Preparation method of low-carbon-emission cold-rolled base material steel strip

A carbon emission and base material technology, applied in the field of iron and steel metallurgy, which can solve the problems of coil hardening, affecting slab continuous casting, and high nitrogen content.

Active Publication Date: 2021-08-06
XINJIANG BAYI IRON & STEEL
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Literature search shows that the smelting method of boron-containing steel in the iron and steel metallurgy industry must go through LF treatment, and some need to go through VD or RH vacuum treatment and then add ferroboron for alloying to improve the yield of boron. Anshan Iron and Steel uses titanium in steel Nitrogen fixation method to solve the problem of hardening steel coils due to high nitrogen content
[0006] For cold-rolled base steel with low carbon, low silicon, and low manganese content, due to the extremely low content of silicon and manganese, silicon-manganese deoxidation is weakened, and only aluminum deoxidation can be used. 2 o 3 Al 2 o 3 Composite inclusions of mainly calcium and magnesium oxides are the main factors affecting product quality, and even affect the straight line of slab continuous casting. It is very easy to oxidize, and needs LF refining to produce reducing slag to produce, but the LF refining process causes molten steel to increase nitrogen and affects the mechanical properties and cold stamping performance of cold-rolled base materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of low-carbon-emission cold-rolled base material steel strip
  • Preparation method of low-carbon-emission cold-rolled base material steel strip
  • Preparation method of low-carbon-emission cold-rolled base material steel strip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The technical solution adopted in the present invention is: a method for preparing a low-carbon emission cold-rolled base material steel strip, comprising:

[0029] 1. Technological process: hot metal desulfurization pretreatment, 120t top-bottom combined blowing converter smelting, converter tapping deoxidation alloying, inclusion removal, slab continuous casting, 1750 hot continuous rolling process production;

[0030] 2. Composition design of steel: The composition of steel is: C: 0.04~0.08wt%, Si: ≤0.030wt%, Mn: 0.15~0.25wt%, P: ≤0.018wt%, S: ≤0.012wt%, Al: 0.020~0.035wt%, N: ≤0.0035wt%, B: 0.0010~0.0018wt%, the balance is iron and impurities;

[0031] 3. The composition and preparation method of the slag washing material: the preparation of the slag washing material: the slag washing material is sintered into slag, and the composition of the synthetic slag: pre-melted slag according to CaO:Al 2 o 3 The mass percentage ratio is 1.4 to 1.6 and then sintered after m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a low-carbon-emission cold-rolled base material steel strip, and belongs to the field of ferrous metallurgy. The preparation method is a method for producing a low-carbon and low-silicon boron-containing cold-rolled deep-drawing base strip steel coil by adopting process routes of top-bottom combined blown converter smelting, converter tapping slag washing and inclusion removal, slab continuous casting and hot continuous rolling. According to the material prepared through the method, the low-carbon and low-silicon component design is adopted, the LF refining procedure is omitted, and through deoxidation, inclusion removal and continuous casting in the converter tapping process, the recovery rate of boron is guaranteed, and the performance stability of steel is improved. As the LF refining procedure is omitted, the nitrogen content in the steel is reduced, the quality of the strip steel is improved, electrode consumption does not exist in the production process, power consumption and carbon dioxide emission are reduced, and a novel method is provided for converter smelting and slab continuous casting of boron-containing low-carbon and low-silicon cold-rolled base material steel strips.

Description

technical field [0001] The invention relates to a method for preparing a low-carbon emission cold-rolled base material steel strip. The process route is smelting in a converter with top-bottom combined blowing, washing the steel slag out of the converter to remove impurities, continuous casting of slabs and continuous hot rolling to produce a low-carbon, low-carbon steel strip. The invention discloses a method for deep-drawing a base strip steel coil by cold-rolling silicon-containing boron, and belongs to the field of iron and steel metallurgy. [0002] technical background [0003] Steel base strip for cold rolling, the production method of steelmaking, usually pretreatment desulfurization of molten iron, converter smelting, LF refining or RH vacuum treatment, slab continuous casting to prepare slabs that meet the specifications, and then produce slabs that meet the requirements of cold rolling through hot continuous rolling. Steel coil (base strip) for rolling needs. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/06B22D11/18C21C5/28C21C7/00C21C7/064C21C7/072C22C38/02C22C38/04C22C38/06
CPCC22C33/06C21C7/064C21C5/28C21C7/0006C21C7/0087C21C7/0056C21C7/072B22D11/18B22D11/001C22C38/02C22C38/04C22C38/06C22C38/001C22C38/002C21C2007/0018C21D2211/005C21D2211/009Y02P10/20
Inventor 吾塔宋维兆赵亮
Owner XINJIANG BAYI IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products