Preparation method for manufacturing building hollow bricks by using mineral tailings

A technology for tailings slag and hollow bricks is applied in the field of hollow bricks, which can solve the problems of easy fracture and poor toughness of hollow bricks, and achieve the effects of increasing production quality, improving molding effect and improving practicability.

Pending Publication Date: 2021-12-24
滁州方大矿业发展有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a preparation method for making building hollow bricks by using mining tailings slag, so as to solve the problem of poor toughness in the above-mentioned background technology, so that the hollow bricks are prone to fracture during the drying and handling process; traditional hollow bricks also Unsuitable for use in environments with large temperature differences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for manufacturing building hollow bricks by using mineral tailings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A preparation method for manufacturing building hollow bricks using mining tailings slag, comprising the following steps:

[0035] Include the following steps:

[0036] S1. Ingredients: add a certain amount of straw powder and white cement to the mining waste;

[0037] S2. Grinding: put the step S1 into the mixer and pulverizer for stirring and mixing;

[0038] S3. Aging: put the materials after the stirring in step S2 into the aging bin, and add a certain proportion of brine and glue for stacking;

[0039] S4. Plasticizing: adding a certain amount of glass fiber powder and calcium carbonate powder to step S3, and then rolling and crushing;

[0040] S5. Molding: put the material in step S4 into the inside of the extruder for extrusion molding;

[0041] S6. Inspection: check the materials in step S5, put the unqualified materials into the extruder again for extrusion, and send the qualified materials into the next step by cart;

[0042] S7. Drying: the qualified mate...

Embodiment 2

[0054] A preparation method for manufacturing building hollow bricks using mining tailings slag, comprising the following steps:

[0055] Include the following steps:

[0056] S1. Ingredients: add a certain amount of straw powder and white cement to the mining waste;

[0057] S2. Grinding: put the step S1 into the mixer and pulverizer for stirring and mixing;

[0058] S3. Aging: put the materials after the stirring in step S2 into the aging bin, and add a certain proportion of brine and glue for stacking;

[0059] S4. Plasticizing: adding a certain amount of glass fiber powder and calcium carbonate powder to step S3, and then rolling and crushing;

[0060] S5. Molding: put the material in step S4 into the inside of the extruder for extrusion molding;

[0061] S6. Inspection: check the materials in step S5, put the unqualified materials into the extruder again for extrusion, and send the qualified materials into the next step by cart;

[0062] S7. Drying: the qualified materi...

Embodiment 3

[0074] A preparation method for manufacturing building hollow bricks using mining tailings slag, comprising the following steps:

[0075] Include the following steps:

[0076] S1. Ingredients: add a certain amount of straw powder and white cement to the mining waste;

[0077] S2. Grinding: put the step S1 into the mixer and pulverizer for stirring and mixing;

[0078] S3. Aging: put the materials after the stirring in step S2 into the aging bin, and add a certain proportion of brine and glue for stacking;

[0079] S4. Plasticizing: adding a certain amount of glass fiber powder and calcium carbonate powder to step S3, and then rolling and crushing;

[0080] S5. Molding: put the material in step S4 into the inside of the extruder for extrusion molding;

[0081] S6. Inspection: check the materials in step S5, put the unqualified materials into the extruder again for extrusion, and send the qualified materials into the next step by cart;

[0082] S7. Drying: the qualified mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of hollow bricks, in particular to a preparation method for manufacturing building hollow bricks by using mining industry tailing slag, which comprises the following steps: S1, material preparation: adding a certain amount of straw powder and white cement into mining industry waste slag; S2, grinding: putting the raw materials in the step S1 into a stirrer and a crusher for stirring and mixing; S3, aging: putting the materials stirred in the step S2 into an aging bin, adding brine and glue according to a certain proportion, and conducting stacking; S4, plasticizing: adding a certain amount of glass fiber powder and calcium carbonate powder into the mixture obtained in the step S3, and then conducting grinding and rolling; and S5, forming: putting the materials in the step S4 into an extruder for extrusion forming. According to the hollow brick, the toughness of the hollow brick can be improved through the arranged straw powder, the hollow brick is not prone to breakage in the airing and carrying process through the arranged straw powder, and the hollow brick is not prone to breakage when encountering the large temperature difference through the arranged glass fiber powder and the property of glass through the arranged glass fiber powder, and the glass fiber powder can make the hollow brick not prone to breakage when encountering the large temperature difference.

Description

technical field [0001] The invention relates to the field of hollow bricks, in particular to a preparation method for manufacturing building hollow bricks by using mine tailings slag. Background technique [0002] Commonly used in non-load-bearing parts, the porosity is equal to or greater than 35%, and the hollow bricks are called hollow bricks. Hollow bricks are divided into cement hollow bricks, clay hollow bricks, and shale hollow bricks. Hollow bricks are the main wall materials commonly used in the construction industry. , due to the advantages of light weight and less consumption of raw materials, it has become the first product recommended by the national construction department. Similar to red bricks, the common raw materials for hollow bricks are clay and cinder ash. [0003] Chinese Patent No. CN112094132A provides a preparation method of an environment-friendly coal-researched stone-based hollow brick, which includes the following steps: mixing fuel, filler and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/06C04B35/80C04B35/622
CPCC04B38/0675C04B35/80C04B35/62204C04B35/622C04B2235/3208C04B2235/5216C04B2235/6021C04B2235/606C04B2235/656
Inventor 童德双黄后林韩业平
Owner 滁州方大矿业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap