Non-ferrous metal dry particles for ceramic tile surfaces and processing and using methods thereof

A technology of non-ferrous metals and ceramic tiles, which is applied in applications, home appliances, and other home appliances. It can solve the problem of low artistic aesthetics and achieve the effects of improving metal gloss, artistic aesthetics, and quality and performance.

Inactive Publication Date: 2020-06-16
山东永乾陶瓷科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When the existing ceramic tiles are used, there is a lack of a material that can enhance the three-dimensional artistic beauty and texture of the ceramic tiles. The ceramic tiles only have functional functions, resulting in low artistic aesthetics. At the same time, adding some non-ferrous metal particles can improve the glazed surface of the ceramic tiles. Gloss, look and feel better

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-ferrous metal dry particles for ceramic tile surfaces and processing and using methods thereof
  • Non-ferrous metal dry particles for ceramic tile surfaces and processing and using methods thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of non-ferrous metal dry granules for ceramic tile surface, its raw materials are as follows by weight: 3 parts of copper particles, 5 parts of aluminum particles, 2 parts of zinc particles, 60 parts of quartz stone, 10 parts of calcite, 15 parts of dolomite, 5 parts of talc , 15 parts of spodumene, 16 parts of alumina, 6 parts of barium carbonate, 7 parts of potassium carbonate, 7 parts of zirconium silicate, 2 parts of borax, and 16 parts of marble.

[0033] The mesh numbers of the copper particles, aluminum particles and zinc particles are all 100 mesh. The particle diameters of the quartz stone, calcite, dolomite, talc, spodumene and marble are all 4mm. The particle size of the alumina, barium carbonate, potassium carbonate, zirconium silicate and borax is 60 mesh, and the alumina, barium carbonate, potassium carbonate, zirconium silicate and borax are all white particles. The content of silicon dioxide in the quartz stone exceeds 53%.

[0034] The present ...

Embodiment 2

[0050]A kind of non-ferrous metal dry granules for ceramic tile surface, its raw materials are as follows in parts by weight: 4 parts of copper particles, 6 parts of aluminum particles, 3 parts of zinc particles, 70 parts of quartz stone, 11 parts of calcite, 16 parts of dolomite, 6 parts of talc , 15.5 parts of spodumene, 18 parts of alumina, 8 parts of barium carbonate, 8 parts of potassium carbonate, 8 parts of zirconium silicate, 3 parts of borax, and 18 parts of marble.

[0051] The mesh numbers of the copper particles, aluminum particles and zinc particles are all 110 mesh. The particle diameters of the quartz stone, calcite, dolomite, talc, spodumene and marble are all 6mm. The particle size of the alumina, barium carbonate, potassium carbonate, zirconium silicate and borax is 80 meshes, and the alumina, barium carbonate, potassium carbonate, zirconium silicate and borax are all white particles. The content of silicon dioxide in the quartz stone exceeds 53%.

[0052] ...

Embodiment 3

[0068] A kind of non-ferrous metal dry granule for ceramic tile surface, its raw materials are as follows by weight: 5 parts of copper particles, 7 parts of aluminum particles, 4 parts of zinc particles, 80 parts of quartz stone, 12 parts of calcite, 17 parts of dolomite, 7 parts of talc , 16 parts of spodumene, 20 parts of alumina, 10 parts of barium carbonate, 9 parts of potassium carbonate, 9 parts of zirconium silicate, 4 parts of borax, and 20 parts of marble.

[0069] The mesh numbers of the copper particles, aluminum particles and zinc particles are all 120 mesh. The particle diameters of the quartz stone, calcite, dolomite, talc, spodumene and marble are all 8mm. The particle size of the alumina, barium carbonate, potassium carbonate, zirconium silicate and borax is 100 mesh, and the alumina, barium carbonate, potassium carbonate, zirconium silicate and borax are all white particles. The content of silicon dioxide in the quartz stone exceeds 53%.

[0070] The present...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses non-ferrous metal dry particles for a ceramic tile surface and processing and using methods thereof. The raw materials comprise the following components in parts by weight: 3-5parts of copper particles, 5-7 parts of aluminum particles, 2-4 parts of zinc particles, 60-80 parts of quartz stone, 10-12 parts of calcite, 15-17 parts of dolomite, 5-7 parts of talc, 15-16 parts of spodumene, 16-20 parts of aluminum oxide, 6-10 parts of barium carbonate, 7-9 parts of potassium carbonate, 7-9 parts of zirconium silicate, 2-4 parts of borax and 16-20 parts of marble. The dry particles are formed by compounding the quartzite, the calcite, the dolomite, the talc, the spodumene, the aluminum oxide, the barium carbonate, the potassium carbonate, the zirconium silicate, the borax, the marble and the zinc oxide materials. The quality and performance of the dry particles are remarkably improved, the dry particles are jetted on the surface of the ceramic tile, the three-dimensional artistic aesthetic feeling and texture of the ceramic tile can be shown, the artistic aesthetic feeling of the ceramic tile is greatly improved besides the functionality, meanwhile, the metal glossiness of the surface of the ceramic tile can be improved by adding the copper particles, the aluminum particles and the zinc particles, and the sense is greatly improved.

Description

technical field [0001] The invention relates to the technical field of ceramic tile treatment, in particular to dry nonferrous metal particles for tile surfaces, and also relates to a method for processing and using dry nonferrous metal particles for ceramic tile surfaces. Background technique [0002] Ceramic tiles, also known as tiles, are a kind of acid and alkali resistant porcelain or stone formed by refractory metal oxides and semi-metal oxides through the process of grinding, mixing, pressing, glazing and sintering. Or decorative materials, called ceramic tiles. Its raw materials are mostly mixed with clay, quartz sand and so on. According to usage: exterior wall tiles, interior wall tiles, floor tiles, square tiles, industrial bricks, etc.; according to molding: dry-pressed bricks, extruded bricks, plastic molded bricks; according to firing components: oxidative tiles, reductive tiles ;According to glazing: glazed tiles, unglazed tiles; according to water absorptio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/02C03C8/18C04B41/86
CPCC03C8/02C03C8/18C04B41/009C04B41/52C04B41/86C04B33/00C04B35/00C04B41/46C04B41/4543C04B41/459C04B41/5022C04B41/4545
Inventor 纪冬冬阿里克谢斯密尔诺夫崔鹏金亚敏巩雪
Owner 山东永乾陶瓷科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com