Colored chinlon 6 fine-denier thermofuse and preparation process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of hot-melt yarn and nylon, which is applied in the field of chemical fiber nylon, and can solve the problem of no colored nylon 6 fine-denier hot-melt yarn
Active Publication Date: 2021-05-11
CHANGLE HENGSHEN SYNTHETIC FIBER
View PDF9 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The existing nylon 6 thermal fuses are all above 50D, and there are no pro
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] Put the dried low-melting point copolyamide chips into the silo, and then enter the screw extruder with the temperature set in each zone from the silo, and enter the spinning box after being melted by the screw extruder, and then pass through the spinning metering pump. After accurate metering, it is squeezed into the spinning assembly, and after being filtered and pressurized by the spinning assembly, it is extruded from the spinneret to form a tow. The tow is cooled by side air and then enters the spinning nozzle for oiling. After oiling, it passes through the tunnel The wound oil roll is colored, and then passes through the pre-internet, cold roll R1, hot roll R2, main network, godet, and then enters the winding head to be wound into a silk cake to produce nylon 6 fine denier colored hot melt Silk.
[0023] 1. Dry the low-melting-point copolyamide chips at 40°C to control their moisture content at 100ppm.
[0024] 2. The temperature of the screw is 160°C, the head p...
Embodiment 2
[0039] 1. Dry the low-melting point copolyamide chips at 80°C, and control the moisture content at 50ppm.
[0040] 2. The temperature of the screw is 190°C, the head pressure of the screw extruder is 120 bar, and the pressure after the metering pump is 150 bar.
[0041] 3. The diameter of the spinneret is 65mm, and the aperture ratio of the spinneret is 0.20:0.70-0.35:0.90.
[0042] 4. The temperature of side blowing is 23.0°C, and the wind speed of side blowing is 0.70m / s.
[0043] 5. Wear-resistant nozzles are used for the oil nozzles. The distance from the cluster position of the oil nozzles to the spinneret is 2.0m, and the length of the tunnel mouth is 4.0m.
[0044] 6. The oil used is oil-soluble spinning oil JL-118, the oil concentration is 40%
[0045] 7. The solution for coloring the tow is a mixed solution of water-soluble pigment and oil-soluble oil agent. The ratio of pigment components is 5wt% of water-soluble pigment and 95wt% of oil-soluble oil agent. After fu...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Melting point
aaaaa
aaaaa
Diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a preparation method of colored chinlon 6 fine-denier thermofuse. The preparation method comprises the following steps of putting dried low-melting-point copolyamide slices into a stock bin, then entering a screw extruder from the stock bin, entering a spinning manifold after being melted by the screw extruder, and then extruding into a spinning assembly after being metered by a spinning metering pump, performing filtering and pressurizing through the spinning assembly, extruding through a spinneret plate to form tows, cooling the tows through cross air blowing, feeding the tows into a spinning oil nozzle for oiling, coloring the oiled tows through a channel opening and a wound oil roller, and feeding the tows into a winding head to be wound into a spinning cake after passing through a pre-interlacer, a cold roller R1, a hot roller R2, a main interlacer and a draw-off godet, thereby obtaining the polyamide 6 fine denier colored thermofuse. The colored chinlon 6 fine-denier thermofuse is researched and developed, and overseas technical monopoly is broken through.
Description
technical field [0001] The invention belongs to the field of chemical fiber nylon, and in particular relates to a colored nylon 6 fine denier thermal fuse and a preparation process thereof. Background technique [0002] Thermal fuse, also known as low-melting fiber, is one of the functional fibers that have developed rapidly in recent years. It controls the melting point between 85°C and 180°C by adjusting the properties of the nylon 6 raw material. At normal temperature, weave the thermal fuse and other fibers into a fabric, and then heat-set the fabric in a dry or wet state. When the temperature reaches the melting point of the thermal fuse, the thermal fuse gradually softens and melts, resulting in stickiness. Knot effect, while other conventional fibers remain unchanged, so that the fibers are bonded together by thermal fuse. Therefore, the thermal fuse can replace chemical adhesives such as glue, avoid the pollution of volatile matter and powder layer, and is environm...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more