Preparation process of high-strength wear-resistant concrete

A preparation process and concrete technology, applied in the field of concrete, can solve the problems of concrete surface crushing, concrete fracture, affecting the use of concrete, etc., and achieve the effects of reducing solidification, reducing loss, reducing time and energy consumption.

Inactive Publication Date: 2020-09-25
卫凤仪
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, when the existing concrete on the market is in use, when it is subjected to a large external collision, the concrete is prone to breakage, and the contact and friction with hard objects for a long time will cause the concrete surface to shatter and affect the use of concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of high-strength wear-resistant concrete
  • Preparation process of high-strength wear-resistant concrete
  • Preparation process of high-strength wear-resistant concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Such as figure 1As shown, the present invention provides technical scheme, a kind of preparation technology of high-strength wear-resistant concrete, and concrete is made up of following components by weight:

[0044] 350 parts of Portland cement, 700 parts of fine aggregate, 1150 parts of coarse aggregate, 185 parts of water, 30 parts of silicon micropowder, 65 parts of epoxy resin, 8 parts of steel fiber, 2.5 parts of water reducing agent, 9 parts of accelerator , 0.4 parts of air-entraining agent, 53 parts of metakaolin. The fine aggregate is mountain sand, the particle size of the fine aggregate is 2.2mm, the coarse aggregate is crushed stone, the particle size of the fine aggregate is 5.7mm, and the water reducer is specifically lignosulfonate water reducer and melamine-based high-efficiency water-reducing agents, the accelerator is specifically potassium silicate-based accelerators, and the air-entraining agent is specifically alkylaromatic sulfonic acid-based ai...

Embodiment 2

[0054] Such as figure 1 As shown, the present invention provides technical scheme, a kind of preparation technology of high-strength wear-resistant concrete, and concrete is made up of following components by weight:

[0055] 300 parts of Portland cement, 500 parts of fine aggregate, 950 parts of coarse aggregate, 180 parts of water, 20 parts of silicon micropowder, 50 parts of epoxy resin, 5 parts of steel fiber, 1 part of water reducing agent, 6 parts of accelerator , 0.15 parts of air-entraining agent, 40 parts of metakaolin.

[0056] The fine aggregate is specifically mountain sand, the particle size of the fine aggregate is 2mm, the coarse aggregate is crushed stone, the particle size of the fine aggregate is 5mm, and the water reducing agent is specifically lignosulfonate water reducing agent. The coagulant is specifically a potassium silicate type accelerator, and the air-entraining agent is specifically an alkyl aromatic hydrocarbon sulfonic acid type air-entraining a...

Embodiment 3

[0066] Such as figure 1 As shown, a preparation process of high-strength wear-resistant concrete, the concrete is composed of the following components by weight: 400 parts of Portland cement, 900 parts of fine aggregate, 1250 parts of coarse aggregate, 190 parts of water, silica powder 40 parts, 80 parts of epoxy resin, 12 parts of steel fiber, 4 parts of water reducing agent, 12 parts of accelerator, 0.6 parts of air-entraining agent, 65 parts of metakaolin.

[0067] The fine aggregate is specifically one or more of mountain sand and lake sand, the particle size of fine aggregate is 2.4mm, the specific coarse aggregate is pebble, the particle size of fine aggregate is 6.5mm, and the specific water reducer is Naphthalene-based high-efficiency water-reducing agents and melamine-based high-efficiency water-reducing agents. The accelerator is specifically aluminate-type accelerators, and the air-entraining agent is specifically fatty alcohol sulfonate-type air-entraining agents. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation process of high-strength wear-resistant concrete. The concrete is prepared from the following components in parts by weight: 300 to 400 parts of Portland cement,500 to 900 parts of fine aggregate, 950 to 1250 parts of coarse aggregate, 180 to 190 parts of water, 20 to 40 parts of silica powder, 50 to 80 parts of epoxy resin, 5 to 12 parts of steel fiber, 1 to4 parts of a water reducing agent, 6 to 12 parts of an accelerator, 0.15 to 0.6 part of an air entraining agent and 40 to 65 parts of metakaolin. The structure of the concrete is scientific and reasonable; the preparation method is safe and convenient to use; and the prepared concrete is high in strength and not prone to damage during heavy pressing and collision, the overall strength of the prepared concrete during use is improved, the wear resistance of the concrete is improved, and the setting rate of the concrete is increased, so the market competitiveness of the prepared concrete is improved.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a preparation process of high-strength wear-resistant concrete. Background technique [0002] Concrete refers to the artificial stone made of cement as the main cementitious material, mixed with water, sand, stones, chemical admixtures and mineral admixtures when necessary, mixed in an appropriate proportion, uniformly stirred, compacted and cured. Concrete is mainly divided into two stages and states: the plastic state before setting and hardening, that is, fresh concrete or concrete mixture; the hard state after hardening, that is, hardened concrete or concrete; [0003] At present, when the existing concrete on the market is in use, when it is subjected to a large external collision, it is prone to concrete fracture, and contacting and friction with hard objects for a long time will cause the surface of the concrete to shatter and affect the use of concrete. Contents of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/20
CPCC04B28/04C04B2111/2038C04B14/06C04B14/02C04B18/146C04B24/281C04B14/48C04B14/106C04B24/18C04B24/125C04B22/08C04B24/20C04B2103/302C04B24/16
Inventor 卫凤仪
Owner 卫凤仪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products