Ceramic insulator with self-cleaning glaze and preparation method of ceramic insulator

A technology of ceramic insulators and self-cleaning glaze, which is applied in the field of insulators, can solve the problems of ceramic insulators such as pollution flashover, and achieve the effects of reducing labor costs, improving safety, and reducing maintenance

Pending Publication Date: 2022-01-21
萍乡市多普电瓷有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a ceramic insulator with self-cleaning glaze and its preparation method, which solves the problem that ceramic insulators are prone to pollution flashover

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An embodiment of the present invention provides a ceramic insulator with a self-cleaning glaze, which includes a ceramic insulator body and a glaze layer on its outer surface. The glaze layer includes the following raw materials in parts by weight: 45 parts of quartz, 20 parts of porcelain powder, and 20 parts of albite , 10 parts of calcite, 10 parts of nano-calcium carbonate, 5 parts of talc, 10 parts of kaolin, 8 parts of silicon oxide powder, 6 parts of polyvinylidene fluoride, 6 parts of nano-titanium dioxide, 5 parts of zinc oxide nanofiber, 55 parts of boric acid, ring 8 parts of oxygen resin, 5 parts of carboxymethyl cellulose.

[0020] Adding zinc oxide nanofibers, nano-titanium dioxide, nano-calcium carbonate, and silicon oxide micropowder to the self-cleaning glaze of ceramic insulators improves the high temperature resistance and oxidation resistance, and adding epoxy resin, carboxymethyl cellulose, boric acid, etc. to the glaze improves the insulator The se...

Embodiment 2

[0030] An embodiment of the present invention provides a ceramic insulator with a self-cleaning glaze, which includes a ceramic insulator body and a glaze layer on its outer surface. The glaze layer includes the following raw materials in parts by weight: 35 parts of quartz, 10 parts of porcelain powder, and 10 parts of albite , 5 parts of calcite, 5 parts of nano-calcium carbonate, 2 parts of talc, 5 parts of kaolin, 4 parts of silicon oxide micropowder, 2 parts of polyvinylidene fluoride, 2 parts of nano-titanium dioxide, 2 parts of zinc oxide nanofiber, 45 parts of boric acid, ring 4 parts of oxygen resin, 2 parts of carboxymethyl cellulose.

[0031] Adding zinc oxide nanofibers, nano-titanium dioxide, nano-calcium carbonate, and silicon oxide micropowder to the self-cleaning glaze of ceramic insulators improves the high temperature resistance and oxidation resistance, and adding epoxy resin, carboxymethyl cellulose, boric acid, etc. to the glaze improves the insulator The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a ceramic insulator with self-cleaning glaze and a preparation method of the ceramic insulator, and relates to the field of insulators. The ceramic insulator with the self-cleaning glaze comprises a ceramic insulator body and a glaze layer on the outer surface of the ceramic insulator body, wherein the glaze layer is prepared from the following raw materials in parts by weight: 35 to 45 parts of quartz, 10 to 20 parts of porcelain powder, 10 to 20 parts of albite, 5 to 10 parts of calcite, 5 to 10 parts of nano calcium carbonate, 2 to 5 parts of talc, 5 to 10 parts of kaolin, 4 to 8 parts of silicon oxide micro powder, 2 to 6 parts of polyvinylidene fluoride, 2 to 6 parts of nano titanium dioxide, 2 to 5 parts of zinc oxide nanofibers, 45 to 55 parts of boric acid, 4 to 8 parts of epoxy resin and 1 to 5 parts of carboxymethyl cellulose. By optimally selecting the glaze layer material meeting the requirements, etching the surface of the ceramic insulator body by adopting the glass etching liquid, and coating the glaze layer on the surface of the dried ceramic insulator body by adopting an atomization spraying mode, pollutants cannot be buried on the surface of the ceramic insulator, rain, snow, ice, dust and the like are not easy to attach, and surface dirt does not need to be removed.

Description

technical field [0001] The invention relates to the field of insulators, in particular to a ceramic insulator with self-cleaning glaze and a preparation method thereof. Background technique [0002] Pollution flashover refers to the pollution attached to the insulating surface of electrical equipment, under humid conditions, its soluble substances gradually dissolve in water, forming a conductive film on the insulating surface, greatly reducing the insulation level of the insulator, and appearing under the action of electric field force Strong discharge phenomenon, voltage, pollution, and humidity are the three necessary conditions for pollution flashover. To prevent pollution flashover, measures should be taken in these three aspects, such as increasing the creepage ratio distance, reducing surface pollution, increasing surface dry area, using New insulators, etc., in order to destroy the formation of pollution flashover conditions and avoid accidents. [0003] In order to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86C03C8/00
CPCC04B41/86C04B41/5022C03C8/00C04B41/4543C04B41/0072
Inventor 张家玉张轶可
Owner 萍乡市多普电瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products