PC/PBT alloy over-CTI plastic and preparation method thereof

A PBT resin and plastic technology, applied in the field of plastic preparation, can solve the problems of uneven mixing of plastic raw materials, affecting the quality of plastic preparation, reducing plastic practicability, etc., to achieve the effects of improving cooling efficiency, being suitable for popularization and use, and being convenient for granulation

Pending Publication Date: 2022-06-14
湖南登科材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many problems in the process of plastic preparation, such as the uneven mixing of raw materials in the preparation of some existing plastics, which affects the quality of plastic preparation, and at the same time, the uneven mixing of some raw materials in the melting process affects the use and reduces the overall practicability of plastics. , not easy to operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC/PBT alloy over-CTI plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A PC / PBT alloy over-CTI plastic and a preparation method thereof, the formula is as follows:

[0022] The raw materials include by weight: 30 parts of PC resin, 20 parts of PBT resin, 3 parts of compatibilizer, 18 parts of wollastonite, and 29 parts of metal oxide.

[0023] A preparation method of PC / PBT alloyed CTI plastic, the preparation method comprises the following steps:

[0024] (1) Weigh 30 parts by weight of PC resin, 20 parts of PBT resin, 3 parts of compatibilizer, 16 to 20 parts of wollastonite, and 20 to 30 parts of metal oxide, and mix them in a storage bucket to obtain a premixed material, spare;

[0025] (2) mixing in a mixer, adding the premix in step (1) to the mixer, mixing the premix in the mixer for 15 minutes, and mixing the mixture evenly and storing it in a storage tank for subsequent use;

[0026] (3) The extruder is operated, and the mixture in the storage tank in step (2) is continuously and stably added to the twin-screw extruder, melted a...

Embodiment 2

[0037] A PC / PBT alloy over-CTI plastic and a preparation method thereof, the formula is as follows:

[0038] 30 parts of PC resin, 20 parts of PBT resin, 3 parts of compatibilizer, 16 parts of wollastonite, and 21 parts of metal oxide.

[0039] A preparation method of PC / PBT alloyed CTI plastic, the preparation method comprises the following steps:

[0040](1) Weigh 30 parts by weight of PC resin, 20 parts of PBT resin, 3 parts of compatibilizer, 16 to 20 parts of wollastonite, and 20 to 30 parts of metal oxide, and mix them in a storage bucket to obtain a premixed material, spare;

[0041] (2) mixing in a mixer, adding the premix in step (1) to the mixer, mixing the premix in the mixer for 15 minutes, and mixing the mixture evenly and storing it in a storage tank for subsequent use;

[0042] (3) The extruder is operated, and the mixture in the storage tank in step (2) is continuously and stably added to the twin-screw extruder, melted and extruded, cooled and pelletized to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses PC / PBT alloy over-CTI plastic and a preparation method thereof. The plastic is prepared from the following raw materials in parts by weight: 30 parts of PC resin, 20 parts of PBT resin, 3 parts of compatilizer, 16 to 20 parts of wollastonite and 20 to 30 parts of metal oxide. The preparation method of the PC / PBT alloy over-CTI plastic is characterized by comprising the following steps: weighing 30 parts by weight of PC resin, 20 parts by weight of PBT resin, 3 parts by weight of compatilizer, 16-20 parts by weight of wollastonite and 20-30 parts by weight of metal oxide, and mixing in a storage barrel to obtain a premix for later use; mixing in a mixer, and operating in an extruder. According to the PC / PBT alloy over-CTI plastic and the preparation method thereof, the operation is simple, the plastic preparation raw materials are conveniently and uniformly mixed, stable and uniform melt extrusion in a double-screw extruder is facilitated, meanwhile, the molten raw materials are conveniently and rapidly cooled, the cooling efficiency is improved, subsequent granulation is facilitated, the plastic manufacturing time is saved, and the plastic manufacturing efficiency is improved.

Description

technical field [0001] The invention relates to a plastic and a preparation method thereof, in particular to a PC / PBT alloy per-CTI plastic and a preparation method thereof, belonging to the technical field of plastic preparation. Background technique [0002] Plastic is a polymer compound that is made of monomer as raw material and polymerized by addition or polycondensation reaction. Its resistance to deformation is moderate, between fiber and rubber. It is composed of additives such as additives and pigments; the main component of plastic is resin; resin refers to a polymer compound that has not been mixed with various additives; the term resin was originally named after the lipids secreted by animals and plants, such as rosin, Shellac, etc.; resins account for about 40% to 100% of the total weight of plastics; the basic properties of plastics are mainly determined by the nature of the resins, but additives also play an important role; some plastics are basically composed...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08K3/36C08K3/22B29B9/06B29B9/12
CPCC08L69/00B29B9/06B29B9/12C08K2003/222C08K2003/2227C08L67/02C08K3/36C08K3/22
Inventor 肖广兴李鹏建熊世杰邓志勇罗宋群
Owner 湖南登科材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap