High-molecular large-mesh breathable and rain-proof mesh cloth and processing technology thereof
A processing technology, large mesh technology, applied in coatings, textiles and papermaking, etc., can solve the problems of high production cost, high processing difficulty, poor air circulation inside and outside, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] A kind of processing technique of macromolecule large-mesh air-permeable rainproof mesh cloth, the specific steps are as follows:
[0031] (1) first modifying the porous inorganic particles with γ-methacryloxypropyltrimethoxysilane to obtain modified porous inorganic particles;
[0032] (2) Then using cross-linked starch, acrylamide and modified porous inorganic particles as raw materials, a polymerization reaction occurs to obtain a polymerization product;
[0033] (3) Add 2-methyl-1,3-pentanediol, polyester polyol, polymerization product, ammonia water with a mass concentration of 5-7%, 1-aminoethyl-3-methylimidazole bis(trifluoromethane The sulfonyl)imide salt is mixed evenly, and then 4-methylcyclohexyl diisocyanate is added, stirred and mixed to obtain a coating solution;
[0034] (4) Finally, apply the coating solution evenly on the outer surface of the polyvinyl chloride mesh cloth base cloth, cure at 25° C. for 22 hours, and dry to obtain the rainproof mesh clo...
Embodiment 2
[0046] A kind of processing technique of macromolecule large-mesh air-permeable rainproof mesh cloth, the specific steps are as follows:
[0047] (1) first modifying the porous inorganic particles with γ-methacryloxypropyltrimethoxysilane to obtain modified porous inorganic particles;
[0048] (2) Then using cross-linked starch, acrylamide and modified porous inorganic particles as raw materials, a polymerization reaction occurs to obtain a polymerization product;
[0049] (3) Add 2-methyl-1,3-pentanediol, polyester polyol, polymerization product, ammonia water with a mass concentration of 7%, 1-aminoethyl-3-methylimidazole bis(trifluoromethanesulfonyl ) the imine salt is mixed evenly, then adding 4-methylcyclohexyl diisocyanate, stirring and mixing to obtain a coating solution;
[0050] (4) Finally, the coating solution was uniformly coated on the outer surface of the polyvinyl chloride mesh cloth base cloth, cured at 28° C. for 20 hours, and dried to obtain the rainproof me...
Embodiment 3
[0062] A kind of processing technique of macromolecule large-mesh air-permeable rainproof mesh cloth, the specific steps are as follows:
[0063] (1) first modifying the porous inorganic particles with γ-methacryloxypropyltrimethoxysilane to obtain modified porous inorganic particles;
[0064] (2) Then using cross-linked starch, acrylamide and modified porous inorganic particles as raw materials, a polymerization reaction occurs to obtain a polymerization product;
[0065] (3) Add 2-methyl-1,3-pentanediol, polyester polyol, polymerization product, ammonia water with a mass concentration of 6%, 1-aminoethyl-3-methylimidazole bis(trifluoromethanesulfonyl ) the imine salt is mixed evenly, then adding 4-methylcyclohexyl diisocyanate, stirring and mixing to obtain a coating solution;
[0066] (4) Finally, apply the coating solution evenly on the outer surface of the polyvinyl chloride mesh cloth base cloth, cure at 27° C. for 21 hours, and dry to obtain the rainproof mesh cloth. ...
PUM
Property | Measurement | Unit |
---|---|---|
Aperture | aaaaa | aaaaa |
Pore volume | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com