Chemical thermal insulation composite film and preparation process thereof

A technology of thermal insulation and preparation technology, which is applied in the field of composite membranes, can solve the problems of lowering production efficiency and increasing the thickness of composite membranes, and achieves the effects of reducing usage, increasing thickness, and enhancing thickness and performance

Active Publication Date: 2022-03-15
衢州市闻天化工有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]Usually, the increase in the thickness of the composite film is of great help to the improvement of various properties, but the increase in the thickness of the composite film will undoubtedly increase the amount of raw materials and reduce production efficiency , how to reconcile the contradiction between the two aspects is a challenge for those skilled in the art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chemical thermal insulation composite film and preparation process thereof
  • Chemical thermal insulation composite film and preparation process thereof
  • Chemical thermal insulation composite film and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0143] A preparation process of chemical thermal insulation composite film, comprising the steps of:

[0144] S1, take 0.05 parts by weight of foaming agent composite powder, add the foaming agent composite powder into the sieve drum 301 of the classification mixing device 3, and then divide 0.2 parts by weight of the porous inorganic particles into two Parts, respectively added in the sieve cylinder 301 and between the sieve cylinder 301 and the working chamber 302, and added the broken beads 307 into the cavity between the sieve cylinder 301 and the working chamber 302; The sieve drum 301 and the working bin 302 are rotated to a horizontal position, and the driving device 304 is started to drive the sieve drum 301 and the working bin 302 to rotate around the central axis synchronously. 500 revolutions per minute, rotate for 5 minutes; after the rotation stops, rotate the sieve cylinder 301 and the working chamber 302 to the position where the opening is inclined downward, an...

Embodiment 2

[0149] A preparation process of chemical thermal insulation composite film, comprising the steps of:

[0150] S1, taking 5 parts by weight of foaming agent composite powder, adding the foaming agent composite powder into the sieve drum 301 of the classification mixing device 3, and then dividing 5 parts by weight of the porous inorganic particles into two Parts, respectively added in the sieve cylinder 301 and between the sieve cylinder 301 and the working chamber 302, and added the broken beads 307 into the cavity between the sieve cylinder 301 and the working chamber 302; The sieve drum 301 and the working bin 302 are rotated to a horizontal position, and the driving device 304 is started to drive the sieve drum 301 and the working bin 302 to rotate around the central axis synchronously. 2000 revolutions per minute, rotate for 3 minutes; after the rotation stops, rotate the sieve cylinder 301 and the working chamber 302 to the position where the opening is inclined downward,...

Embodiment 3

[0155] A preparation process of chemical thermal insulation composite film, comprising the steps of:

[0156] S1, taking 3 parts by weight of foaming agent composite powder, adding the foaming agent composite powder into the sieve drum 301 of the classification mixing device 3, and then dividing 3 parts by weight of the porous inorganic particles into two parts Parts, respectively added in the sieve cylinder 301 and between the sieve cylinder 301 and the working chamber 302, and added the broken beads 307 into the cavity between the sieve cylinder 301 and the working chamber 302; The sieve drum 301 and the working bin 302 are rotated to a horizontal position, and the driving device 304 is started to drive the sieve drum 301 and the working bin 302 to rotate around the central axis synchronously. 1200 revolutions per minute, rotate for 4 minutes; after the rotation stops, rotate the sieve cylinder 301 and the working chamber 302 to the position where the opening is inclined dow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a chemical heat insulation composite film and a preparation process thereof, the composite film comprises: a polyester film layer comprising a first polyester film layer and a second polyester film layer, the density of the first polyester film layer being greater than the density of the second polyester film layer; the fluorine-silicon nano coating is coated on the second polyester film layer; the first polyester film layer, the second polyester film layer and the fluorosilicone nano coating are sequentially arranged to form the composite film. The composite film and the preparation process thereof have the advantages of being simple in structure, low in production cost, high in efficiency and good in heat insulation and heat preservation performance, mechanical strength, damp-heat aging resistance and corrosion resistance.

Description

technical field [0001] The invention relates to a composite film, in particular to a chemical heat insulation composite film and a preparation process thereof. Background technique [0002] With the development of polymer material technology, more and more composite membranes have been widely used in production and life. At present, there are many different types of composite films on the market, such as barrier composite films, heat-resistant composite films, selectively permeable composite films, fresh-keeping composite films, conductive composite films, etc. for different use scenarios. [0003] Among a wide variety of composite films, thermal insulation composite films are widely used, which requires composite films to have good thermal insulation performance, mechanical strength and moisture-heat aging resistance. When the thermal insulation composite membrane is used in the chemical industry, it is also required to have good corrosion resistance. [0004] Usually, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/36B32B27/32B32B27/08B32B33/00B32B7/12C08J9/36C08L23/12B29C48/08B29C48/21B29C55/16
CPCB32B27/36B32B27/32B32B27/08B32B33/00B32B7/12C08J9/365B29C48/08B29C48/21B29C55/16C08J2323/12B32B2255/10B32B2255/26B32B2307/304
Inventor 许文天石成
Owner 衢州市闻天化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap