Ceramizable heat-preservation fireproof coating and preparation method thereof

A kind of technology of fireproof coating and ceramicization, which is applied in the field of heat preservation and fire prevention to achieve the effect of improving mechanical properties, good protection effect and excellent heat preservation ability

Inactive Publication Date: 2021-08-24
宁波卓翔科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the existing technology has a large room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramizable heat-preservation fireproof coating and preparation method thereof
  • Ceramizable heat-preservation fireproof coating and preparation method thereof
  • Ceramizable heat-preservation fireproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A ceramicized thermal insulation and fireproof coating, in parts by weight, its preparation raw materials include the following components: 15 parts of high temperature resistant silicone resin, 35 parts of thermal insulation fillers, 5 parts of other functional fillers, 2 parts of auxiliary agents, and 50 parts of dilution solvent .

[0024] Wherein, the high temperature resistant silicone resin is methyl silicone resin (SH9502); the insulating filler is hollow ceramic microspheres with a particle size of 5 μm; other functional fillers, in parts by weight, include: 5 parts of carbon black, 5 parts of white 5 parts of carbon black, 1 part of zinc oxide; the auxiliary agents, in parts by weight, include: 1 part of siloxane coupling agent KH5501, 1 part of dispersant, 1 part of defoamer; A mixture of toluene.

[0025] The preparation method of the ceramizable thermal insulation and fireproof coating comprises the following steps: (1) mixing and stirring the high temperat...

Embodiment 2

[0027] A ceramicized thermal insulation and fireproof coating, in parts by weight, its preparation raw materials include the following components: 25 parts of high temperature resistant silicone resin, 50 parts of thermal insulation fillers, 10 parts of other functional fillers, 4 parts of auxiliary agents, and 200 parts of dilution solvent .

[0028] Wherein, the high temperature resistant silicone resin is methyl phenyl silicone resin (Rhodia 6405); the insulating filler is hollow glass microbeads with a particle size of 50 μm; other functional fillers, in parts by weight, include: carbon 8 parts of black, 10 parts of white carbon black, 3 parts of zinc oxide, 5 parts of titanium oxide; the auxiliary agents, in parts by weight, include: siloxane coupling agent KH5502 parts, dispersant 1.5 parts, defoamer 1.5 parts parts; the diluting solvent is No. 120 mineral spirits.

[0029] The preparation method of the ceramizable thermal insulation and fireproof coating comprises the ...

Embodiment 3

[0031] A ceramicized thermal insulation and fireproof coating, in parts by weight, its preparation raw materials include the following components: 30 parts of high temperature resistant silicone resin, 75 parts of thermal insulation fillers, 15 parts of other functional fillers, 5 parts of auxiliary agents, and 500 parts of dilution solvent .

[0032] Wherein, the high temperature resistant silicone resin is methylphenyl silicone resin (SH9603); the insulating filler is hollow ceramic microspheres with a particle size of 100 μm; other functional fillers, by weight, include: 10 parts of carbon black , 15 parts of white carbon black, 5 parts of zinc oxide, and 10 parts of titanium oxide; the additives, in parts by weight, include: siloxane coupling agent KH5503 parts, dispersant 2 parts, defoamer 2 parts; The diluting solvent is banana water.

[0033] The preparation method of the ceramizable thermal insulation and fireproof coating comprises the following steps: (1) mixing and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a ceramizable heat-preservation fireproof coating comprising the following preparation raw material components in parts by weight: 5 to 30 parts of high-temperature-resistant silicon resin, 35 to 75 parts of heat-preservation filler, 5 to 15 parts of other functional fillers, 2 to 5 parts of auxiliaries and 50 to 500 parts of a diluting solvent. According to the coating, high-temperature-resistant silicon resin is used as a matrix, and the heat-preservation filler and other functional fillers are added, so that the mechanical property, high-temperature resistance, weather resistance and other properties of the coating are improved, and the coating can be subjected to ceramization reaction at the high temperature of 500 DEG C or above, so that the coating can bear high-temperature heating of 1400 DEG C and cannot be burnt through for a long time; and moreover, the coating has relatively low thermal diffusivity, can provide better heat preservation capability when the temperature is rapidly changed, has a good protection effect when being applied to the field of lithium ion batteries, and effectively solves the problems existing in a protection material in the prior art.

Description

technical field [0001] The invention relates to the technical field of thermal insulation and fire protection, and more particularly, to a ceramicized thermal insulation and fireproof coating. Background technique [0002] Lithium-ion batteries have the characteristics of high energy density and low power density, and are widely used in portable electronic devices and new energy vehicles. However, the battery performance of current lithium-ion batteries will drop sharply at low temperatures. For example, low temperature affects the three-dimensional structure of the positive electrode material and thus restricts the diffusion rate of lithium ions, and the compatibility between the electrolyte and the negative electrode and separator deteriorates at low temperature. Moreover, due to the high energy density of lithium batteries, once structural damage occurs, dangerous thermal runaway will occur, resulting in smoke, fire or even explosion, which seriously affects the safety of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D7/61
CPCC08K2003/2237C08K2003/2296C09D5/18C09D183/04C09D7/61C09D7/70C08K13/04C08K7/24C08K3/04C08K7/26C08K3/22C08K7/28C08K7/06
Inventor 王欣袁玉兵李慧晓简开宇
Owner 宁波卓翔科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com