Preparation method for antibacterial cloth and antibacterial cloth

A technology for fabrics and raw materials, applied in textile, biochemical fiber treatment, yarn and other directions, can solve the problems of easy shedding and poor durability, and achieve the effect of good antibacterial effect, good antibacterial durability, and delaying the disappearance of antibacterial properties.

Active Publication Date: 2020-12-18
杭州麒隆化纤有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, since the antibacterial agent is only covered on the surface of the fiber, it is easy to fall off after friction or washing, and the durability is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for antibacterial cloth and antibacterial cloth
  • Preparation method for antibacterial cloth and antibacterial cloth
  • Preparation method for antibacterial cloth and antibacterial cloth

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0052] 1. Pretreatment: Put 30kg of bagasse viscose fiber, 10kg of coconut charcoal fiber, and 30kg of polyester fiber into a water bath for water bath heat treatment. The temperature of the water bath in the water bath is 75°C, and the water bath time is 2 hours;

[0053] Place the fiber treated in the water bath in a drying room, and dry at 120°C until the fiber humidity is 18%;

[0054] Soak the dried fibers in the mixture of antistatic agent and anti-fluffing agent for 1 hour. The antistatic agent can be non-ionic antistatic agent LD-940H, and the anti-fluffing agent can be G-KQ, LD-940H and G- The volume ratio of KQ is 1:2.5;

[0055] Place the soaked fibers in a drying room and dry at 120°C for 3 hours;

[0056] 2. The dried bagasse viscose fiber and polyester fiber are spirally intertwisted to obtain a blended yarn;

[0057] 3. The blended yarn and the dried coconut charcoal fiber are spirally twisted according to the corresponding parts by weight to obtain the bagass...

preparation example 2

[0059] 1. Pretreatment: Put 35kg of bagasse viscose fiber, 15kg of coconut charcoal fiber, and 35kg of polyester fiber into a water bath for water bath heat treatment. The temperature of the water bath in the water bath is 75°C, and the water bath time is 2 hours;

[0060] Place the fiber treated in the water bath in a drying room, and dry at 120°C until the fiber humidity is 18%;

[0061] Soak the dried fibers in the mixture of antistatic agent and anti-fluffing agent for 1 hour. The antistatic agent can be non-ionic antistatic agent LD-940H, and the anti-fluffing agent can be G-KQ, LD-940H and G- The volume ratio of KQ is 1:2.5;

[0062] Place the soaked fibers in a drying room and dry at 120°C for 3 hours;

[0063] 2. The dried bagasse viscose fiber and polyester fiber are spirally intertwisted to obtain a blended yarn;

[0064] 3. The blended yarn and the dried coconut charcoal fiber are spirally twisted according to the corresponding parts by weight to obtain the bagass...

preparation example 3

[0066] 1. Pretreatment: Put 40kg of bagasse viscose fiber, 20kg of coconut charcoal fiber, and 40kg of polyester fiber into a water bath for water bath heat treatment. The temperature of the water bath in the water bath is 75°C, and the water bath time is 2 hours;

[0067] Place the fiber treated in the water bath in a drying room, and dry at 120°C until the fiber humidity is 18%;

[0068] Soak the dried fibers in the mixture of antistatic agent and anti-fluffing agent for 1 hour. The antistatic agent can be non-ionic antistatic agent LD-940H, and the anti-fluffing agent can be G-KQ, LD-940H and G- The volume ratio of KQ is 1:2.5;

[0069] Place the soaked fibers in a drying room and dry at 120°C for 3 hours;

[0070] 2. The dried bagasse viscose fiber and polyester fiber are spirally intertwisted to obtain a blended yarn;

[0071] 3. The blended yarn and the dried coconut charcoal fiber are spirally twisted according to the corresponding parts by weight to obtain the bagass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of textile products, and particularly discloses a preparation method for antibacterial cloth and the antibacterial cloth. The antibacterial cloth comprises 20-30 parts of cotton fibers, 10-20 parts of polyurethane fibers, 50-60 parts of carex meyeriana fibers, 50-60 parts of silk fibers, 30-40 parts of bagasse composite fibers, 50-60 parts of silk fibers and 50-60 parts of wool fibers; wherein the bagasse composite fibers are prepared by blending 30-40 parts of bagasse viscose fibers, 10-20 parts of coconut carbon fibers, and 30-40 parts of polyester fibers.The cloth is compact in structure, good in air permeability and good in wear resistance. The preparation method for the cloth comprises preparation of warp yarns and weft yarns and preparation of an antibacterial agent. The antibacterial cloth prepared through the method can be used for antibacterial and deodorant products and has the advantages of being remarkable in antibacterial effect, good inantibacterial durability, washable and the like.

Description

technical field [0001] The application relates to the field of textile products, more specifically, it relates to a preparation method of an antibacterial cloth and the antibacterial cloth. Background technique [0002] Due to the diversity of the fabric structure, dirt, sweat, etc. are easily deposited on the fabric tissue, and various bacteria and microorganisms are easy to breed. If these harmful bacteria cannot be eliminated, various diseases will occur and endanger the health of the wearer. In order to make the cloth antibacterial, two methods of antibacterial fiber or fabric finishing are usually used to carry out antibacterial treatment on the cloth. [0003] The antibacterial fiber is to add the antibacterial agent into the spinning solution and mix, and then spin through the spinneret hole to form the antibacterial fiber. Antibacterial agents include inorganic antibacterial agents, organic antibacterial agents and natural antibacterial agents. [0004] The fabric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/08D03D15/00D02G3/04D06B3/02D06M15/03D06M101/38D06M101/06
CPCD03D15/00D06B3/02D02G3/04D06M16/00D06M15/03D10B2201/02D10B2331/10D10B2201/01D10B2211/04D10B2211/02D10B2331/04D06M2101/06D06M2101/38
Inventor 孙彬高飞
Owner 杭州麒隆化纤有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com