Fe-doped Ni-MOF nanosheet as well as preparation method and application thereof

A nanosheet, soluble technology, applied in electrodes, electrical components, electrolysis process, etc., can solve the problems of hindering electrocatalytic performance and poor electrical conductivity of MOFs, and achieve the effect of excellent electrocatalytic performance, improved oxygen evolution performance, and simple method.

Active Publication Date: 2021-10-29
GUANGDONG UNIV OF PETROCHEMICAL TECH
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the poor electrical conductivity of MOFs hinders the development of electrocatalytic performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fe-doped Ni-MOF nanosheet as well as preparation method and application thereof
  • Fe-doped Ni-MOF nanosheet as well as preparation method and application thereof
  • Fe-doped Ni-MOF nanosheet as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A preparation method of Fe-doped Ni-MOF nanosheets, comprising the following steps:

[0043] S1. Precursor NiCo-LDH nanosheets prepared by hydrothermal method

[0044] S1.1, the Co(NO 3 ) 2 ·6H2 O (0.08g, 0.275mmol), Ni (NO 3 ) 2 ·6H 2 O (0.04g, 0.1375mmol), hexamethylenetetramine (HMT, 0.234g) were dissolved in 12mL of ethylene glycol aqueous solution (the volume ratio of ethylene glycol to deionized water was 1:5), and stirred until a uniform solution to obtain solution A;

[0045] S1.2. Place nickel foam in hydrochloric acid solution and ultrasonically clean it for 20 minutes; then ultrasonically clean it with water for 4 times, each cleaning time is 5 minutes; finally use ethanol to ultrasonically clean it for 5 minutes to obtain pretreated nickel foam; among them, hydrochloric acid solution It is obtained by mixing hydrochloric acid with a mass concentration of 37% and water at a volume ratio of 1:3;

[0046] S1.3. Put a piece of S1.2 pretreated foamed nicke...

Embodiment 2

[0052] A preparation method of Fe-doped Ni-MOF nanosheets, comprising the following steps:

[0053] S1. Precursor NiCo-LDH nanosheets prepared by hydrothermal method

[0054] S1.1, the Co(NO 3 ) 2 ·6H 2 O (0.08g, 0.275mmol), Ni (NO 3 ) 2 ·6H 2 O (0.04g, 0.1375mmol), hexamethylenetetramine (HMT, 0.234g) were dissolved in 12mL of ethylene glycol aqueous solution (the volume ratio of ethylene glycol to deionized water was 1:5), and stirred until a uniform solution to obtain solution A;

[0055] S1.2. Place nickel foam in hydrochloric acid solution and ultrasonically clean it for 20 minutes; then ultrasonically clean it with water for 4 times, each cleaning time is 5 minutes; finally use ethanol to ultrasonically clean it for 5 minutes to obtain pretreated nickel foam; among them, hydrochloric acid solution It is obtained by mixing hydrochloric acid with a mass concentration of 37% and water at a volume ratio of 1:3;

[0056] S1.3. Put a piece of S1.2 pretreated foamed nic...

Embodiment 3

[0062] A preparation method of Fe-doped Ni-MOF nanosheets, comprising the following steps:

[0063] S1. Precursor NiCo-LDH nanosheets prepared by hydrothermal method

[0064] S1.1, the Co(NO 3 ) 2 ·6H 2 O (0.08g, 0.275mmol), Ni (NO 3 ) 2 ·6H 2 O (0.04g, 0.1375mmol), hexamethylenetetramine (HMT, 0.24g) were dissolved in 12mL of ethylene glycol aqueous solution (the volume ratio of ethylene glycol to deionized water was 1:5), and stirred until a uniform solution to obtain solution A;

[0065] S1.2. Place nickel foam in hydrochloric acid solution and ultrasonically clean it for 20 minutes; then ultrasonically clean it with water for 4 times, each cleaning time is 5 minutes; finally use ethanol to ultrasonically clean it for 5 minutes to obtain pretreated nickel foam; among them, hydrochloric acid solution It is obtained by mixing hydrochloric acid with a mass concentration of 37% and water at a volume ratio of 1:3;

[0066] S1.3. Put a piece of S1.2 pretreated foamed nick...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a Fe-doped Ni-MOF nanosheet as well as a preparation method and application thereof, and belongs to the technical field of electrochemical material preparation. The method comprises the following steps that: S1, terephthalic acid and soluble iron salt are fully dissolved in a solvent to obtain a solution B, wherein the mass ratio of the terephthalic acid to the soluble ferric salt is 1: (0.1-0.3); and S2, a NiCo-LDH nanosheet material taking foamed nickel as a substrate and the solution B obtained in the step S1 are put into a closed container, then solvothermal high-pressure reaction is carried out at 100-120 DEG C, and after the reaction is completed, filtering and drying are performed to obtain the Fe-Ni-MOF nanosheet. The electro-catalyst of the Fe-Ni-MOF layered nanosheet structure, which is low in price and excellent in electro-catalytic performance, is synthesized by a method of combining a technology of creating a high-temperature and high-pressure environment through a solvothermal method and a metal ion synergistic effect, and the method is simple and convenient to operate.

Description

technical field [0001] The invention relates to the technical field of preparation of electrochemical materials, in particular to an Fe-doped Ni-MOF nanosheet and its preparation method and application. Background technique [0002] The electrocatalytic oxygen evolution reaction (OER) is a crucial half-reaction in energy storage conversion technologies such as water electrolysis and metal-air batteries. Limited by the four-electron transfer coupling process, OER is a kinetically slow process. Even with expensive catalysts, the OER process still requires a high overpotential. Therefore, it is of great significance to develop highly active and stable OER electrocatalysts. [0003] At present, according to the properties of materials, OER catalysts in alkaline environments can be roughly divided into two categories: one is RuO 2 , IrO 2 and other noble metal-doped catalysts; the second is based on Fe, Ni, Co and other transition metal catalysts. Precious metal materials ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G83/00C25B11/095C25B1/04H01M4/90H01M4/88
CPCC08G83/008C25B11/095C25B1/04H01M4/9008H01M4/88Y02E60/36Y02E60/50
Inventor 林双燕孙婷婷徐志堃李林
Owner GUANGDONG UNIV OF PETROCHEMICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com