Control method for surface roughness of aluminum profile after electrolytic coloring, extinction and painting

Pending Publication Date: 2021-11-23
汨罗振升铝业科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Electrolytic coloring is a process of surface treatment of aluminum profiles, one of which is black, but when the black product needs to be matched with a matting paint process, it is easy to have problems of rough surface and reduced gloss, and the use of electrolytic coloring The method of soaking in the bath solution cannot completely remove the surface particles, resulting in a low pass rate of the produced products, which greatly increases the production cost, which is not conducive to the mass production of products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Control method for surface roughness of aluminum profile after electrolytic coloring, extinction and painting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0023] see figure 1 , an embodiment provided by the present invention: the method for controlling the surface roughness of aluminum profiles after electrolytic coloring and matting painting, comprising the following steps: Step 1, degreasing; Step 2, alkali etching; Step 3, neutralization; Step 4, anodizing Step 5, electrolytic coloring; Step 6, sulfuric acid cleaning; Step 7, extinction electrophoresis; Step 8, drying and curing;

[0024] Wherein in the abov...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a control method for surface roughness of an aluminum profile after electrolytic coloring, extinction and painting. The control method comprises the following steps of 1, degreasing; 2, alkali etching; 3, neutralizing; 4, anodic oxidation; 5, electrolytic coloring; 6, sulfuric acid cleaning; 7, extinction electrophoresis; and 8, drying and curing. In the step 1, the concentration of H2SO4 in a sulfuric acid solution subjected to degreasing treatment is 20-100 g / L, in the step 2, the concentration of NaOH in an alkaline solution is 25-90 g / L, the concentration of AL<3+> is 30-80 g / L, in the step 4, the concentration of H2SO4 in the sulfuric acid solution is 150-180 g / L, the concentration of AL<3+> is 5-20 g / L, in the step 6, the concentration of H2SO4 in the sulfuric acid solution is 80-100 g / L, and the water cutting and draining time is 3-5 min. Compared with an existing control method for surface roughness of the aluminum profile after electrolytic coloring, extinction and painting, the control method has the advantages that after electrolytic coloring, the sulfuric acid cleaning process is added, particles on the surface of the aluminum profile after coloring can be thoroughly eliminated, and the smooth surface effect can be obtained.

Description

technical field [0001] The invention relates to the technical field of profile processing, in particular to a method for controlling surface roughness of aluminum profiles after electrolytic coloring and matting paint. Background technique [0002] Electrolytic coloring is a process of surface treatment of aluminum profiles, one of which is black, but when the black product needs to be matched with a matting paint process, it is easy to have problems of rough surface and reduced gloss, and the use of electrolytic coloring The way of immersion in the tank solution cannot completely remove the surface particles, resulting in a low pass rate of the produced products, which greatly increases the production cost and is not conducive to the mass production of the products. Contents of the invention [0003] The object of the present invention is to provide a method for controlling the surface roughness of aluminum profiles after electrolytic coloring and matting painting, so as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D11/14C25D11/16C25D11/18C25D11/04C25D11/24
Inventor 欧高峰
Owner 汨罗振升铝业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products