A kind of high-strength recycled concrete and preparation method thereof

A recycled concrete, high-strength technology, applied in the field of concrete production, can solve problems such as cracks, limit the use range of recycled concrete, and low mechanical properties of recycled concrete, achieve the effect of reducing the number of gaps, improving synergistic effects, and increasing the use range

Active Publication Date: 2022-07-26
开平达宇管桩混凝土有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The current processing steps of recycled concrete generally include crushing, cleaning, and grading. Among them, when the discarded concrete blocks are broken, it is easy to cause cracks in the original aggregate, resulting in lower mechanical properties of the subsequently prepared recycled concrete. Therefore, most of the current recycled concrete is used in non-structural and non-load-bearing concrete fields such as backfill and roadbed, which limits the scope of use of recycled concrete.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength recycled concrete and preparation method thereof
  • A kind of high-strength recycled concrete and preparation method thereof
  • A kind of high-strength recycled concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0051] A high-strength recycled concrete is prepared by the following steps:

[0052] Step 1: The calcium sulfate whisker and coumarone resin are stirred for 15min under the condition of rotating speed of 220r / min in proportion, and the reinforcing agent is obtained after mixing evenly;

[0053]Step 2: Mix the reinforcing agent, the naphthalene-based water reducing agent, the cement, the regenerated coarse aggregate and the regenerated fine aggregate in proportion for 1.5 hours under the condition of a rotating speed of 90 r / min, and after mixing uniformly, a mixture A is obtained;

[0054] Step 3: Mix mixture A, water, sand and fly ash in proportion for 0.5h under the condition of rotating speed of 130r / min, and obtain high-strength recycled concrete after mixing evenly.

Embodiment 4

[0056] The difference from Example 3 is that the weight ratio of the naphthalene-based water-reducing agent to the reinforcing agent in Example 4 is 1:4, wherein the addition of the naphthalene-based water-reducing agent is 1kg, and the addition of the reinforcing agent is 4kg.

Embodiment 5

[0058] The difference from Example 3 is that the weight ratio of the naphthalene-based water-reducing agent to the reinforcing agent in Example 5 is 1:6, wherein the addition of the naphthalene-based water-reducing agent is 1kg, and the addition of the reinforcing agent is 6kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The present application relates to the field of concrete production, and more particularly, to a high-strength recycled concrete and a preparation method thereof. The high-strength recycled concrete includes cement, water, fly ash, sand, recycled aggregate, naphthalene-based water-reducing agent, and reinforcing agent; the preparation method is as follows: firstly, the calcium sulfate whiskers and coumarone resin are uniformly mixed in proportion to obtain Reinforcing agent, and then mixing the reinforcing agent, naphthalene-based water reducing agent, cement and recycled aggregate in proportion to obtain mixture A, and finally mixing mixture A, water, sand and fly ash in proportion to obtain high-strength recycled concrete . The present application has the effect of expanding the use range of recycled concrete.

Description

technical field [0001] The present application relates to the field of concrete production, and more particularly, to a high-strength recycled concrete and a preparation method thereof. Background technique [0002] Concrete is abbreviated as "concrete": it refers to the collective name of engineering composite materials that cement aggregates into a whole by cementing materials. The term concrete usually refers to using cement as cementing material, sand and stone as aggregates; and Water is mixed in a certain proportion, and the cement concrete obtained by mixing is widely used in civil engineering. [0003] With the gradual enhancement of people's awareness of environmental protection, more and more civil engineering has been applied to recycled concrete for construction. Recycled concrete refers to the waste concrete blocks after a series of processing steps, and then mixed with gradation in a certain proportion, partially or completely replacing natural aggregates such...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B14/38C04B24/00C04B24/28C04B103/30
CPCC04B28/04C04B24/00C04B14/383C04B24/28C04B2103/302C04B2201/50C04B2201/20C04B18/08C04B14/06C04B18/04
Inventor 李剑锋张秀匀张卓艺
Owner 开平达宇管桩混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products