Two-component coating type antiskid coating material and preparation method thereof

An anti-skid coating, two-component technology, applied in the direction of fiber raw material processing, inorganic compound addition, paper forming aid addition, etc., can solve the problems of poor anti-skid performance of paper skateboards, expand product application fields, increase surface friction coefficient, The effect of enhancing the anti-slip ability

Pending Publication Date: 2021-07-27
MYS GRP CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a two-component coating type anti-skid coating and its preparation method, aiming to solve the problem of poor anti-skid performance of paper slides

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The present invention also provides a preparation method of a two-component coating type anti-skid coating, comprising the following steps:

[0028] Step S1: the nano-Al 2 o 3 Disperse in absolute ethanol, add γ-aminopropyltriethoxysilane to deionized water, adjust the pH to 3 with glacial acetic acid, mix the two under the condition of constant temperature heating and magnetic stirring by dropping, Nano-Al after full reaction 2 o 3 Dispersions;

[0029] Step S2: Incorporate nano-CaCO 3 Disperse in deionized water, add sodium stearate after stirring, and fully react to obtain nano-CaCO 3 Dispersion liquid; take nanometer Al 2 o 3 Dispersion and Nano CaCO 3 The dispersion liquid was placed in a beaker and stirred at room temperature to obtain nano-Al 2 o 3 with CaCO 3 Dispersions;

[0030] Step S3: Dissolve the water-based polyurethane modified epoxy resin, heat and stir in a water bath, and successively dissolve the nano-Al 2 o 3 with CaCO 3 Add the dispers...

Embodiment 1

[0043] 1. Nano Al 2 o 3 with CaCO 3 Preparation of the dispersion:

[0044] 3 parts nano-Al 2 o 3 Disperse in anhydrous ethanol / water mixture (the mass ratio of the two is 1:1), add 2wt% of γ-aminopropyltriethoxysilane to deionized water at the same time, adjust the pH to about 3 with glacial acetic acid, The two are mixed by dropping at 65°C under the condition of constant temperature heating and magnetic stirring, and after fully reacting for 3 hours, the nano-Al 2 o 3 Dispersion; 2 parts of nano-CaCO 3 Disperse in deionized water, add 3wt% sodium stearate after stirring, and fully react at 50°C for 1 hour to obtain nano-CaCO 3 Dispersion liquid; take 5 parts of nano-Al respectively 2 o 3 Dispersion and Nano CaCO 3 Put the dispersion in a beaker and stir for 3 hours at room temperature to obtain nano-Al 2 o 3 with CaCO 3 Dispersions.

[0045] 2. Preparation of anti-skid coating:

[0046] Take 30wt% of water-based polyurethane modified epoxy resin to dissolve, ...

Embodiment 2

[0050] 1. Nano Al 2 o 3 with CaCO 3 Preparation of the dispersion:

[0051] 6 parts nano-Al 2 o 3 Disperse in anhydrous ethanol / water mixture (the mass ratio of the two is 1:1), add 5wt% of γ-aminopropyltriethoxysilane to deionized water at the same time, adjust the pH to about 3 with glacial acetic acid, The two are mixed by dropping at 70°C under the condition of constant temperature heating and magnetic stirring, and after fully reacting for 4 hours, the nano-Al 2 o 3 Dispersion liquid; 6 parts of nano-CaCO 3 Disperse in deionized water, add 5wt% sodium stearate after stirring, and fully react at 60°C for 2 hours to obtain nano-CaCO 3 Dispersion liquid; take 8 parts of nano-Al respectively 2 o 3 Dispersion and Nano CaCO 3 Put the dispersion in a beaker and stir for 3 hours at room temperature to obtain nano-Al 2 o 3 with CaCO 3 Dispersions.

[0052] 2. Preparation of anti-skid coating:

[0053] Take 40wt% of water-based polyurethane modified epoxy resin to di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a two-component coating type antiskid coating material and a preparation method thereof. The antiskid coating material is composed of a component A solution and a component B solution, wherein the component A solution is composed of the following components by weight: 30-50% of waterborne polyurethane modified epoxy resin, 10-15% of a nano Al2O3 and CaCO3 dispersion liquid, 25-30% of fluff powder, and the balance of water, and the component B solution comprises the following components in percentage by weight: 30-50% of a polyamide curing agent, 1-2% of a defoaming agent, 1-2% of a flatting agent and the balance of water. According to the invention, the two-component anti-skid coating material is coated on the paper slide plate, so that the surface friction coefficient is increased, the anti-skid capability of the paper slide plate is enhanced, and the problems that the paper slide plate is easy to slip in the stacking and carrying processes, cannot be carried and loaded on equipment and the like are solved.

Description

technical field [0001] The invention belongs to the technical field of anti-skid paper preparation, in particular to a two-component coating type anti-skid coating and a preparation method. Background technique [0002] Paper skateboards can be used as pads or pallets in different occasions and environments, and have broad development space and application prospects in the field of transportation packaging. It is light in weight, cheap, high in strength, recyclable, and its thickness is only about 1mm. It saves transportation and storage space to a great extent, thereby reducing freight and storage costs. It is used to replace wooden pallets, plastic pallets, and paper pallets for transportation. A new type of environmentally friendly packaging material for appliances. [0003] The paper slide board is made of multi-layer high-strength kraft cardboard through the board-making equipment, but the paper is easy to become smooth so that it will slip during the accumulation and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H17/55D21H17/67D21H21/06D21H21/12D21H21/14
CPCD21H17/55D21H17/675D21H21/12D21H21/06D21H21/14
Inventor 寇艳萍陈枫胡泽顺
Owner MYS GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap