Long-life cement concrete bridge multi-medium waterproof composite layer

A cement concrete and multi-media technology, applied in bridges, bridge parts, bridge materials, etc., can solve problems such as difficult to ensure the coordination of stress and strain, low bond strength, etc.

Pending Publication Date: 2022-04-15
SOUTHEAST UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This is because, from the point of view of the concrete bridge deck pavement system, the elastic modulus of the asphalt concrete pavement layer and the cement concrete slab differs by tens of times, while the elastic modulus of the existing bonding course materials is small, and they are different from the concrete slab The bonding strength between them is low, and the single-layer structure is difficult to ensure the coordination of stress and strain of the entire pavement system under load.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-life cement concrete bridge multi-medium waterproof composite layer
  • Long-life cement concrete bridge multi-medium waterproof composite layer
  • Long-life cement concrete bridge multi-medium waterproof composite layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The three-component two-component binder, rubber-modified asphalt and single-size gravel used in the multi-media waterproof composite layer of the above-mentioned long-life cement concrete bridge are composed of simultaneous construction, and the content is as follows according to the amount of spreading:

[0028] Two-component binder 1.0kg / m 2 ;

[0029] Rubber modified asphalt 2.0kg / m 2 ;

[0030] Single particle size crushed stone 60% coverage.

[0031] The two-component adhesive is a two-component epoxy resin adhesive, and the curing strength reaches more than 60% of the final strength within 30 minutes, and the final strength exceeds 10Mpa.

[0032] The two-component epoxy resin binder adopts bisphenol F type epoxy resin, which is Taiwan Nanya NPEF-170 bisphenol F type epoxy resin.

[0033] The rubber-modified asphalt is 40% waste tire rubber powder-modified asphalt with a softening point of not less than 75°C. It is purchased from Jiangsu Baoli Asphalt Company...

Embodiment 2

[0049] The three-component two-component binder, rubber-modified asphalt and single-size gravel used in the multi-media waterproof composite layer of the above-mentioned long-life cement concrete bridge are composed of simultaneous construction, and the content is as follows according to the amount of spreading:

[0050] Two-component binder 1.2kg / m 2 ;

[0051] Rubber modified asphalt 1.8kg / m 2 ;

[0052] Single particle size gravel 65% coverage.

[0053] The two-component adhesive is a two-component epoxy resin adhesive, and the curing strength reaches more than 60% of the final strength within 30 minutes, and the final strength exceeds 10Mpa.

[0054] The two-component epoxy resin binder adopts bisphenol F type epoxy resin, which is Taiwan Nanya NPEF-170 bisphenol F type epoxy resin.

[0055] The rubber-modified asphalt is 40% waste tire rubber powder-modified asphalt with a softening point of not less than 75°C. It is purchased from Jiangsu Baoli Asphalt Company and is...

Embodiment 3

[0071] The three-component two-component binder, rubber-modified asphalt and single-size gravel used in the multi-media waterproof composite layer of the above-mentioned long-life cement concrete bridge are composed of simultaneous construction, and the content is as follows according to the amount of spreading:

[0072] Two-component binder 1.4kg / m 2 ;

[0073] Rubber modified asphalt 1.6kg / m 2 ;

[0074] Single particle size crushed stone 70% coverage.

[0075] The two-component adhesive is a two-component epoxy resin adhesive, and the curing strength reaches more than 60% of the final strength within 30 minutes, and the final strength exceeds 10Mpa.

[0076] The two-component epoxy resin binder adopts bisphenol F type epoxy resin, which is Taiwan Nanya NPEF-170 bisphenol F type epoxy resin.

[0077] The rubber-modified asphalt is 40% waste tire rubber powder-modified asphalt with a softening point of not less than 75°C. It is purchased from Jiangsu Baoli Asphalt Company...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A long-service-life cement concrete bridge multi-medium waterproof composite layer is characterized in that a waterproof bonding composite layer is sequentially composed of a bi-component adhesive layer and a rubber modified asphalt layer outwards along a bridge floor, single-particle-size broken stones are inserted between the bi-component adhesive layer and the rubber modified asphalt layer in a penetrating mode, the bi-component adhesive layer is formed by bi-component bonding materials, and the rubber modified asphalt layer is formed by the bi-component bonding materials. The rubber modified asphalt layer is formed by rubber modified asphalt, the rubber modified asphalt layer, the bi-component bonding material, the rubber modified asphalt and the single-particle-size gravel are constructed synchronously, and according to the spreading amount, the content of the bi-component bonding material is 1.0-1.5 kg / m < 2 >, the content of the rubber modified asphalt is 1.6-2.0 kg / m < 2 >, and the coverage rate of the single-particle-size gravel is 60-70%. The waterproof composite layer material disclosed by the invention has outstanding waterproofness, durability, bonding strength and shearing strength, and can be well applied to bridge deck pavement of a cement concrete bridge, so that the service life of the concrete bridge deck is prolonged.

Description

technical field [0001] The invention belongs to the technical field of bridge deck paving materials, in particular to a long-life cement concrete bridge multi-media waterproof composite layer. Background technique [0002] The waterproof bonding layer is an important functional layer to ensure that the asphalt concrete pavement and the cement concrete bridge deck work together. Its function is not only to firmly bond the pavement layer and the bridge deck to ensure the coordination of deformation and the overall bearing capacity of the two, but also to prevent moisture from penetrating into the concrete bridge deck structure. Serious early damage phenomena of bridge deck pavement, such as asphalt layer shifting, exposed bridge deck, cracking, etc., have appeared in many concrete bridge actual projects. The survey found that most of these diseases are caused by the failure of interlayer bonding. [0003] The commonly used waterproof bonding layer for concrete bridge deck pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01D19/08E01D21/00C04B26/26E01D101/24C04B111/27
Inventor 陈先华龚晓静王国清邱文利王志斌许忠印权恒友张博王洪涛陈攀李海冬张莹刘栋黄威翰林瑞轻杨军
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products