Multifunctional coating and preparation method thereof

A multi-functional, coating technology, applied in anti-corrosion coatings, fire-retardant coatings, cement coatings, etc., can solve the problems of affecting construction efficiency, applicator trouble, long construction time, etc., to save construction time, improve efficiency, and easy to use. Effect

Pending Publication Date: 2022-03-22
深圳阿米防火防水高科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The matching between coatings often determines the durability of the coating; therefore, the matching between coatings often causes troubles for applicators
The application method of anti-slip coatings on the market: four or more layers of construction, the construction time is long, which affects the construction efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A multi-functional coating, including components a and component B, where:

[0044] Component A includes 1 part of phrochloroethylate, 10 plant phosphate, 10 plant polypropyl ether, 1 serial methacrylate butter, 1 octyl acrylate, plant methyl group 1 part of acrylate, 1 plant acrylic acid, 1 plant allyl polyoxyethylene ethyl ester, 1 plant sulfate, 1 plant ammonia, plant isomeric alcohol polyoxyethylene ether 1 part, 1 part of vegetarian sulfate, 1 mineral acrylic copolymer, plant triethylene glycol ether _ two (3_ tert-butyl _4_ hydroxyl group _5_ methylphenyl) 1 part of acid esters, 100 parts of water;

[0045] Component B includes 100 parts of mineral ferro-aluminate cement, 100 magnesium oxide 85 powder 200 mesh, 100 pieces of stone sand, 10 mineral double flour, 10 mineral lignin sulfate 1 share.

[0046] During use with this relative ratio of ingredients, the following procedure is performed:

[0047]1 part of phrochloroethylate, 10 plant phosphate, 10 plant polypropy...

Embodiment 2

[0052] A multi-functional coating, including components a and component B, where:

[0053] Component A includes: 6 parts of plant acrylate, 60 parts of plant phosphate, 60 parts of plant polypropyl ether, 6 servic methacrylate, 6 parts of octyl acrylate, and vegetative methyl groups 6 parts of acrylate, 6 servic acrylic acid, 6 servantine allyl polyoxyethylene ether sulfate, 6 parts of plant sulfate, 6 parts of plant ammonia, plant isomeric alcohol polyoxyethylene ether 6 copies of sodium phytosulfate, 6 parts of mineral acrylic acid copolymer, plant triethylene glycol ether _ two (3_ tert-butyl _4_ hydroxyl _5_ methylphenyl) 6 parts of sour esters, 600 water;

[0054] Component B includes: 600 mineral ferro-aluminate cement, 200 mesh of magnesium oxide, 600 mesh, 600 mesh, 600 mineral flour, 60 mineral lignin sulfate 6 share.

[0055] In the preparation, the following procedure is used:

[0056] 6 parts of plantacrylate, 60 parts of plantic phosphate, 60 parts of plant polypropyl...

Embodiment 3

[0061] A multi-functional coating, including components a and component B, where:

[0062] Component A includes 3.5 parts of plant acrylate, 35 parts of plant phosphate, 35 parts of plant polypropyl ether, 3.5 parts of phytomethyl methacrylate, 3.5 parts of octyl acrylate, plant methyl group 3.5 parts of acrylate, 3.5 parts of vegetable acrylic acid, 3.5 parts of plant allyl polyoxyethylene ether sulfate, 3.5 parts of plant sulfate, 3.5 parts of plant ammonia, plant isomeric alcohol polyoxyethylene ether 3.5 parts of plant sodium phytosulfate, 3.5 parts of mineral acrylic acid copolymer, plant triethylene glycol ether _ two (3_ tert-butyl _4_ hydroxyl-based _5_ methylphenyl) propionate 3.5 parts 350 water;

[0063] Component B includes: 350 mineral ferro-aluminated cement, 85 powder of magnesium oxide, 350 mesh, 350 mesh, 35 mineral flour, 35 mineral lignin sulfate 3.5 share.

[0064] In the process of preparing a coating using the above component, the following preparation proces...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multifunctional coating which comprises a component A and a component B. The component A comprises 1-6 parts of plant methyl acrylate, 10-60 parts of plant phosphate ester, 10-60 parts of plant polypropyl ether, 1-6 parts of plant butyl methacrylate, 1-6 parts of plant 2-ethylhexyl acrylate, 1-6 parts of plant 2-ethylhexyl methacrylate and 1-6 parts of plant acrylic acid. 1-6 parts of plant allyl polyoxyethylene ether ammonium sulfate, 1-6 parts of plant potassium persulfate, 1-6 parts of plant ammonia water, 1-6 parts of plant isomeric alcohol polyoxyethylene ether, 1-6 parts of plant lauryl sodium sulfate, 1-6 parts of mineral acrylic copolymer, 1-6 parts of plant triethylene glycol ether-di (3-tertiary butyl-4-hydroxyl-5-methyl phenyl) propionate and 100-600 parts of water. The component B is prepared from 100 to 600 parts of mineral iron aluminate cement, 100 to 600 parts of 200-mesh magnesium oxide 85 powder, 100 to 600 parts of 50-mesh quartz sand, 10 to 60 parts of mineral heavy calcium carbonate powder, 10 to 60 parts of mineral kaolin and 1 to 6 parts of mineral sodium lignin sulfonate. The coating is safe and can be widely applied to the technical field of coatings.

Description

Technical field [0001] The present invention relates to the field of coatings, and specifically, a multi-functional coating and a preparation method thereof. Background technique [0002] The non-slip coating on the market is usually composed of four materials: protective primers, intermediate coatings, non-slip pellets, cover paint. Among them, the protective properties of protective primers are focused due to different substrates (metal or concrete). Steel is dominated by anti-rust, and concrete focuses on anti-carbonization, anti-seepage, and alkali resistance. Accessibility between coatings often determines the durability of the coating; the matching choice between the coating is often caused by the trouble of application. The application of non-slip coatings on the market: 4 floors or more construction, long construction time, affecting construction efficiency. [0003] Therefore, a technique capable of overcoming the above defects is to be proposed. Inventive content [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/08C09D5/18C09D5/08C09D7/61C09D7/63C09D7/65
CPCC09D1/08C09D5/18C09D5/08C09D7/61C09D7/63C09D7/65
Inventor 陈天
Owner 深圳阿米防火防水高科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com