Modified carbon fiber reinforced polymer matrix composite material

A technology of fiber reinforcement and composite materials, applied in the field of composite materials, can solve problems such as high cost and complicated preparation process, and achieve the effects of increased strength, increased tensile strength of monofilaments, and reduced contact angle

Active Publication Date: 2022-04-01
SICHUAN UNIV
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ILSS of the composite material prepared by this method needs to be further improved
In addition, the method reported in the literature requires multiple layers of self-assembled GO / SiO on the surface of carbon fibers. 2 Multi-layer film, the preparation process is more complicated and the cost is higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified carbon fiber reinforced polymer matrix composite material
  • Modified carbon fiber reinforced polymer matrix composite material
  • Modified carbon fiber reinforced polymer matrix composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Embodiment 1, prepare the carbon fiber after chitosan encapsulation

[0053] Step 1: Preparation of OCFs

[0054] Sizing carbon fiber T700 (purchased from Japan Toray Co., Ltd.) was refluxed in acetone at 90° C. for 60 h by Soxhlet extraction method, and then vacuum-dried overnight at 80° C. for later use. The desized carbon fibers are named DCFs. Subsequently, the DCFs were placed in AgNO at 70 °C 3 / K 2 S 2 o 8 solution (in solution, AgNO 3 The concentration is 0.01mol / L, K 2 S 2 o 8 concentration of 0.1mol / L) for 1h, and then repeatedly washed with deionized water and dried to obtain oxidized DCFs, named OCFs.

[0055] Step 2: Preparation of OCFs-CS1

[0056] Prepare an aqueous acetic acid solution with a concentration of 3mol / L, dissolve 30mg of chitosan (CS) in 100mL of the above aqueous acetic acid solution, mix thoroughly under ultrasound, immerse OCFs in the mixed liquid, soak and sizing at room temperature for 5min. After washing, vacuum-dry overnigh...

Embodiment 2

[0057] Embodiment 2, prepare the carbon fiber after chitosan encapsulation

[0058] According to the method of embodiment 1, difference only is that the consumption of chitosan in the second step is revised to 59mg from 30mg, makes the carbon fiber after chitosan encapsulation, named after OCFs-CS2.

Embodiment 3

[0059] Embodiment 3, prepare the carbon fiber after chitosan encapsulation

[0060] According to the method of embodiment 1, difference only is that the consumption of chitosan in the second step is revised to 89mg from 30mg, makes the carbon fiber after chitosan encapsulation, named after OCFs-CS3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a modified carbon fiber reinforced polymer-based composite material, and belongs to the field of composite materials. According to the invention, the oxidized carbon fiber is encapsulated by using the biomass polymer to obtain the modified carbon fiber OCFs-CS, and the interlaminar shear strength of the carbon fiber composite material prepared by compounding the OCFs-CS as the reinforcing fiber and the resin matrix is greatly improved, and the carbon fiber composite material has excellent mechanical strength. According to the preparation method disclosed by the invention, carbon nanotubes are further grafted on OCFs-CS to obtain modified carbon fibers OCFs-CS-CNTs, and the mechanical strength of the carbon fiber composite material prepared by compounding the OCFs-CS-CNTs serving as reinforced fibers and a resin matrix is further improved. The modified carbon fiber reinforced polymer-based composite material disclosed by the invention has excellent interface performance and mechanical strength, and has a wide application prospect in the fields of aerospace, transportation tools, energy equipment and the like.

Description

technical field [0001] The invention belongs to the field of composite materials, in particular to a modified carbon fiber reinforced polymer-based composite material with improved mechanical properties and interface properties. Background technique [0002] Carbon fiber reinforced polymer matrix composites (CFRP) are widely used in aerospace, energy, sports equipment and other fields due to their high strength, light weight, and good environmental stability. The interface properties of CFRP are crucial to its mechanical behavior. An excellent interface can transfer the load from the resin matrix to the fiber, reduce stress concentration, and improve the interface performance of the composite material. However, chemically inert and smooth fiber surfaces lead to poor wettability, and the interfacial-matrix bonding strength is too weak to efficiently transfer loads from the matrix to the fibers. [0003] In order to improve the interfacial properties between carbon fiber and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K9/04C08K9/02C08K7/06C08J5/06
Inventor 邹华维张程梁梅张雪琴
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com