Method for improving fluidity of cast magnesium alloy in casting mould

A technology of casting magnesium alloy and fluidity, which is applied in the casting field of alloy castings, can solve problems such as difficult filling of alloy liquid in thin-walled parts, hidden dangers of conventional coating quality, etc., and achieve improved surface quality, strong adhesion, and improved smoothness Effect

Active Publication Date: 2020-07-03
新江科技(江苏)有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem solved by the invention is: in the process of forming complex magnesium alloy castings, it is difficult to fill the mold with alloy liquid in thin-walled parts, and there are quality hidden dangers in conventional coatings, and discloses a method for improving the fluidity of cast magnesium alloys in molds , to achieve the purpose of improving the fluidity of the molten metal in the mold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving fluidity of cast magnesium alloy in casting mould

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to make the above-mentioned purposes, features and advantages of the present invention more obvious and understandable, the following in conjunction with the attached figure 1 The specific embodiment of the present invention will be described in detail.

[0022] In the following description, a specific method and details of using a hand-held acetylene flamethrower to coat sand cores with smoked carbon are set forth, so as to fully understand the present invention. But the present invention can be implemented in a variety of other ways that are different from those described here, for example: except for acetylene, other ignited organic matter can also produce black smoke, that is, carbon particles; the metal mold surface can also be coated in this way carbon, etc. Those skilled in the art can make extensions and improvements without violating the connotation of the present invention. Accordingly, the present invention is not limited to the specific embodiment...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for improving the fluidity of a cast magnesium alloy in a casting mould. The method specifically comprises the following steps of spraying an alkyl sodium sulfonate aqueous solution on the surface of the casting mould or a mud core first; coating and brushing sodium silicate after the casting mould or the mud core is dried; and then, igniting an organic matter withhigh carbon content; aligning a flame of the organic matter with a casting mould surface to perform roasting, so that carbon particles produced by incomplete combustion of the organic matter are uniformly adhered to the surface of a mould core in contact with a molten metal; and therefore, the roughness of the casting mould surface is reduced, and the fluidity of the molten metal in the casting mould is improved. According to the method disclosed by the invention, the fluidity of the cast magnesium alloy in the casting mould can be improved, so that the capacity of the cast magnesium alloy for forming a complex thin-walled casting is enhanced; meanwhile, the fluidity of the molten metal is enhanced; and under the same casting conditions, the alloy casting temperature is reduced, so that the defects of loosening and the like are reduced.

Description

technical field [0001] The invention relates to a casting method of an alloy casting, in particular to a method for improving the fluidity of an alloy in a mold. Background technique [0002] In aerospace, automobile and other fields, on the premise of satisfying the performance of products, reducing weight can increase the load of the system and save more energy. Magnesium alloys are more and more widely used due to their advantages such as low density, high specific strength, and excellent processing performance. The continuous development of the industry requires all kinds of magnesium alloy castings with excellent performance and complex structure to meet various needs. [0003] In the casting process, the molten alloy must first fill the mold and then solidify to form a casting. If the molten metal cannot fill the mold, it will cause defects such as cold shut and insufficient pouring, and the casting will be scrapped. During the filling process, on the one hand, the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 陈加运何凯秦守益张娜张旭亮王小冬曾柏栋
Owner 新江科技(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap