A technology for protecting ink and glass cover. It is used in glass molding, glass re-molding, ink and other directions. It can solve the problems of large ink particle size and poor ink operation, so as to reduce mold damage and poor polishing ratio. The effect of reducing, saving costs and cleaning time

Inactive Publication Date: 2021-08-10
DONGGUAN RBD TECH
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the scheme of the prior art, the granularity of the ink is required to be relatively large, and the ink needs to be strictly filtered with a 420-mesh mesh before it can be used. In addition, the product printing in the ink configuration is likely to cause fine impurities and hard particles. After hot bending, it will cause deep concave and convex points on the product, which makes the ink configuration difficult to operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot bending protection ink and hot bending polishing process of glass cover plate
  • Hot bending protection ink and hot bending polishing process of glass cover plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of hot bending protection ink of the present invention, the composition of described protection ink comprises: silicone resin 50%, aluminum oxide 10%, accelerator DM20%, calcium carbonate 10% and glass powder 10% according to weight percentage; Glass powder adopts It is made by mixing poly-p-phenylene benzobisoxazole fiber, silicon dioxide and titanium dioxide. Hot bending protection ink is white paste fluid with aromatic smell, molecular weight MN*10 3 21, temperature resistance 800-1000°C, flash point 56°C, Xiang value 4KOHmg / g, acid value 5KOHmg / g.

[0043] The preparation method is as follows: Measure the above-mentioned raw materials, take them separately according to the proportion of raw materials, put all the raw materials except the accelerator DM into the mixer for stirring and mixing, the stirring speed is the stirring speed of the mixing barrel (counterclockwise): 60±2r / min, rotating speed of stirring blade (clockwise): 80±5r / min, working gap betwee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to hot-bending protective ink and a hot-bending polishing process of a glass cover plate. The protective ink is prepared from the following components in percentage by weight: 45-55% of silicon resin, 5-15% of aluminum oxide, 15-25% of auxiliaries, 5-15% of calcium carbonate and 5-15% of glass powder. According to the hot bending polishing process, hot bending protection printing ink is adopted, so the effect of an interlayer can be effectively achieved, the proportion of concave-convex points is reduced, mold damage is reduced, the service life of a mold is prolonged, the polishing capacity is improved, the proportion of poor polishing is reduced, and cost is saved.

Description

technical field [0001] The invention relates to the technical field of glass cover processing, in particular to a thermal bending protection ink and a thermal bending polishing process for a glass cover. Background technique [0002] Affected by the complex structure of the curved surface of 3D products, the current industry has stricter requirements on the glass cover plate. The original appearance of the product has a high proportion of concave and convex points. Due to improper cleaning of graphite dust, it is easy to scratch the mold, resulting in poor appearance of product concave and convex points and dents. For hot bending The resulting defects and the increase in polishing time will increase the cost of the enterprise. It takes a long time to improve the appearance of the glass cover and polish to remove the bumps and indentations, which directly increases the cost of hot bending and polishing. Therefore, the protection during the processing of the glass cover is ver...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/03C03B23/023C03C17/00
CPCC09D11/102C09D11/03C03B23/023C03C17/009C03C17/007C03C2217/445C03C2217/475C03C2218/119C03C2218/328C03C2218/365C03C2218/355Y02P40/57
Inventor 唐克焱王祯国钟文武伍杰
Owner DONGGUAN RBD TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap