Novel guniting material for inhibiting spontaneous combustion of gangue dump and application method thereof

A technology of gangue hill and shotcrete, applied in the field of coal gangue hill spontaneous combustion fire-extinguishing material, can solve the problems of inconvenient grouting hole, high treatment cost, many hidden dangers, etc., and achieves low construction risk factor, low construction cost and low cost Effect

Active Publication Date: 2020-06-05
INNER MONGOLIA UNIV OF SCI & TECH
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the process of controlling the spontaneous combustion of gangue hills by grouting method, grouting holes need to be drilled on the top and slope of gangue hills. There are certain requirements for slope angle and slope height. The slope height of each level is less than 10 meters, and the accumulation angle of repose is less than 30°; For some gangue hills with long slopes and large slope angles, it is not convenient to drill grouting holes during the grouting process, the operation is difficult, there are many safety hazards, and the treatment cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Weigh 600g of fly ash, 100g of desulfurized gypsum, 100g of silica fume powder, 100g of calcium carbide mud, and 100g of cement, add 15g of chopped glass fiber with a length of 15mm, add 50g of composite admixture, add 700g of water, stir evenly, and use cement glue The fluidity measured by the sand fluidity tester is 98mm, the water separation rate of the slurry is 3.7% in 3 hours, and 4.4% in 6 hours. Pour the slurry into the mortar triple test mold of 70.7*70.7*70.7, put it together with the test mold in an environment with a temperature of (20±2)°C and a relative humidity of ≥50%, remove the mold after 48 hours, and place the test block at a temperature of ( 20 ± 1) ℃, relative humidity not lower than 90% in the curing box, test the compressive strength of the test block in the 3d, 7d, 28d periods are 3.9Mpa, 9.8Mpa, 17.8Mpa respectively, and the softening coefficient after 28d is 0.91 .

Embodiment 2

[0031] Weigh 550g of fly ash, 120g of desulfurized gypsum, 80g of silica fume powder, 70g of calcium carbide mud, and 80g of cement, add 13g of chopped glass fiber with a length of 15mm, add 60g of composite admixture, add 750g of water, stir evenly, and use cement glue The fluidity measured by the sand fluidity tester is 104mm, the water separation rate of the slurry is 3.3% in 3 hours, and 4.1% in 6 hours. Pour the slurry into the mortar triple test mold of 70.7*70.7*70.7, put it together with the test mold in an environment with a temperature of (20±2)°C and a relative humidity of ≥50%, remove the mold after 48 hours, and place the test block at a temperature of ( 20 ± 1) ℃, relative humidity not less than 90% in the curing box, test the compressive strength of the test block in the period of 3d, 7d, and 28d respectively to be 3.6Mpa, 8.9Mpa, 17.3Mpa, and the softening coefficient after 28d is 0.92 .

Embodiment 3

[0033] A field test was carried out on a spontaneous combustion gangue hill in Wuhai. A spontaneous combustion area of ​​2,000 square meters was selected. The internal temperature of the gangue hill was detected to be 423°C by thermocouple. Ash 50%, desulfurized gypsum 12%, silica fume powder 13%, calcium carbide mud 10%, cement 15%. Chopped glass fiber accounts for 1.5% of the total amount, composite admixture accounts for 5% of the total amount, and the water-cement ratio is 0.67. Prepare a uniform slurry, and use a spraying machine to spray the slurry on the surface of the gangue from top to bottom. The thickness is 12-15cm. After the shotcrete layer is cured, spray water on the surface of the shotcrete cured layer after 72 hours, and last for 3-4 times. The compressive strengths of the 3d, 7d, and 28d sampling tests after construction were 3.3Mpa, 8.2Mpa, and 17.7Mpa. 30d, 45d, 60d, and 90d after spraying treatment, the temperature readings of the embedded thermocouples c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel guniting material for inhibiting spontaneous combustion of a gangue dump and an application method thereof, and belongs to the field of spontaneous combustion extinguishment of the gangue dump. The raw material of the guniting material is mainly coal-based solid waste, which comprises power plant by-product fly ash and desulfurized gypsum taking coal as fuel; the guniting material further includes by-product calcium carbide slurry of a PVC plant, by-product silica fume powder of a silicon iron smelting plant and a composite additive. The guniting material is sprayed on the surface of a gangue dump by using a guniting machine to form a solidified layer, so that the effects of preventing wind, stopping leakage and isolating air are achieved, air is prevented from entering a fire source in the gangue dump, and spontaneous combustion of the gangue dump is inhibited.

Description

technical field [0001] The invention belongs to the field of spontaneous combustion fire extinguishing materials for coal gangue, in particular to a spraying material prepared from industrial solid waste such as fly ash, which is used for suppressing spontaneous combustion of coal gangue. Background technique [0002] The reason for the spontaneous combustion of coal gangue is that if the heat released during the oxidation of coal and pyrite in gangue cannot be completely dissipated in the surrounding environment, it will cause the gangue to heat up, and the increase in temperature will further accelerate the oxidation exothermic reaction. After reaching the critical temperature point, the oxidation reaction speed will be accelerated sharply. At this time, if sufficient oxygen supply can still be obtained, gangue will quickly enter the state of spontaneous combustion. The existence of a large amount of coal in the gangue maintains the smoldering of the gangue pile for a long...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/14A62C3/06A62C99/00A62D1/00
CPCA62C3/06A62C99/0045A62D1/0007C04B28/144C04B2111/00017C04B2111/00155C04B2111/00275C04B2111/00482C04B2111/00577C04B2111/00775C04B2111/00974C04B2201/50C04B18/08C04B18/146C04B18/0418C04B7/00C04B14/42C04B22/00C04B22/062C04B22/147
Inventor 董红娟王博张金山卢悦李庭月史鑫章姚贺瑜
Owner INNER MONGOLIA UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com