Hydrophilic self-adhesive adhesive suitable for cold compress self-adhesive compression bandage, preparation method and application

A compression bandage, hydrophilic technology, applied in bandages, dressings, adhesive dressings, etc., can solve problems such as poor compression effect, inability to absorb cold compresses, and lack of hydrophilicity.

Active Publication Date: 2022-07-08
杭州高斯博医疗用品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional cold compress bandage is composed of elastic cotton base material and cold compress liquid, the compression effect is poor, and the outer layer needs to be fixed with PP non-woven self-adhesive elastic bandage to strengthen the compression effect
However, the adhesive and substrate of ordinary self-adhesive bandages are not hydrophilic, so they cannot absorb cold compress fluid, and the adhesive force decreases significantly after wetting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Ingredients: 50 parts of polyisoprene latex (IR-550) (solid content 50%), 5 parts of liquid paraffin, 5 parts of polyacrylate emulsion, 5 parts of PEG (600), 5 parts of PVA (1799) parts, 5 parts of PVP (K90), and 50 parts of water.

[0021] Add 50 kilograms of cold water, 5 kilograms of PEG600, 5 kilograms of PVA1799, and 5 kilograms of PVP K90 into batching kettle A in turn, turn on stirring, heat to a system temperature of 85-90 degrees and maintain this temperature, and stop heating after the material is completely dissolved and the system is transparent. (about 3 hours), continue to stir until the temperature of the system drops below 45 degrees.

[0022] 50 kilograms of polyisoprene latex (50% solid content) are added in batching kettle B, start stirring, be heated to 40-45 degree of system temperature and maintain this temperature, then add 5 kilograms of liquid paraffin successively, 5 kilograms of polyacrylates Emulsion, add the aforementioned materi...

Embodiment 2

[0025] Ingredients: 50 parts of polyisoprene latex (solid content 50%), 8 parts of liquid paraffin, 5 parts of polyacrylate emulsion, 4 parts of PEG (2000), 6 parts of PVA (2099), 3 parts of PVP (K90), 50 parts of water.

[0026] Add 50 kilograms of cold water, 4 kilograms of PEG2000, 6 kilograms of PVA2099, and 3 kilograms of PVP K90 into batching kettle A in turn, turn on stirring, heat to the system temperature of 85-90 degrees and maintain this temperature, and stop heating after the material is completely dissolved and the system is transparent. (about 3 hours), continue to stir until the temperature of the system drops below 45 degrees.

[0027] 50 kilograms of polyisoprene latex (50% solid content) are added in batching kettle B, start stirring, be heated to 40-45 degrees of system temperature and maintain this temperature, then add 8 kilograms of liquid paraffin successively, 5 kilograms of polyacrylates Emulsion, add the aforementioned materials after stirring for 2 ...

Embodiment 3

[0030] Ingredients: 50 parts of natural rubber latex (solid content 60%), 12 parts of liquid paraffin, 6 parts of polyacrylate emulsion, 6 parts of PEG (1500), 4 parts of PVA (2499), 2 parts of PVP (K90), 60 parts of water,

[0031] Add 60 kilograms of cold water, 6 kilograms of PEG1500, 4 kilograms of PVA2499, and 2 kilograms of PVP K90 into batching kettle A in turn, turn on stirring, heat to a system temperature of 85-90 degrees and maintain this temperature, and stop heating after the material is completely dissolved and the system is transparent. (about 3 hours), continue to stir until the temperature of the system drops below 45 degrees.

[0032] 50 kilograms of natural latex (60% solid content) are added in batching kettle B, start stirring, be heated to 40-45 degree of system temperature and maintain this temperature, then add 12 kilograms of liquid paraffin successively, 6 kilograms of polyacrylate emulsion, stir 2 After 1 hour, the aforementioned materials were added...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hydrophilic self-adhesive suitable for cold compressing self-adhesive compression bandages and a preparation method and application, wherein the weight percentage of the hydrophilic self-adhesive comprises: polyvinyl alcohol: 1%-10%, polyvinyl alcohol Ethylene Glycol: 1%-10%, Polyvinylpyrrolidone: 0%-10%, Natural Latex or Polyisoprene Latex: 20%-30%, Liquid Paraffin: 3%-10%, Polyacrylate Emulsion: 2%-5%, water: 50%-70%, other components: balance; the weight percentage of the natural latex or polyisoprene latex is calculated as dry rubber. The patent of the present invention provides a hydrophilic self-adhesive adhesive suitable for cold compressing self-adhesive elastic bandages, using natural latex or polyisoprene latex and PVA, PVP, PEG, etc. Sufficient adhesive force can be achieved, and the peel strength is greater than or equal to 0.03KN / m.

Description

technical field [0001] The invention belongs to the technical field of self-adhesive adhesives, in particular to a hydrophilic self-adhesive adhesive suitable for cold compressing self-adhesive compression bandages. Background technique [0002] The traditional cold compress bandage system is composed of elastic cotton base material and cold compress liquid, which has poor compression effect. The outer layer needs to be fixed with PP non-woven self-adhesive elastic bandage to strengthen the compression effect. However, the adhesive and substrate of ordinary self-adhesive bandages do not have hydrophilic properties, so they cannot absorb cold compresses, and the adhesive force decreases significantly after wetting. SUMMARY OF THE INVENTION [0003] The invention provides a hydrophilic self-adhesive adhesive with good hydrophilicity and strong adhesion after wetting, which is suitable for cold compressing self-adhesive compression bandages. The present invention also provid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/24A61L15/26A61L15/10A61L15/58A61F13/02
CPCA61L15/26A61L15/24A61L15/10A61L15/58A61F13/0253A61F13/0256C08L71/02C08L29/04C08L39/06C08L23/20C08L33/08
Inventor 来焱郑乐回
Owner 杭州高斯博医疗用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap