Oxygen barrier layer and self-flat-topped lattice point digital flexible resin plate comprising same and provided with convex parts with gritted surfaces

A technology of flexible resin and oxygen barrier layer, which is applied in the field of digital flexible resin plate of self-flat-top dots, which can solve the problems of high cost and so on.

Pending Publication Date: 2022-05-13
LUCKY HUAGUANG GRAPHICS
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Requires different plate washing equipment than usual, and therefore requires higher cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oxygen barrier layer and self-flat-topped lattice point digital flexible resin plate comprising same and provided with convex parts with gritted surfaces
  • Oxygen barrier layer and self-flat-topped lattice point digital flexible resin plate comprising same and provided with convex parts with gritted surfaces
  • Oxygen barrier layer and self-flat-topped lattice point digital flexible resin plate comprising same and provided with convex parts with gritted surfaces

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059]The preparation method of the coating solution for the oxygen barrier layer can be as follows: dissolve the flexible adhesive with oxygen barrier effect and the water-soluble resin containing amine groups in water, slowly add the aqueous solution of the water-based flexible resin containing carboxyl groups under stirring, and finally add Surfactant, stirring, to obtain an oxygen barrier layer coating solution; or, the flexible adhesive with oxygen barrier effect and the water-based carboxyl group-containing flexible resin are dissolved in water, and under stirring, slowly add the water-soluble resin containing amine group Aqueous solution, finally add surfactant, stir to obtain oxygen barrier layer coating liquid.

[0060] Water is used as a solvent, and when the oxygen barrier layer is formed after coating on the photoreceptor, the water is evaporated.

[0061] The surfactant here is a leveling agent, and the leveling agent is a commonly used leveling agent for the oxyg...

Embodiment 1

[0102] This patent is realized by adding an oxygen barrier functional layer on the basis of the digital flexographic plate, and the technology involved in the digital flexographic plate is omitted.

[0103] In the preparation of the coating solution for the oxygen barrier layer, the total weight of the following ingredients is 80 grams, and the following raw materials are prepared in terms of dry weight percentage:

[0104] Polyvinylpyrrolidone K30, available in the market, 80%;

[0105] Molecular weight is 2000 amine-containing water-soluble resin PD-2000, from Lucky Chemical Company, 10%;

[0106] Carboxyl-containing flexible resin SR, from Lucky Chemical Company, 5%;

[0107] Surfactant - perfluorobutyl xanthyl fluoride, 5%.

[0108] In addition to the above ingredients,

[0109] water, 920 g.

[0110] The preparation method of the coating solution for the oxygen barrier layer is as follows: dissolve polyvinylpyrrolidone and SR resin in water, slowly add PD-2000 aqueous...

Embodiment 2

[0118] In the preparation of the coating solution for the oxygen barrier layer, the following ingredients have a total weight of 80 grams, and are prepared from the following raw materials by weight percentage:

[0119] Polyvinylpyrrolidone K90, available in the market, 50%;

[0120] The amine-containing water-soluble resin PD-70000 resin with a molecular weight of 70,000 is from Lucky Chemical Company, 30%;

[0121] Carboxyl-containing flexible resin SR, from Lucky Chemical Company, 12.5%;

[0122] Surfactant - perfluorobutyl xanthyl fluoride, 7.5%.

[0123] In addition to the above ingredients,

[0124] water, 920 g.

[0125] The preparation method of the oxygen barrier layer coating solution is as follows: dissolve polyvinylpyrrolidone and SR water together, under high-speed stirring (1000-2000 rpm), slowly add PD-70000 aqueous solution, finally add surfactant, and stir properly After that, it becomes an oxygen barrier layer coating liquid. It is also possible to excha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides an oxygen barrier layer and a self-flat-topped lattice point digital flexible resin plate containing the oxygen barrier layer, wherein the surface of a convex part of the self-flat-topped lattice point digital flexible resin plate is sanded. The oxygen barrier layer contains particles with the size of 0.01-10 microns; the particles in the oxygen barrier layer are formed by reacting amido-containing water-soluble resin and carboxyl-containing polymer resin in water, that is, the particles are directly formed in the oxygen barrier layer coating liquid, the process of dispersing solid particles is omitted, and the purpose that the particles are contained in the oxygen barrier layer is achieved. The oxygen barrier layer coating liquid is coated on the photosensitive elastomer, namely the ultraviolet polymerization relief printing plate forming layer, the surface of the sand mesh has higher printing ink transfer capability, the ink layer of the printed matter is thicker, and the color rendition is more vivid.

Description

technical field [0001] The invention relates to a flexographic printing plate that can be digitally imaged, in particular to an oxygen barrier layer and a self-flat top dot digitized flexible resin plate whose surface is grained on a raised portion. This application belongs to the green printing materials of the sub-direction 3.19 Eco-environmental materials under the key direction of 3.1 New functional material industry in the 3 New Material Industry of the Strategic Emerging Industry Catalog. Background technique [0002] Digitally imageable flexographic printing plates are basically known. It comprises at least one dimensionally stable support film, a photopolymerizable elastomeric layer and a digitally imageable layer. Examples of digitally imageable layers are laser ablatable layers, inkjet printer writeable layers, or thermal imaging layers, where laser ablatable layers are currently popular in the digital flexographic market. [0003] The laser ablatable layer, also...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B41C1/00B41N1/12B41N1/22B41N3/03
CPCB41C1/00B41N1/12B41N1/22B41N3/03
Inventor 王晓阳高英新陈雷黄永山许文然李喜乐黄黎明马秋安王国才李志勇王向利陈瑞芳马天如
Owner LUCKY HUAGUANG GRAPHICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products