A preparation method and application of lanthanum-modified Platanus biochar

A technology of sycamore and biochar, applied in chemical instruments and methods, water pollutants, other chemical processes, etc., can solve problems such as unknown performance of adsorbing P, no research on adsorption capacity, etc., and achieves low cost, stable water effluent effect, A wide range of effects

Active Publication Date: 2022-03-22
BEIJING UNIV OF TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] (2) Study on the adsorption performance of biochar in fixed bed column to treat P in urban sewage: none of the previous studies have studied the adsorption capacity of engineered biochar for P in actual wastewater
Furthermore, the performance of biochar as a filter medium for P adsorption in dynamic real wastewater streams in fixed-bed filter reactors remains unknown.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of lanthanum-modified Platanus biochar
  • A preparation method and application of lanthanum-modified Platanus biochar
  • A preparation method and application of lanthanum-modified Platanus biochar

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029] Mix dioctyl sulfosuccinate sodium salt with distilled water at a volume ratio of 1:5 to obtain a mixed solution. The mass ratio of Platanus chinensis fruit balls to the mixed solution is 1:4. Put the sycamore fruit balls into the mixed solution after being crushed. Stir at low temperature for 24 hours, separate and obtain fruit hairs, wash and dry at 105°C. The dried fruit hairs were soaked in 2.5M KOH solution for 2 hours, ultrasonicated at 40KHz for 30 minutes, and dried again. Fruit hairs were pretreated in a tube furnace at 200 °C for 30 min, and 2 Keep in the air flow for 90min, finally at 10℃·min -1 The heating rate was increased to 600 ° C for 2 h. The obtained biochar TC was ground with a 200-mesh sieve and washed to neutral drying. Add 300mgTC to 50mL of 0.2M La(NO 3 ) 3 ·6H 2 In a Erlenmeyer flask of O, 1M NaOH was added by co-precipitation method to maintain the pH at 11, and magnetically stirred for 24h. After centrifugation at 6000 rpm, a solid preci...

example 2

[0032] Mix dioctyl sulfosuccinate sodium salt with distilled water at a volume ratio of 1:5 to obtain a mixed solution. The mass ratio of Platanus chinensis fruit balls to the mixed solution is 1:4. Put the sycamore fruit balls into the mixed solution after being crushed. Stir at low temperature for 24 hours, separate and obtain fruit hairs, wash and dry at 105°C. The dried fruit hairs were soaked in 2.5M KOH solution for 2 hours, ultrasonicated at 40KHz for 30 minutes, and dried again. Fruit hairs were pretreated in a tube furnace at 200 °C for 30 min, and 2 Keep in the air flow for 90min, finally at 10℃·min-1 The heating rate was increased to 600 ° C for 2 h. The obtained biochar TC was ground with a 200-mesh sieve and washed to neutral drying. Add 300mgTC to 50mL of 0.2M La(NO 3 ) 3 ·6H 2 In a Erlenmeyer flask of O, 1M NaOH was added by co-precipitation method to maintain the pH at 11, and magnetically stirred for 24h. After centrifugation at 6000 rpm, a solid precipi...

example 3

[0035] Mix dioctyl sulfosuccinate sodium salt with distilled water at a volume ratio of 1:5 to obtain a mixed solution. The mass ratio of Platanus chinensis fruit balls to the mixed solution is 1:4. Put the sycamore fruit balls into the mixed solution after being crushed. Stir at low temperature for 24 hours, separate and obtain fruit hairs, wash and dry at 105°C. The dried fruit hairs were soaked in 2.5M KOH solution for 2 hours, ultrasonicated at 40KHz for 30 minutes, and dried again. Fruit hairs were pretreated in a tube furnace at 200 °C for 30 min, and 2 Keep in the air flow for 90min, finally at 10℃·min -1 The heating rate was increased to 600 ° C for 2 h. The obtained biochar TC was ground with a 200-mesh sieve and washed to neutral drying. Add 300mgTC to 50mL of 0.2M La(NO 3 ) 3 ·6H 2 In a Erlenmeyer flask of O, 1M NaOH was added by co-precipitation method to maintain the pH at 11, and magnetically stirred for 24h. After centrifugation at 6000 rpm, a solid preci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of lanthanum hydroxide modified biochar, belongs to the field of functional materials and environmental water treatment, and is used for removing phosphate in municipal sewage. This invention uses plane tree fruit balls as the raw material of biochar, and after modification with lanthanum, an efficient, economical and environmentally friendly adsorbent La‑TC is prepared. For the concentration of phosphorus in municipal sewage 4-10mg / L, when the dosage of La-TC is 0.3-0.5g / L, the pH of the solution is 3-9, and the temperature is 25-40°C, it will be ready within 15-20min Achieve 100% removal of phosphate. At the same time, it has strong anti-competitive anion interference ability, and after 3 adsorption-desorption cycles, the adsorption rate of La‑TC can still reach 100%. In the experiment of using a fixed bed column to remove municipal sewage, at a flow rate of 1mL / min, the maximum bed volume of 0.5g-1.0g La-TC was 420BV-480BV, indicating that La-TC has a wide range of practical engineering applications. Prospects.

Description

technical field [0001] The invention discloses a preparation method of lanthanum hydroxide modified biochar, belongs to the field of functional materials and environmental water treatment, and is used for removing phosphate in urban sewage. Background technique [0002] Phosphate is a limiting nutrient factor for phytoplankton in water bodies, and its unreasonable discharge will inevitably lead to eutrophication of water bodies. Studies have shown that when the concentration of phosphate in the water body reaches 0.02mg / L, it is enough to stimulate the growth of algae and cause serious algae blooms. Therefore, it is very important to protect the water ecological environment to remove the phosphate in the sewage before it is discharged into the receiving water body. At present, there are many technical means to remove phosphate in sewage, such as enhanced biological phosphorus removal EBPR, chemical precipitation, ion exchange, membrane treatment technology and adsorption me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28C02F101/10
CPCB01J20/20B01J20/06C02F1/283C02F1/281C02F2101/105
Inventor 曾薇贾子悦许欢欢李帅帅彭永臻
Owner BEIJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com