.

Description

technical field [0001] The invention belongs to the technical field of construction waterproofing engineering, and particularly relates to a self-adhesive waterproofing membrane binding material and a waterproofing membrane prepared therefrom. Background technique [0002] With the development of the economy and the progress of the times, the requirements for building materials are getting higher and higher, and the original building materials can no longer meet the needs of the development of the times. Many buildings have reduced their service life due to water erosion, and people are paying more and more attention to the quality of waterproof materials. At present, elastomer (SBS) modified asphalt waterproofing membrane is still the mainstream product, especially when the roof is exposed, it is difficult to be replaced by other materials due to its excellent high temperature resistance. The coil needs to be hot-melted during construction. When the blowtorch is baked, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J195/00C09J11/04C09J11/08C09J7/21C08B37/08
CPCC09J195/00C09J11/04C09J11/08C09J7/21C08B37/003C08K2201/011C08L2201/02C08L2201/08C09J2203/346C09J2400/263C09J2301/124C09J2301/408C08L95/00C08L53/02C08L91/00C08L5/08C08K9/06C08K7/10
Inventor 梁子双梁本树陆子明
Owner 安徽省奥佳建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More