Medical adhesive material capable of rapidly stopping bleeding and preparation method thereof

A rapid and carboxymethyl chitosan technology, applied in the field of medical adhesive materials for rapid hemostasis, can solve problems such as poor hemostasis performance, and achieve the effect of improving hemostasis performance and hemostasis performance.

Active Publication Date: 2021-01-15
FUALIE SCI & TECH DEVING BEIJING
View PDF18 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For this reason, the technical problem to be solved by the present invention is to provide a kind of medical glue material that can stop bleeding rapidly, to solve the problem of poor hemostatic performance of simple cyanoacrylic medical glue material in the prior art;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical adhesive material capable of rapidly stopping bleeding and preparation method thereof
  • Medical adhesive material capable of rapidly stopping bleeding and preparation method thereof
  • Medical adhesive material capable of rapidly stopping bleeding and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0022] The preparation of preparation example 1α-n-butyl cyanoacrylate

[0023] This preparation example is used for preparing required n-butyl cyanoacrylate, specifically comprises the following steps:

[0024] (1) Butyl ester transesterification reaction

[0025] CNCH 2 COOC 2 h 5 +C 4 h 9 OH—C 2 h 5 ONa→CNCH 2 COOC 4 h 9 +C 2 h 5 Oh

[0026] In a 5L three-necked beaker equipped with a stirrer and a thermometer, put 1400ml of ethyl cyanoacetate and 1200ml of n-butanol, turn on the stirring, condense water, add 25g of sodium ethoxide to 40°C and above; heat up to 100°C and the top temperature reaches 78 Start distilling ethanol at -82°C. When the internal temperature reaches 110°C and the top temperature reaches 98-100°C, stop heating and collect about 680ml of ethanol;

[0027] Cool down to an internal temperature of about 50°C, turn on the heating, change the bottle with the vacuum pump to receive n-butanol, the vacuum degree is -0.1MPa, and change the bottle ...

preparation example 2

[0037] Preparation Example 2 The preparation of n-octyl cyanoacrylate

[0038] This preparation example is used for preparing required n-octyl cyanoacrylate, specifically comprises the following steps:

[0039] (1) with step (1) in the preparation example 1;

[0040] (2) with step (2) in the preparation example 1;

[0041] (3) Synthesis of n-octyl α-cyanoacrylate

[0042]

[0043] Add 380ml of methanol-formaldehyde solution and 0.95ml of piperidine into a 5L three-neck flask equipped with a stirrer, dropping funnel, condenser, and water separator. When the temperature in the bottle reaches 40°C or above, start adding cyanoacetic acid After adding 750ml of octyl esters dropwise, collect methanol until the internal temperature reaches 120°C; then add 300ml of petroleum ether dropwise, start dehydration, and speed up stirring. After the water is finished, collect about 300ml of petroleum ether; when the internal temperature reaches 130°C, add 20g of phosphorus pentoxide and...

Embodiment 1

[0048] The preparation method of the medical adhesive material for rapid hemostasis described in the present embodiment comprises the following steps:

[0049] (1) According to the mass ratio of 55wt%: 45wt%, the above-mentioned n-butyl cyanoacrylate and n-octyl α-cyanoacrylate are fully mixed to obtain a medical glue base, and set aside;

[0050] (2) get carboxymethyl chitosan and be placed in the airtight container that 1-methylimidazole trifluoroacetate ionic liquid (accounting for the 8wt% of described carboxymethyl chitosan quality) is housed, get rid of air and to The container is filled with CO 2 , control the temperature in the airtight container to 80°C and the pressure to 8MPa, so that the charged CO 2 The gas is in a supercritical state, and under the condition that the carboxymethyl chitosan is not in contact with the ionic liquid, the carboxymethyl chitosan is modified with the ionic liquid for 10 minutes, and the conventional discharge Press to obtain the desir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of biomedical materials, particularly relates to a medical adhesive material capable of rapidly stopping bleeding, and further discloses a preparation method of the medical adhesive material. According to the medical adhesive material disclosed by the invention, alpha-n-butyl cyanoacrylate and alpha-n-octyl cyanoacrylate are used as a mixed medical adhesive matrix, and a hemostatic material namely carboxymethyl chitosan is swelled and modified in a manner that CO2 supercritical fluid carries selected ionic liquid, so that the bleeding stopping performance of the carboxymethyl chitosan is effectively improved, the bleeding stopping performance of the whole medical adhesive material is greatly improved, and rapid bleeding stopping is achieved.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, in particular to a medical glue material for rapid hemostasis, and further discloses a preparation method thereof. Background technique [0002] Medical glue refers to the preparation, material or substance that can adhere to the surface or make the surface bond in the medical application. It belongs to the special functional adhesive of biomedicine. It is mainly used for local adhesion and repair of organs or tissues. Traditional suturing, or the combination and positioning of tissues and blood vessels for closure and other technical fields, in addition to the usual bonding and mechanical functions, also has biomedical functions. Compared with traditional methods such as suturing and stapling, the use of medical glue can effectively shorten the operation time and significantly reduce the pain of patients. It is the preferred material for medical operations at present. [0003] At p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L24/08A61L24/06A61L24/00
CPCA61L24/08A61L24/06A61L24/001A61L2400/04C08L5/08C08L35/04
Inventor 王威田霞张俊杰张怡婷费维滢彭婷婷郭修峰
Owner FUALIE SCI & TECH DEVING BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com