High temperature and high strength low-carbon martensite refractory steel and preparation method thereof

A technology of low-carbon martensite and heat-strength steel, which is applied in the field of aero-engines, can solve problems such as insufficient high-temperature strength, difficulty in meeting the strength and safety requirements of load-bearing components, and working temperature limits, so as to avoid the precipitation of delta ferrite and improve The effect of application stability and high temperature resistance

Active Publication Date: 2020-12-18
UNIV OF SCI & TECH BEIJING
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although GX-8 heat-strength steel has high strength and high toughness, the working temperature is limited to a maximum of 600°C
With the continuous increase of the thrust of modern advanced aero-engines, the service temperature of aero-engine suspensions and other load-bearing components can reach above 600°C. The tensile strength at 700°C is only about 200MPa, which is difficult to meet the strength and safety requirements of load-bearing components

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature and high strength low-carbon martensite refractory steel and preparation method thereof
  • High temperature and high strength low-carbon martensite refractory steel and preparation method thereof
  • High temperature and high strength low-carbon martensite refractory steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] The present invention also provides a method for preparing high-temperature, high-strength, low-carbon martensitic heat-strength steel according to any of the above-mentioned embodiments, comprising the following steps:

[0063] Smelting steps: Prepare raw materials according to the following mass percentages:

[0064] C: 0.10~0.25wt%, Cr: 10.0~13.0wt%, Ni: 2.0~3.2wt%, Mo: 1.50~2.50wt%, Si≤0.60wt%, Mn≤0.60wt%, W: 0.4~0.8wt% %, V: 0.1-0.5wt%, Co: 0.3-0.6wt%, Al: 0.3-1.0wt%, Nb: 0.01-0.2wt%, the rest is Fe, and then the raw materials are smelted to obtain a smelted billet.

[0065] The process of raw material smelting is well known to those skilled in the art, and the present invention is not particularly limited. For example, the method of vacuum induction melting + electroslag remelting (ESR) can be used, and electric arc furnace (EAF) + refining (LF) can also be used. + Vacuum degassing (VD) + Electroslag remelting (ESR) and other smelting methods that can guarantee t...

Embodiment 1

[0086]

[0087] Prepare raw materials by the following mass percentages:

[0088] C: 0.14wt%, Cr: 10.3wt%, Ni: 2.05wt%, Mo: 1.55wt%, Si: 0.35wt%, Mn: 0.31wt%, W: 0.42wt%, V: 0.16wt%, Nb: 0.08wt%, Co: 0.3wt%, Al: 0.28wt%, and the rest is Fe, and the raw materials are smelted to obtain a smelted billet.

[0089]

[0090] For the forging of the smelted slab, the initial forging temperature is 1100°C, and the final forging temperature is 880°C to obtain steel ingots.

[0091]

[0092] Carry out normalizing treatment to the steel ingot, the normalizing treatment temperature is 1100 ℃, the holding time is 3h, and then air-cooled to room temperature.

[0093]

[0094] Heat the heat-treated steel ingot to 1150°C in a high-temperature furnace for 2 hours, then water-cool to room temperature, then heat to 580°C and temper for 2 hours, then cool to room temperature, and then heat the quenched and tempered steel ingot at 480°C for 6 hours. Then cool to room temperature.

Embodiment 2

[0096]

[0097] Prepare raw materials by the following mass percentages:

[0098] C: 0.18wt%, Cr: 12.8wt%, Ni: 2.53wt%, Mo: 2.44wt%, Si: 0.4wt%, Mn: 0.51wt%, W: 0.38wt%, V: 0.23wt%, Nb: 0.12wt%, Co: 0.33wt%, Al: 0.31wt%, and the rest is Fe. The raw materials are smelted to obtain a smelted billet.

[0099]

[0100] For smelting slab forging, the initial forging temperature is 1100°C and the final forging temperature is 860°C to obtain steel ingots.

[0101]

[0102] The steel ingot is annealed at 900°C, held for 8 hours, then cooled to 520°C with the furnace, and then air-cooled to room temperature.

[0103]

[0104] Heat the heat-treated ingot to 1200°C in a high-temperature furnace for 1 hour, then water-cool it to room temperature, then heat it to 600°C and temper it for 2 hours, then cool it to room temperature, and then heat the tempered steel ingot at 500°C for 4 hours. Then cool to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides high temperature and high strength low-carbon martensite refractory steel and a preparation method thereof. Chemical components of the low-carbon martensite refractory steel comprise, by mass percentage, 0.10-0.25 wt% of C, 10.0-13.0 wt% of Cr, 2.0-3.2 wt% of Ni, 1.50-2.50 wt% of Mo, smaller than or equal to 0.60 wt% of Si, smaller than or equal to 0.60 wt% of Mn, 0.4-0.8 wt% of W, 0.1-0.5 wt% of V, 0.3-0.6wt% of Co, 0.3-1.0wt% of Al, 0.01-0.2wt% of Nb and the balance Fe. According to the refractory steel, high temperature strengthening is achieved due to the fact that nanometer coherent carbide and an intermetallic compound are precipitated at the same time, excellent toughness is achieved, use for some structural parts under special working conditions such as an aero-engine is achieved, the service life of the refractory steel is prolonged, and the use temperature of the refractory steel is increased.

Description

technical field [0001] The invention relates to the technical field of aero-engines, in particular to a high-temperature, high-strength, low-carbon martensitic heat-strength steel and a preparation method thereof. Background technique [0002] The aero-engine is one of the precise mechanical structures in the aircraft. Since the aero-engine is usually in complex working conditions, in order to meet the safety of the flight, its reliability requirements are very high. Among them, the aero-engine suspension is a kind of aero-engine Structural parts are used to carry aero-engines, which are often in harsh working environments such as high temperature, humidity, high stress and corrosive media, which affects the high-temperature strength, toughness and corrosion resistance of structural parts used in special working conditions such as aero-engine suspension Performance and other performance have higher requirements. [0003] The steel commonly used for aero-engine structural pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/02C22C38/04C22C38/46C22C38/52C22C38/48C22C38/06C21D1/26C21D1/28C21D1/18C21D8/00
CPCC21D1/18C21D1/26C21D1/28C21D8/005C21D2211/008C22C38/02C22C38/04C22C38/06C22C38/44C22C38/46C22C38/48C22C38/52
Inventor 黄进峰张津赵超张诚连勇李建强张程
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com