A ceramic fiber porous filter material reinforcement, its preparation method and ceramic fiber reinforcement material

A technology of ceramic fiber and filter material, which is applied in the field of ceramic fiber porous filter material enhancer and ceramic fiber reinforcement material, and can solve the problems of limited strengthening effect and the like

Active Publication Date: 2022-04-26
FUJIAN LONGKING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Restricted by the porous characteristics of ceramic fiber materials, the strengthening effect is relatively limited through the regulation of product raw materials, formulas or microstructures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The present invention also provides a preparation method of ceramic fiber porous filter material reinforcing agent, comprising the following steps:

[0041] A) adding 2 to 8 parts by weight of surfactant into 100 parts by weight of deionized water, and then adding 5 to 40 parts by weight of active mineral powder to obtain a mixed solution;

[0042] B) dispersing the mixed solution by ball milling to obtain a mixed slurry;

[0043] C) adding 20-80 parts by weight of inorganic adhesive material into the mixed slurry, stirring and mixing to obtain a ceramic fiber porous filter material reinforcement.

[0044] In the present invention, the kind and consumption of described tensio-active agent, deionized water, active mineral powder and inorganic sticky material are the same as the kind of above-mentioned surfactant, deionized water, active mineral powder and inorganic sticky material It is consistent with the dosage and will not be repeated here.

[0045] In the present i...

Embodiment 1

[0064] Add 2 parts by weight of polyethylene glycol to 100 parts by weight of deionized water, then add 2 parts by weight of kaolin, 1 part by weight of bentonite and 5 parts by weight of nano silicon dioxide, and use a planetary ball mill to grind and disperse; then, Transfer the ground slurry to an overhead stirrer, add 10 parts by weight of aluminum sol, 8 parts by weight of silica sol and 2 parts by weight of aluminum dihydrogen phosphate, stir and mix at a high speed to obtain a ceramic fiber porous filter material reinforcement . The obtained reinforcing agent has a solid content of 10.43% and a viscosity of 5 mPa·s at room temperature. After strengthening treatment, the ultimate strength of the radially compressed C-ring sample of the ceramic fiber filter tube is 0.97MPa, and the pressure difference is 400Pa.

Embodiment 2

[0066] Add 5 parts by weight of polyethylene glycol to 100 parts by weight of deionized water, then add 2 parts by weight of kaolin, 1 part by weight of bentonite and 7 parts by weight of nano silicon dioxide, and use a planetary ball mill to grind and disperse; then, Transfer the ground slurry to an overhead stirrer, add 8 parts by weight of aluminum sol, 8 parts by weight of silica sol and 4 parts by weight of aluminum dihydrogen phosphate, stir and mix at a high speed to obtain a ceramic fiber porous filter material reinforcement . The obtained reinforcing agent has a solid content of 11.20% and a viscosity of 6 mPa·s at room temperature. After strengthening treatment, the ultimate strength of the radially compressed C-ring sample of the ceramic fiber filter tube is 1.15MPa, and the pressure difference is 420Pa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a ceramic fiber porous filter material reinforcement, which comprises the following components in parts by weight: deionized water: 100 parts, inorganic adhesive material: 20-80 parts, active mineral powder: 5-40 parts, surface Active agent: 2 to 8 parts; the inorganic adhesive material is one or more of aluminum sol, silica sol and aluminum dihydrogen phosphate; the active mineral powder is kaolin, bentonite, calcined kaolin and nano-silica one or more of them. After the reinforcing agent in the present invention is implanted into the ceramic fiber porous filter material, the bonding strength between matrix materials can be effectively improved, and the problem that the strength of the ceramic fiber porous filter material is low and easy to be damaged during use can be solved. At the same time, it can effectively balance the contradictions between the structure and function of the ceramic fiber porous filter material such as strength, density and filtration performance, and then obtain a ceramic fiber porous filter material with high strength and good filtration performance.

Description

technical field [0001] The invention belongs to the technical field of porous inorganic materials, and in particular relates to a ceramic fiber porous filter material reinforcing agent, a preparation method thereof and a ceramic fiber reinforcing material. Background technique [0002] High-temperature flue gas filtration and dust removal technology is a key step to realize the comprehensive utilization of high-temperature flue gas, and it is also an advanced environmental protection technology. The core of this technology lies in the filter material, which has high requirements due to the long-term operation under high temperature and complex flue gas conditions. [0003] Ceramic fiber combines the excellent properties of traditional thermal insulation materials and refractory materials, and has the advantages of high temperature resistance, good thermal stability, small heat capacity, light weight and mechanical vibration resistance, so it is widely used in many industrial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/34
CPCC04B28/344C04B2201/10C04B24/28C04B14/106C04B14/104C04B14/062C04B22/06C04B24/283C04B18/023
Inventor 沈忠华谢剑龙卢雪声林柳柳黄星林荷
Owner FUJIAN LONGKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com