Application of modified jade powder in health care and treatment patches
A technology of jade powder and treatment paste, which is applied in the direction of treatment, medical preparations with non-active ingredients, medical preparations containing active ingredients, etc., can solve the problems of unreachable, low SWIR radiation rate and radiation amount, and achieve the effect of improving Effect, no smog pollution, improve the effect of treatment effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] The preparation method of the modified jade powder of the present embodiment comprises the following steps:
[0033] 1) Raw material preparation: natural jade crushed stone powder and transition metal oxide are mixed in a weight ratio of 10:1 to obtain a mixed powder;
[0034] 2) Multi-phase composite: put the mixed powder in a muffler furnace, heat up to 550°C at a rate of 5°C / min, and continue calcining for 2 hours to obtain high-temperature multi-phase composite jade powder;
[0035] 3) Quenching hydration: quickly place the high-temperature multi-phase composite jade powder in a saturated magnesium hydroxide aqueous solution with a pH of 10-11 and soak for 3 hours, filter, and wash with water repeatedly until the filtrate is acid-base neutral. After filtering, let it stand for aging After 12 hours, place it in an oven at 80°C for 10 hours and dry it for 10 hours. The moisture content is lower than 10%, and the processed jade powder is obtained;
[0036] 4) Superfin...
Embodiment 2
[0038] The preparation method of the modified jade powder of the present embodiment comprises the following steps:
[0039] 1) Raw material preparation: natural jade crushed stone powder and transition metal oxide are mixed in a weight ratio of 10:1 to obtain a mixed powder;
[0040] 2) Multi-phase composite: put the mixed powder in a muffler furnace, heat up to 550°C at a rate of 5°C / min, and continue calcining for 2 hours to obtain high-temperature multi-phase composite jade powder;
[0041] 3) Quenching hydration: In a fume hood, quickly place the high-temperature multi-phase composite jade powder in an ammonia-ammonium chloride aqueous solution with a pH of 10-11 and soak for 3 hours, filter, and wash repeatedly until the filtrate is acid-base neutral And there is no ammonia smell. After filtering, let it stand for aging for 12 hours, and dry it in an oven at 80°C for 10 hours. The moisture content is less than 10%, and the treated jade powder is obtained;
[0042] 4) Sup...
Embodiment 3
[0044] The preparation method of the modified jade powder of the present embodiment comprises the following steps:
[0045] 1) Preparation of materials: natural jade crushed stone powder and transition metal oxides are mixed at a weight ratio of 10:0.8;
[0046] 2) Multi-phase composite: put the mixed powder in a muffler furnace, heat up to 800°C at a rate of 8°C / min, and continue calcining for 2 hours to obtain high-temperature multi-phase composite jade powder;
[0047] 3) Quenching hydration: quickly place the high-temperature multi-phase composite jade powder in a saturated magnesium hydroxide aqueous solution with a pH of 10-11 and soak for 3 hours, filter, and wash with water repeatedly until the filtrate is acid-base neutral. After filtering, let it stand for aging After 12 hours, place it in an oven at 80°C for 10 hours and dry it for 10 hours. The moisture content is lower than 10%, and the processed jade powder is obtained;
[0048] 4) Superfine crushing: pulverize ...
PUM
Property | Measurement | Unit |
---|---|---|
particle size (mesh) | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com