Preparation method of MgO-CaO-ZrO2 sand

A sand ball and drying technology, applied in zirconia and other directions, can solve the problems of difficulty in production, storage and application, easy hydration, etc. Effect

Inactive Publication Date: 2020-07-14
海城市军刚中档镁砂有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After calcined at high temperature, the MgO-CaO sand exposes a new surface and is easy to hydrate, which brings great difficulties to production, storage and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 100kg of MgO-CaO powder and 10kg of Zr(OH) with a concentration of 1mol / L 4 The sol is placed in a mixer and mixed for 20 minutes to obtain MgO-CaO-ZrO 2 Material; MgO-CaO-ZrO 2 Put the material into the ball press machine and press it into MgO-CaO-ZrO with a diameter of 40mm at 60MPa 2 Sand balls; MgO-CaO-ZrO 2 Place sand balls at 110°C for 10 hours to obtain dry MgO-CaO-ZrO 2 Sand balls; dry MgO-CaO-ZrO 2 Sand balls are calcined in a kiln at 1500°C for 3 hours to obtain MgO-CaO-ZrO 2 sand.

[0020] After testing the MgO-CaO-ZrO prepared in this example 2 Sand: CaO content is 40wt%, MgO content is 50wt%, bulk density is 2.7g / cm 3 ; After being kept at 50°C and 90% humidity for 10 hours, after drying at 110°C, the hydration weight gain rate of the green body is 1.5%; the thermal shock resistance of MgO-CaO refractories reaches 12 times.

Embodiment 2

[0022] 100kg of MgO-CaO powder and 15kg of Zr(OH) with a concentration of 1mol / L 4 The sol is placed in a mixer and mixed for 20 minutes to obtain MgO-CaO-ZrO 2 Material; MgO-CaO-ZrO 2 Put the material into the ball press machine and press it into MgO-CaO-ZrO with a diameter of 40mm at 70MPa 2 Sand balls; MgO-CaO-ZrO 2 Place sand balls at 110°C for 12 hours to obtain dry MgO-CaO-ZrO 2 Sand balls; dry MgO-CaO-ZrO 2 The sand balls are calcined in a kiln at 1600°C for 4 hours to obtain MgO-CaO-ZrO 2 sand.

[0023] After testing the MgO-CaO-ZrO prepared in this example 2 Sand: CaO content 43wt%, MgO content 46wt%, bulk density 2.9g / cm 3 ; After being kept at 50°C and 90% humidity for 10 hours, after drying at 110°C, the hydration weight gain rate of the green body is 1.0%; the thermal shock resistance of MgO-CaO refractories reaches 15 times.

Embodiment 3

[0025] 100kg of MgO-CaO powder and 20kg of Zr(OH) with a concentration of 1mol / L 4 The sol is placed in a mixer and mixed for 20 minutes to obtain MgO-CaO-ZrO 2 Material; MgO-CaO-ZrO 2 Put the material into the ball press machine and press it into MgO-CaO-ZrO with a diameter of 40mm at 80MPa 2 Sand balls; MgO-CaO-ZrO 2 The sand balls are placed at 110°C for 15 hours until the water content is lower than 1%, and the dried MgO-CaO-ZrO 2 Sand balls; dry MgO-CaO-ZrO 2 The sand balls are calcined in a kiln at 1800°C for 5 hours to obtain MgO-CaO-ZrO 2 sand.

[0026] After testing the MgO-CaO-ZrO prepared in this example 2 Sand: CaO content is 38wt%, MgO content is 46wt%, bulk density is 3.1g / cm 3 ; After being kept at 50°C and 90% humidity for 10 hours, after drying at 110°C, the hydration weight gain rate of the green body is 0.5%; the thermal shock resistance of MgO-CaO refractories reaches 19 times.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of MgO-CaO-ZrO2 sand. The preparation method comprises the following steps: carrying out heat treatment on dolomite ore and magnesite ore, hydrating, sieving with a 0.2 mm sieve, drying a filter body obtained by sieving, and grinding to 200 meshes or below to obtain MgO-CaO2 powder; placing MgO-CaO powder and Zr(OH)4 sol in a mixer to be evenly mixed,conducting ball pressing after mixing, and drying till the moisture is smaller than 1%; and finally, placing the mixture in a kiln to be calcined, and obtaining the MgO-CaO-ZrO2 sand. The MgO-CaO-ZrO2sand prepared by the preparation method disclosed by the invention is good in hydration resistance, high in refractoriness, high in thermal stability and strong in alkaline slag corrosion resistance,has a purification effect on molten steel, and is an ideal raw material for preparing high-grade materials such as magnesium-calcium refractory materials and ceramics.

Description

technical field [0001] The invention relates to the technical field of inorganic chemical industry, in particular to a MgO-CaO-ZrO 2 Sand preparation method. Background technique [0002] MgO-CaO refractories have good high temperature stability and slag resistance, especially the free CaO can purify molten steel. Therefore, MgO-CaO refractories are widely used in AOD refining ladles. However, calcium-containing materials are easily hydrated to form Ca(OH) 2 It causes volume expansion, which in turn leads to material damage, which limits the use of MgO-CaO materials to a large extent. [0003] At present, MgO-CaO sand produced from dolomite is calcined from dolomite raw material at about 1000°C, which is the first step product when MgO-CaO sand is calcined by two-step calcination method. The bulk density of lightly burned MgO-CaO sand is very low, only 1.45g / cm 3 about. Sintered MgO-CaO sand is a product obtained by sintering dolomite powder at 1700-1800°C. There are t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B2/10C04B2/02C04B2/00C01G25/02C04B35/66
CPCC04B2/10C04B2/02C04B2/00C01G25/02C04B35/66
Inventor 刘士军罗旭东杨孟孟周晓蕾
Owner 海城市军刚中档镁砂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com