A kind of measuring method of pH value of aqueous solution

An aqueous solution and solution technology, which is applied in the direction of material analysis by observing the influence of chemical indicators, and analysis by chemical reaction of materials, etc., can solve problems such as affecting the accuracy and accuracy of pH value, and solve the problem of inconsistent measurement results. Accurate, effective screening, improving accuracy and the effect of linear relationship

Active Publication Date: 2022-03-08
BEIJING NORMAL UNIVERSITY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The degradation process of AuNRs seriously affects its precision and accuracy as a colorimetric probe for measuring the pH value of solutions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of measuring method of pH value of aqueous solution
  • A kind of measuring method of pH value of aqueous solution
  • A kind of measuring method of pH value of aqueous solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1.1 Preparation of gold nanorods

[0038] The AuNRs used in this description were prepared by seed synthesis.

[0039] The seed solution was prepared by mixing 25 μL HAuCl in a 25 mL round bottom flask 4 (50mM) and 5mL CTAB (0.1M). After stirring slowly for 5 min, add freshly prepared 300 μL NaBH 4 solution on ice (0.01 M), then vigorously stirred for 30 sec. Finally, place it in a water bath at 30° C. and incubate for 1 hour to obtain a seed solution.

[0040] Growth solution was prepared as follows: 200 µL HCl (1M), 100 µL HAuCl 4 (50mM) and 10mL CTAB (0.1M) were added into a 50mL glass round bottom flask and stirred gently. Finally, add 120 μL AgNO 3 (10mM) and 100μL ascorbic acid (100mM) to prepare the seed growth solution.

[0041] When preparing AuNRs, inject 24 μL of seed solution into the above seed growth solution and stir vigorously for 30 s, and then incubate in a water bath at 30 °C for 24 hours to wait for the growth to complete. 10 mL of AuNRs was ...

Embodiment 2

[0045] In this example, the AuNRs synthesized in Example 1 are used to detect the pH value. The AuNRs solution was freshly prepared, the solutions to be tested were standard solutions with pH values ​​of 1.0, 2.0, 3.0, 4.0, 5.0, 6.0, and 7.0, and the etching solution consisted of 3.3mM KI and 6.6MH 2 o 2 composition.

[0046]100 μL of AuNRs solution and 100 μL of etching solution were added to 800 μL of solutions with different pH values, shaken vigorously and then transferred to a cuvette, the etching temperature was 20 °C, and the etching time was 1500 s. , the United States) to monitor, continuously collect RGB signals, and convert the RGB values ​​​​into the hue value H according to the following formula

[0047]

[0048] R, G and B in formula (1) are the component values ​​of red, green and blue respectively, Max channel and min channel are the maximum and minimum intensities in the red, green, and blue channels.

[0049] Using the newly prepared AuNRs as a colori...

Embodiment 3

[0054] In this embodiment, the AuNRs after being placed (aged) at room temperature for a long time are used as colorimetric probes for pH measurement.

[0055] After the AuNRs synthesized in Example 1 were left at room temperature for 25 days, they were used as a colorimetric probe, and the pH value of the aqueous solution was measured using the same conditions as in Example 2. It was found that the AuNRs placed for 25 days showed different response patterns ( Figure 4 ), the response rotates counterclockwise at the beginning of the reaction, and then starts to rotate clockwise after 400s. This phenomenon was consistent at every pH value tested. Overall, the resolution between the change curves is poor.

[0056] The maximum tone value is plotted against the pH value, and it can be found that the linear relationship is poor in the range of pH=1-7 ( Figure 5 ), the calibration curve has a lower linear correlation coefficient (R 2 =0.927, less than 0.95), the linear equatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
volumeaaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for measuring the pH value of an aqueous solution based on gold nanorods, and belongs to the technical field of nanomaterials. The method comprises the following steps: (A) continuously monitoring the RGB color space values ​​of the solution after adding the gold nanorod solution and the etching solution to the solution to be tested, corresponding to the red, green and blue color component values ​​respectively, until the etching reaction ends; (B) Convert the GRB color space value into a hue value; (C) plot the hue value against the etching reaction time in the polar coordinate system, and obtain the reversal value of the hue within 400 seconds after the start of etching and the entire etching The maximum reverse value in the process; (D) When the reverse value is less than 38°, the maximum reverse value of the hue value is substituted into the calibration curve to realize the measurement of pH value. In the method provided by the invention, during the measurement process, the quality of the gold nanorods is screened through the inversion value, and unqualified colorimetric probes are eliminated, thereby significantly improving the measurement precision and accuracy.

Description

technical field [0001] The invention relates to a method for measuring the pH value of an aqueous solution based on gold nanorods, and belongs to the technical field of nanomaterials. Background technique [0002] The traditional methods for measuring the pH value of a solution include test paper, pH meter, etc. However, the accuracy and resolution of the test paper method are poor, and the pH meter requires a large volume of solution to complete the measurement, and the matching glass The electrodes are relatively fragile, and the maintenance and activation steps are relatively cumbersome. [0003] Gold nanorods (gold nanorods, AuNRs) are longitudinally elongated gold nanoparticles with two LSPR absorption peaks, corresponding to the transverse and longitudinal absorption bands, respectively. Due to its extremely high molar extinction coefficient, gold nanorods are ideal probes for colorimetric pH measurement. However, as an anisotropic nanostructure, gold nanorods tend t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/80
CPCG01N21/80
Inventor 秦卫东任航
Owner BEIJING NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com