Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Efficient low-phosphorus scale and corrosion inhibitor and preparation method thereof

A scale and corrosion inhibitor, high-efficiency technology, applied in chemical instruments and methods, scale removal and water softening, natural water treatment, etc., to achieve excellent corrosion inhibition performance, improve the effect of corrosion inhibition performance

Pending Publication Date: 2021-03-16
SHANDONG TIANQING TECH DEV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the problems existing in the above-mentioned prior art, the purpose of the present invention is to provide a kind of high-efficiency low-phosphorus scale and corrosion inhibitor and its preparation method, to solve the problems existing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient low-phosphorus scale and corrosion inhibitor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Add 10kg of sodium nitrite and 30kg of deionized water into the stirring tank, stir and dissolve; add 15kg of borax to the above solution, stir and dissolve, then add 10kg of zinc sulfate heptahydrate, stir and dissolve; finally add 12kg of 2-phosphine to the reaction kettle Acyl-1,2,4-butanetricarboxylic acid, 12kg polyepoxysuccinic acid, 15kg acrylic acid / 2-acrylamide-2-methylpropanesulfonic acid copolymer; stir evenly at room temperature for 20-30min to obtain high-efficiency Low phosphorus scale and corrosion inhibitor.

Embodiment 2

[0031] Add 5kg of sodium nitrite and 20kg of deionized water into the stirring tank, stir and dissolve; add 10kg of disodium octaborate tetrahydrate to the above solution, stir and dissolve, then add 15kg of zinc chloride, stir and dissolve; Add 5kg of hydroxyethylene diphosphonic acid, 10kg of polyepoxysuccinic acid, and 10kg of acrylic acid / propylene sulfonate sodium copolymer; stir evenly at room temperature for 20 to 30 minutes to obtain a high-efficiency low-phosphorus scale and corrosion inhibitor.

Embodiment 3

[0033] Add 15kg of sodium nitrite and 50kg of deionized water into the stirring tank, stir and dissolve; add 20kg of potassium tetraborate to the above solution, stir and dissolve, then add 5kg of zinc chloride, stir and dissolve; finally add 10kg2 -Hydroxyphosphinoacetic acid, 15kg polyaspartic acid, 20kg acrylic acid / 2-acrylamide-2-methylpropanesulfonic acid / hydroxypropyl acrylate terpolymer; stir evenly at room temperature for 20-30min to obtain high-efficiency and low-efficiency Phosphorus scale and corrosion inhibitor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Alkalinityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an efficient low-phosphorus scale and corrosion inhibitor and a preparation method thereof. The efficient low-phosphorus scale and corrosion inhibitor comprises the following raw materials in parts by weight: 5-15 parts of organic phosphine, 10-20 parts of sulfonate copolymer, 10-15 parts of carboxylic acid polymer, 10-20 parts of borate, 5-15 parts of sodium nitrite, 5-15parts of zinc salt and 10-50 parts of deionized water. The efficient low-phosphorus scale and corrosion inhibitor has the characteristics of small amount and high efficiency. The efficient low-phosphorus scale and corrosion inhibitor is suitable for a circulating cooling water system with low hardness and low alkalinity, and has excellent corrosion inhibition performance on carbon steel and stainless steel equipment.

Description

technical field [0001] The invention belongs to the technical field of water treatment, and in particular relates to a high-efficiency low-phosphorus scale and corrosion inhibitor and a preparation method thereof. Background technique [0002] my country is one of the countries with the most water shortages in the world. The total annual water resources are more than 2.8 trillion tons, ranking sixth in the world, and the per capita water volume is less than 2400m 3 , only 1 / 4 of the world's per capita water volume, ranking 110th in the world, and listed by the United Nations as one of the 13 water-poor countries. At present, water scarcity coverage is almost all over the country. As far as the north where water is not abundant, water shortage is already the most serious problem facing the development of industry and agriculture. The circulating cooling water used for cooling in industrial water accounts for a relatively large proportion, accounting for 60% to 80% of the to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C02F5/14C02F5/10C23F11/08C02F103/02
CPCC02F5/145C02F5/105C23F11/08C02F2303/08C02F2103/023
Inventor 郭翠娟张留成刘文峰谢泽新高松耿俊玲梁新新高云峰郑萍范春燕
Owner SHANDONG TIANQING TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com